Nanocrystalline micro-mesoporous ZSM/MCM-41 composite was synthesized using alkaline treatment method and two step of crystallization in poly tetraflouroethylene (PTFE) lined autoclave. The synthesized zeolites was characterized by X-Ray diffraction (XRD), Scanning electron microscopy (SEM), Transmission electron microscopy (TEM), Atomic force microscopy (AFM), Fourier transport infrared (FTIR), and N₂ adsorption-desorption (BET). It was approved that the best results for alkaline leaching can be got with 1.5M NaOH solution. High surface (BET) area of 630 m²/g with pore volume of 0.55 cm³/g has been got. AFM reports showed a nano-level size for average particle size of 50nm.

In this work, we have examined the spectral response of (p-CuAlSe2/n-Si) detector, (CAS) thin films deposited by thermal evaporation at RT with a thickness (450) nm, and annealing temperature at (473K) for 2 h. Optical transmission measurements displayed reasonably slight transmission besides higher absorbance trendy the visible region, energy gaps were observed by annealing, were found to be direct, and decreased with the effect of annealing. The extreme responsivity value arises at wavelength 459 nm, with improvement value of specific detectivity and quantum efficiency the annealing films be situated originate as greatest suitable aimed at numerous device application.

Bruggeman's symmetric effective-medium model of vanadium oxide is introduced, in which the transmittance was studied because of its importance in the subject of smart windows, it was studied from ( 5 nm-1000 nm) for each of the regions of the electromagnetic spectrum, the ultraviolet and visible region, and the near and medium sub-regions of the infrared and the results showed that the importance of studying the transmittance of vanadium oxide as a good candidate For this kind of industries. Our results showed that the small sizes of the material guarantee an almost constant and high transmittance to the visible region; this is due to the agreement of the direction of the dipoles in the material with the direction of the internal el

The change in the optical band gap and optical activation energy have been investigated for pure Poly (vinyl alcohol)and Poly (vinyl alcohol) doped with Aluminum sulphate to proper films from their optical absorption spectra. The absorption spectra were measured in the wave range from (200-700) nm at temperature range (25-140) 0C. The optical band gap (Eg) for allowed direct transition decrease with increase the concentration of Aluminum sulphate. The optical activation energy for allowed direct transition band gap was evaluated using Urbach- edges method. It was found that ?E increases with increasing the concentration of Al2 (SO4)3 and decreases when temperature increases.

In this research, the influence of the fermentation treatments and baking in Iraqi’s flour type (Ibaa 99, Al-rashed, Tamus, Abu-grabe) and Turkish flour type (Muaamel) on phytic acid was investigated. In whole wheat flour, the phytic acid was (1500, 1290, 1450, 1230, 1440 ( mg/ 100 g flour respectively, and the inorganic phosphorous was (29.18, 25.15, 23.89, 20.85, 22.83) mg/100 g flour respectively. The dough prepared from flour with a higher phytic acid content also contained higher amount of phytic acid. During fermentation, degradation of phytic acid occurred. The cumulative loss of phytic acid after fermentation in all type of dough was ~ 23, 22, 34, 26 and 27% respectively،While increased of inorganic phosphorous occurred. The c

In this study, Al2O3 thin films were prepared by dc reactive sputtering technique using different gas mixtures of argon and oxygen gases (90:10, 70:30, 50:50, 30:70, and 10:90). These films were characterized to introduce their surface morphology and elemental composition as functions of the oxygen content in the gas mixture. The gas mixing ratio plays a crucial role in controlling the nanoscale morphology of the prepared thin films. The [Al]/[O] ratio varies non-linearly with the Ar:O2​ mixing ratio. Increasing the oxygen content leads to a progressive decrease in surface roughness, resulting in smoother and more uniform films with finer granular features. These results presented herein are useful to optimize the sputtering process to ac

The azo Schiff base [Reaction of 4-aminoanypyrine and P-hydroxy acetophenone] and O-Phenylene diamine have been prepared. One azo Schiff base chelate of Co(Il), Ni(II), Cu(II) and Zn(II)ion was also prepared. The chemical frameworks of the azo Schiff base and like elemental analyses (CHN), determinations of molar conductance, 1 H &13C NMR, IR mass and electronic spectroscopy .The elemental analyses exhibited the combination of [L: M] 1:1 ratio. Established on the values IR spectral, it is showed that the azo Schiff base compound acts as neutral hexadentate ligand bonded with the metal ion from two hydroxyl, two azomethine and two azo groups of the azo Schiff base compound in chelation was confirmed by IR , 1Hand 13CNMR spectral outco

This research studying the phenomenon of Doppler (frequency Doppler) as a method through which the direction and speed of the blood cells flows in blood vessels wear measured. This Doppler frequency is relied upon in medicine for measuring the speed of blood flow, because the blood flow is an important concept from the concepts of medicine. It represents the function and efficient of the heart and blood vessels in the body so any defect in this function will appear as a change in the speed of blood flow from the normal value assumed. As this speed changes alot in cases of  disease and morbidity  of the heart, so in order to identify the effect of changing the Doppler frequency on the speed of blood flow and the relationship of