Cadmium oxide thin films were prepared by D.C magnetron plasma sputtering using different voltages (700, 800, 900, 1000, 1100 and 1200) Volt. The Cadmium oxide structural properties using XRD analysis for just a voltage of 1200 volt at room temperature after annealing in different temperatures (523 and 623) K were studied .The results show that the films prepared at room temperature have some peaks belong to cadmium element along the directions (002), (100), (102) and (103) while the other peaks along the directions of (111), (200) and (222) belong to cadmium oxide. Annealed samples display only cadmium oxide peaks. Also, the spectroscopic properties of plasma diagnostic for CdO thin films were determined and the results show that the el

Complexes of the Cr(III), Fe(III), Rh(III), Ru (III), Mo hexagonal valence and Co(II) were prepared using the azo dye 1,1'-(1,3-phenylene bis(diazene-2,1-diyl))bis(2,4,6-trihydroxy-3,1-phenylene))bis(ethan-1-one), which was prepared newly from diazonium salt with 2,4,6-trihydroxyacetophenone, after isolation. The compounds were characterized using proton and carbon nuclear magnetic resonance of the ligand and fine elemental analysis, infrared, ultraviolet-visible, mass measurement, thermogravimetric analysis, differential thermal scanning, metal percentage determination, chlorine content determination, magnetic susceptibility, and molar conductivity. The results showed that the tetra coordinated anionic bond, when linked to metal ions via t

Prostate cancer (PC), accounts for more than one-fourth of all cancer diagnoses, and the most frequently diagnosed cancer among men in 2022. The immunoglobulin (IG) Program death ligand-1(PD-1) cell surface receptor is predominantly expressed on the surface of many cells. The purpose of this study was to demonstrate the relationship between Program death ligand expression and some aggressive features of prostate cancer including perineural invasion, vascular invasion and necrosis. Thirty cases of prostate cancer with age range from 60 to 80 year old and 30 cases of normal prostate tissue with age under 25 year old were separated into two groups in a retrospective case-control

Background: Poly (methylmethacrylate) is not ideal in every aspect and has disadvantages such as insufficient surface hardness, increase water sorption and poor impact resistance and the latter being the primary cause of fracture of denture base resins. The aim of this study was to evaluate the effect of addition of silanized nano- hydroxyapatite (HA) on some properties of heat cured acrylic denture base material. Materials and methods: HA nano particles were first silanized with MPS (tri methacryloxypropyletrimethoxy silane coupling agent) then ultrasonicated with methylmethacrylate (monomer) to disperse agglomerated nano particles and mixed with polymer. 2% by wt of HA nano particles was selected as the best concentration that add

A series of 4-(methylsulfonyl)aniline derivatives were synthesized in order to obtain new compounds as a potential anti-inflammatory agents with expected selectivity against COX-2 enzyme. In vivo acute anti-inflammatory activity of the final compounds 11–14 was evaluated in rat using an egg-white induced edema model of inflammation in a dose equivalent to 3 mg/Kg of diclofenac sodium. All tested compounds produced significant reduction of paw edema with respect to the effect of propylene glycol 50% v/v (control group). Moreover, the activity of compounds 11 and 14 was significantly higher than that of diclofenac sodium (at 3 mg/Kg) in the 120–300 minute time interval, while compound 12 expressed a comparable effect to that of di

Reaction of,2- [( 4- amio phenyl ) diazenyl] 1,3,4- thiadiazole -5- thiol (S1) with p- chlorobenzeldehyde,3,4 – dimethoxy benzaldehyde and pyrrol-2- carbonxaldehyde gave -5- [{4-(4-chlorobenzylidene amino) phenyl} diezenyl]-1,3,4- thiadiazole-2- thiol (S2),5-[{ 4-[(3,4- dimethoxybenzyldene )amino phenyl ] diazenyl)-1,3,4- thiadiazole-2-thiol,(S3) and -5- [4-(1,H – pyrrol -2- yl- methylene)amino phenyl] diazenyl)-1,3,4- thiadiazole-2- thiol (S4) respectively as schiff's bases compounds. On the same route-2-[(4-amino-1- naphthyl ) diazenyl] -1,3,4- thiadiazole -5- thiol (S5) reacts with –p- chloro benzaldehyde and –m- nitrobenzaldehyde to give the follwing schiff's bases -5-[{ 4-(4- chloro benzylidene ) amino -1- naphthyl} diazenyl]