Copper oxide (CuO) nanoparticles were synthesized through the thermal decomposition of a copper(II) Schiff-base complex. The complex was formed by reacting cupric acetate with a Schiff base in a 2:1 metal-to-ligand ratio. The Schiff base itself was synthesized via the condensation of benzidine and 2-hydroxybenzaldehyde in the presence of glacial acetic acid. This newly synthesized symmetric Schiff base served as the ligand for the Cu(II) metal ion complex. The ligand and its complex were characterized using several spectroscopic methods, including FTIR, UV-vis, 1H-NMR, 13C-NMR, CHNS, and AAS, along with TGA, molar conductivity and magnetic susceptibility measurements. The CuO nanoparticles were produced by thermally decomposing the

Hypothesis Nanofluid flooding has been identified as a promising method for enhanced oil recovery (EOR) and improved Carbon geo-sequestration (CGS). However, it is unclear how nanoparticles (NPs) influence the CO2-brine interfacial tension (γ), which is a key parameter in pore-to reservoirs-scale fluid dynamics, and consequently project success. The effects of pressure, temperature, salinity, and NPs concentration on CO2-silica (hydrophilic or hydrophobic) nanofluid γ was thus systematically investigated to understand the influence of nanofluid flooding on CO2 geo-storage. Experiments Pendant drop method was used to measure CO2/nanofluid γ at carbon storage conditions using high pressure-high temperature optical cell. Findings CO2/nano

Copper oxide (CuO) nanoparticles were synthesized through the thermal decomposition of a copper(II) Schiff-base complex. The complex was formed by reacting cupric acetate with a Schiff base in a 2:1 metal-to-ligand ratio. The Schiff base itself was synthesized via the condensation of benzidine and 2-hydroxybenzaldehyde in the presence of glacial acetic acid. This newly synthesized symmetric Schiff base served as the ligand for the Cu(II) metal ion complex. The ligand and its complex were characterized using several spectroscopic methods, including FTIR, UV-vis, 1H-NMR, 13C-NMR, CHNS, and AAS, along with TGA, molar conductivity and magnetic susceptibility measurements. The CuO nanoparticles were produced by thermally decomposing the

This study includes using green or biosynthesis-friendly technology, which is effective in terms of low cost and low time and energy to prepare V₂O₅NPs nanoparticles from vanadium sulfate VSO₄.H₂O using aqueous extract of Punica Granatum at a concentration of 0.1M and with a basic medium PH= 8-12. The V₂O₅NPs nanoparticles were diagnosed using several techniques, such as FT-IR, UV-visible with energy gap Eg = 3.734eV, and the X-Ray diffraction XRD was calculated using the Debye Scherrer equation. It was discovered to be 34.39nm, Scanning Electron Microscope (SEM), Transmission Electron Microscopy TEM. The size, structure, and composition of synthetic V₂O₅

This work analyzes the impact of MgO nanoparticles on the properties of an epoxy resin solution with uniform structure and particular degree of cure synthesized by the reaction of epoxy resin and pyromellitic dianhydride. Various concentrations of epoxy/MgO nanocomposites were fabricated by mechanical mixing, ultrasonication-based dispersion and casting processes. FTIR results have shown clear differences in the vibrations of C-H, epoxide rings, and main amine N-H groups. This confirms the interaction between MgO particles and the epoxy polymer matrix. X-ray diffraction analysis detected prominent peak at 18.35 degrees, along with additional ones at 43.44 degrees and 62.56 degrees, associated with the (200) and (220) planes of MgO crystal,

Wastewater discharge containing organic dyes may pose a hazard to the environment, which necessitates that dye removal must occur prior to wastewater release into water bodies. Herein, copper oxide nanoparticles (CuO NPs) were prepared by a green precipitation method to enable decolorization of a cationic dye (methyl violet; MV) from aqueous media. Complementary tools were employed to characterize the CuO NPs adsorbent: spectroscopy (FTIR and UV-VIS), microscopy (FESEM and TEM), XRD, BET surface area analysis, and point of zero charge (pHPZC) via potentiometry. The FTIR bands at 722, 663, 569, and 465 cm−1 correspond to the vibrational modes of CuO NPs, along with the optical absorbance band at 275 nm that supports the formation of Cu

Wastewater discharge containing organic dyes may pose a hazard to the environment, which necessitates that dye removal must occur prior to wastewater release into water bodies. Herein, copper oxide nanoparticles (CuO NPs) were prepared by a green precipitation method to enable decolorization of a cationic dye (methyl violet; MV) from aqueous media. Complementary tools were employed to characterize the CuO NPs adsorbent: spectroscopy (FTIR and UV-VIS), microscopy (FESEM and TEM), XRD, BET surface area analysis, and point of zero charge (pHPZC) via potentiometry. The FTIR bands at 722, 663, 569, and 465 cm1 correspond to the vibrational modes of CuO NPs, along with the optical absorbance band at 275 nm that supports the formation of CuO NPs.

This assay rapidly detects chlorpromazine hydrochloride using its ability to reduce gold ions to form nanoparticles. Its low cost, resilience to interferences and short analysis time could facilitate environmental monitoring and biomedical analysis.