In this investigation, the mechanical properties and microstructure of Metal Matrix Composites (MMCs) of Al.6061 alloy reinforced by ceramic materials SiC and Al₂O₃ with different additive percentages 2.5, 5, 7.5, and 10 wt.% for the particle size of 53 µ_m are studied. Metal matrix composites were prepared by stir casting using vortex technique and then treated thermally by solution heat treatment at 530 ⁰C for 1 hr. and followed by aging at 175 ⁰C with different periods. Mechanical tests were done for the samples before and after heat treatment, such as impact test, hardness test, and tensile test. Also, the microstructure of the metal matrix composites was examine

Microwave heating is caused by the ability of the materials to absorb microwave energy and convert it to heat. The aim of this study is to know the difference that will occur when heat treating the high strength aluminum alloys AA7075-T73 in a microwave furnace within different mediums (dry and acidic solution) at different times (30 and 60) minutes, on mechanical properties and fatigue life. The experimental results of microwave furnace heat energy showed that there were variations in the mechanical properties (ultimate stress, yielding stress, fatigue strength, fatigue life and hardness) with the variation in mediums and duration times when compared with samples without treatment. The ultimate stress, yielding stress and fatigue streng

This study focuses on producing wood-plastic composites using unsaturated polyester resin reinforced with Pistacia vera shell particles and wood industry waste powder. Composites with reinforcement ratios of 0%, 20%, 30%, and 40% were prepared and tested for thermal conductivity, impact strength, hardness, and compressive strength. The results revealed that thermal conductivity increases with reinforcement, while maintaining good thermal insulation, reaching a peak value of 0.633453 W/m·K. Hardness decreased with increased reinforcement, reaching a minimum nominal hardness value of 0.9479. Meanwhile, impact strength and compressive strength improved, with peak values of 14.103 k/m² and 57.3864568 MPa, respectively. The main aim is to manu

Purpose: Current denture liner materials suffer from low tear strength, poor abrasion resistance, weak bond strength to denture material, and increasing risk of denture stomatitis due to adherence. The aim of this study was to evaluate the effects of the addition of cellulose nanofibers (CNFs) to commercial soft denture liner material on the adherence of and physical and mechanical properties. Materials and Methods: CNFs at concentrations of 0.0, 0.5, and 1.0 wt.% were incorporated into a soft liner material. Antifungal effects were assessed by quantifying the adherence of . The Shore A hardness, tensile strength, peel bond strength, and surface roughness tests were employed to assess the properties of the denture liner materials. Chemica

Background: Polymethyl methacrylate (PMMA) resin is extensively utilized in prosthodontics and orthodontics, particularly in fabricating artificial teeth, provisional crowns, denture bases, and orthodontic retainers. Aims: This study aimed to evaluate the effects of incorporating cerium oxide and polyether ether ketone nanoparticle (CP) composite into PMMA resin on transverse strength, impact strength, surface hardness, and denture base adaptation. Materials and Methods: A total of 120 PMMA specimens were divided into three groups based on the concentration of CP composite added to PMMA resin, with each group consisting of 40 specimens: a control group without fillers, group (A) containing 1% wt. of composite filler with a ratio of

Although the number of implants has increased gradually and consistently over the years to around one million per year globally, there is still far more potential for advancement in the field of dental implantology which is typically growing quickly. This study investigates the effect of nanofiller reinforcement high-performance polymer matrix to enhance mechanical and physical characteristics. Calcium silicate (CS)/Polyetherketoneketone (PEKK) biomedical composite (G0 as a control group) is reinforced with different weight percentages (G1-G4) of tellurium dioxide nanoparticles (TeO₂NPs) ( n = 5). This research uses ethanol as a binder for mixing various weight percentages (wt%) of TeO₂NPs w

The dual nature of asphalt binder necessitates improvements to mitigate rutting and fatigue since it performs as an elastic material under the regime of rapid loading or cold temperatures and as a viscous fluid at elevated temperatures. The present investigation assesses the effectiveness of Nano Alumina (NA), Nano Silica (NS), and Nano Titanium Dioxide (NT) at weight percentages of 0, 2, 4, 6, and 8% in asphalt cement to enhance both asphalt binder and mixture performance. Binder evaluations include tests for consistency, thermal susceptibility, aging, and workability, while mixture assessments focus on Marshall properties, moisture susceptibility, resilient modulus, permanent deformation, and fatigue characteristics. NS notably im

The dual nature of asphalt binder necessitates improvements to mitigate rutting and fatigue since it performs as an elastic material under the regime of rapid loading or cold temperatures and as a viscous fluid at elevated temperatures. The present investigation assesses the effectiveness of Nano Alumina (NA), Nano Silica (NS), and Nano Titanium Dioxide (NT) at weight percentages of 0, 2, 4, 6, and 8% in asphalt cement to enhance both asphalt binder and mixture performance. Binder evaluations include tests for consistency, thermal susceptibility, aging, and workability, while mixture assessments focus on Marshall properties, moisture susceptibility, resilient modulus, permanent deformation, and fatigue characteristics. NS notably im

Carbides or nitrides thin films present materials with good mechanical properties for industrial applications as they can be coatings at low temperatures serve temperature sensitive surfaces. In this work the effect of the C percentage on the mechanical properties represented by the Young modulus (E) of combinatorial magnetron sputtered TiC_x (34%x˂65%) has been studied. The structure of the produced films is TiC independent on the C concentration. The mechanical properties are increased with increasing the C concentration up to 50%, and then decreasing with further C % increasing. These results can be explained by considering the resultant residual stresses.