Background: Type 2 diabetes mellitus is a condition characterized by an elevation of oxidative stress, which has been implicated in diabetic progression and its vascular complications. Aim: Assessing the impact of gliclazide modified release (MR) versus glimepiride on oxidative stress markers, glycemic indices, lipid profile, and estimated glomerular filtration rate in uncontrolled type 2 diabetic patients on metformin monotherapy. Methods: This was an observational comparative study conducted in Thi-Qar specialized diabetic, endocrine, and metabolism center. Sixty-six patients were randomized into two groups based on the addition of the sulfonylureas (SUs). Group 1 (33 patients) was on gliclazide MR, whereas Group 2 (33 patients)

Cadmium Oxide thin films were deposited on glass substrate by spray pyrolysis technique at different temperatures (300,350,400, 500)oC. The optical properties of the films were studied in this work. The optical band-gap was determined from absorption spectra, it was found that the optical band-gap was within the range of (2.5-2.56)eV also width of localized states and another optical properties.

The effect of annealing temperature (Ta) on the electrical properties like ,D.C electrical conductivity (σ DC), activation energy (Ea),A.C conductivity σa.c ,real and imaginary (ε1,ε2) of dielectric constants ,relaxation time (τ) has been measured of ZnS thin films (350 nm) in thickness which were prepared at room temperature (R.T) using thermal evaporation under vacuum . The results showed that σD.C increases while the activation energy values(Ea) decreases with increasing of annealing temperature.(Ta) from 303- 423 K .
The density of charge carriers (nH) and Hall mobility (μH) increases also with increasing of annealing temperature Hall effect measurements showed that ZnS films were n-type converted to p-type at high annealin

Through this study, the following has been proven, if  is an algebraically paranormal operator acting on separable Hilbert space, then  satisfies the ( ) property and  is also satisfies the ( ) property for all . These results are also achieved for  ( ) property.    In addition, we prove that for a polaroid operator with finite ascent then after the property ( ) holds for  for all.

GaN thin films were deposited by thermal evaporation onto
glass substrates at substrate temperature of 403 K and a thickness of
385 nm . GaN films have amorphous structure as shown in X-ray
diffraction pattern . From absorbance data within the range ( 200-
900 ) nm direct optical energy gap was calculated . Also the others
optical parameters like transmittance T, reflectance R , refractive
index n , extinction coefficient k , real dielectric constant 1 Î , and
imaginary dielectric constant 2 Î were determined . GaN films
have good absorbance and minimum transmittance in the region of
the visible light .

The local asphalt concrete fracture properties represented by the fracture energy, J-integral, and stress intensity factor are calculated from the results of the three point bending beam test made for pre notches beams specimens with deformation rate of 1.27 ^mm/min. The results revealed that the stress intensity factor has increased by more than 40% when decreasing the testing temperature 10˚C and increasing the notch depth from 5 to 30^mm. The change of asphalt type and content have a limited effect of less than 6%.

In the present work, lead silicate glasses have been prepared with
different amount of lead oxide content. Structure properties such as
X-ray diffraction, AFM, and FTIR analyses have been done. The
exceeding of PbO content more than 25wt% revealed a decreasing in
density. The X- ray revealed that the strongest peak related to
Hexagonal silica dioxide and the other crystal phases formed were
related to silica oxide (SiO2) and lead oxide (PbO). Growth and
decayed phases in X-ray have been observed with changing lead
oxide content. Homogeneous surface was obtained using AFM
analyzer with an average diameter around 100 nm. Infrared spectrum
is characterized by the presence of large absorption band between
120

This work deals with thermal cracking of three samples of extract lubricating oil produced as a by-product from furfural extraction process of lubricating oil base stock in AL-Dura refinery. The thermal cracking processes were carried out at a temperature range of 325-400 ºC and atmospheric pressure by batch laboratory reactor. The distillation of cracking liquid products was achieved by general ASTM distillation (ASTM D -86) for separation of gasoline fraction up to 220 ºC from light cycle oil fraction above 220 ºC. The comparison between the conversions at different operating conditions of thermal cracking processes indicates that a high conversion was obtained at 375°C, according to gasoline production. According to gasoline produ