Bacteria strain H8, which produces high amount of exopolysaccharide (EPS), was isolated from soil, and identified as strain of Azotobacter chrococcum by its biochemical /physiological characteristics, EPS was extracted, partially purified and used as bioflocculant. The biochemical analysis of the partially purified EPS revealed that it was an alginate. analysis of EPS by Fourier transform infrared spectrometry (FTIR) show that the -OH groups present in bioflocculant are clearly seen at 3433.06 cm-1, the peaks attributed to the -CH3 groups present at 2916.17 cm-1 , and some distinct peaks such as carboxyl group showed strong absorption bands at 1604.66 cm-1, 1411.80 cm-1 and 1303.79 cm-1 indicate the chemical structure of alginate. The effects of various salts, temperature, bioflocculant dosage and pH on the flocculation activity (turbidity removal) were evaluated. When various salts, were used as cation, results showed that CaCl2 and ZnSO4.7H2O enhanced flocculation activity 57.3% and 55.3% respectively compared with CuSO4 and MnCl2 which was 37.5% and 10 % respectively. The bioflocculant had strong thermal stability within the range of 20-100 °C, and the flocculating activity was over 50 %, the maximum flocculation activity was observed at an optimum bioflocculant dosage of 0.25 mL /10 mL (60.8%)., the bioflocculant had highest flocculating activity at alkaline condition pH 10 (77.7 %). After optimization of flocculation conditions, bioflocculant produced was applied to deal with river water and the flocculating activity (turbidity removal) increased to 81%.
This paper presents two main parts: The first part involves manufacturing the specimens form composite material for mechanical testing (tensile, flexural and fatigue tests), then design a custom foot orthesis (CFO) and manufacturing from composite lamination (3nylglass 2carbon fiber 3nylglass) for patient suffer from flexible flat foot since birth and over-pronation. The second part of this research involves a design a model of custom foot orthesis in (solid work 2018) and then analysis of custom foot orthosis in engineering analysis program (ANSYS V.18.2).The applied pressure in boundary condition adopted from Force Sensor Resistance (FSR 402 ) in various regions in foot after wearing composite CFO. Used a composite materials in engineerin
... Show More
(2)
A particulate composite material was prepared by adding the Titanium dioxide (TiO2) with a particle size of (75-150) µm to Epoxy resin at weight percentage of (10%,20%,30%,40%,50%).The following some mechanical properties were studied,fracture toughness, hardness.casting preparation methods were used in this study includes preparing plate of matrix and composites. specimens were prepared according to ASTM for the Mechanical properties tests. After that Another samples were heat treated for three and six hour at 65C?. Fracture toughness (Kic) represent for stress intensity factor results were showed that the curve of three hours aging increases in fracture toughness (Kic) for composites but for six hours aging increases fracture tough
... Show More
For any group G, we define G/H (read” G mod H”) to be the set of left cosets of H in G and this set forms a group under the operation (a)(bH) = abH. The character table of rational representations study to gain the K( SL(2,81)) and K( SL(2, 729)) in this work.
(11)
Agent technology has a widespread usage in most of computerized systems. In this paper agent technology has been applied to monitor wear test for an aluminium silicon alloy which is used in automotive parts and gears of light loads. In addition to wear test monitoring، porosity effect on
wear resistance has been investigated. To get a controlled amount of porosity, the specimens have
been made by powder metallurgy process with various pressures (100, 200 and 600) MPa. The aim of
this investigation is a proactive step to avoid the failure occurrence by the porosity.
A dry wear tests have been achieved by subjecting three reciprocated loads (1000, 1500 and 2000)g
for three periods (10, 45 and 90)min. The weight difference a
The development of Japanese society passed through long historical stages and as a result of the bitter experience of Japan in the Second World War and its exhaustion, it was able to build a modern modern state after 1945. Japan is a country of culture, civilization, science and technology, a country that appreciates the value of solidarity work. And the role of active civil society. This is what makes us in Iraq stand and draw their experience in the advancement and development, especially that they also passed bitter political stages, Iraq today passes through the most historical periods of forestry through its historical heritage in terms of the existence of complex social problems, the US occupation of Iraq in 2003 highlighte
... Show More
Polymer films of PEG and PVA and their blend with different
concentrations of MnCl2 (0, 2, 4, 6 and 10 %.wt) were study using
casting technique. The X-ray spectra of pure PEG, PVA and
PVA:PEG films and with addition of 2% concentrations from
(MnCl2) show amorphous structures. The results for FTIR show the
interaction between the filler and polymer blend results in
decreasing crystallinity with rich amorphous phase. This
amorphous nature confirms the complexation between the filler and
the polymer blend. The optical properties of (PVA:PEG/MnCl2)
contain the recording of absorbance (A) and explain that the
absorption coefficient (α), refractive index (n), extinction coefficient
(ko) and the dielectric cons