M(II) Ions using amino acid L- proline as a primary ligand and either Nicotinamide or 8- hydroxyqinoline as secondary ligand, respectively: a. The mixed ligand complexes of composition,[M(pro)2(na)2]. b. The mixed ligand complexes of composition , Na[M(pro)2(Q)]. Where proline (C5H9NO2) symbolized as pro H , Nicotinamide (C6H6N2O) symbolized as (NA) , 8- hydroxyqinoline, (C9H7NO2) symbolized as (8-HQ). The ligands and the metal chlorides were brought into reaction at room temperature (37ºc) in ethanol as solvent .The reaction required the following molar ratios [(1:2:2) metal:2NA:2pro-] and [(1:1:2) metal:Q:2pro-] with M+2 ions, where M = [Mn (II), Co(II), Ni(II), Cu(II), Zn(II), Cd(II) and pd(II)]. Products were found to be solid crystall

In the present work, the phthalic acid (phthH2) and 1.10 phenonthroline (phen), and their complexes were synthesized and isolated as [M(phth)(phen)2], Mn(II), Fe(II), Co(II), Ni(II) Cu(II), Zn(II), and Cd(II) ions. These complexes were characterized by elemental analysis, melting point, conductivity, percentage metal, UV–Vis, FT-IR, and magnetic moment measurements. The molar conductance indicates that all the metal complexes in DMSO are nonelectrolytic. phthalic acid (phtha), and 1,10-Phenanthroline (phen), behaved as bidentate, coordinating to the metal ion through their two oxygen and two pyridinyl nitrogen atoms respectively, as corroborated by. Electronic spectra, FTIR, spectroscopy amusement indicated that all the metal complexes ad

Abstract 

Locally natural occurring Iraqi rocks of Bauxite and Porcelanite (after pre calcinations at 1000^oC for 1hr) were used, with the addition of different proportions of MgO and Al₂O₃, to prepare refractory materials. The effects of these additives on the physical and thermal properties of the prepared refractories were investigated.

Many batches of Bauxite/MgO, Bauxite/Al₂O₃, Bauxite/MgO/Al₂O₃, and   Porcelanite/ MgO/Al₂O₃ were prepared. The mixture is milled and classified into different size fractions; fine (less than 45μm) 40%, middle (45-75μm) 40%, and coarse (75-106μm) 20% .

Preparation of epoxy/MgO and epoxy/SiO2 nanocomposites is
studding. The nano composites were processed by different nano
fillers concentrations (0, 0.01, 0.02, 0.03, 0.04, 0.05, 0.07 and
0.1 wt%). Epoxy resin and nanocomposites containing different
shape nano fillers of (MgO:SiO2 composites), are shear mixing with
ratio 1:1,with different nano hybrid fillers concentrations (0.025,
0.05, 0.1, 0.15, 0.2 and 0.25 wt%) to preparation of epoxy/(MgOSiO2)
hybrid nanocomposites. Experimental tests results indicate that
the composite materials have significantly higher modulus of
elasticity than the matrix material but the hybrid nanocomposites
have lower modulus of elasticity. The wear rate was decreased in
nanoc

         Recently, emulgel has emerged as one of the most interesting topical preparations in the field of pharmaceutics. In this research clotrimazole was formulated as topically applied emulgel ; different formulas were prepared. The prepared emulgels were evaluated for their physical appearance , rheological behaviour , and in vitro drug release . The influence of the type of gelling agent (carbopol 934 and methyl cellulose), the concentration of both the emulsifying agent (2% and 4% w/w of mixture of span 20 and tween 20) and the oil phase (5% and 7.5% w/w of liquid paraffin) and the type of oil phase (liquid paraffin and cetyl alcohol), on the drug release from the prepared emulgels was invest

Background. Material tribology has widely expanded in scope and depth and is extended from the mechanical field to the biomedical field. The present study aimed to characterize the nanocoating of highly pure (99.9%) niobium (Nb), tantalum (Ta), and vanadium (V) deposited on 316L stainless steel (SS) substrates which considered the most widely used alloys in the manufacturing of SS orthodontic components. To date, the coating of SS orthodontic archwires with Nb, Ta, and V using a plasma sputtering method has never been reported. Nanodeposition was performed using a DC plasma sputtering system with three different sputtering times (1, 2, and 3 hours). Results. Structural and elemental analyses were conducted on the deposited coating