A new Turbidimetric method characterized by simplicity, accuracy and speed for determination of Hydronium ion by continuous flow injection analysis. The method was based on the formation of complex Zn3[Fe(CN)6] for Zinc(II) that was eluted by Hydronium ion from cation exchanger column with Potassium hexacyanoferrate(III) for the formation of a pale yellow precipitate and this precipitate was determined using homemade Linear Array Ayah-5SX1-T-1D continuous flow injection analyser. The optimum parameters were 2.7 mL.min-1 flow rate using H2O as a carrier stream, 1.7 mL.min-1 reagent stream, 110 L sample volume and open valve for the purge of the sample segment. Data treatment shows that linear range 0.01-0.1 mol.L-1 for each acids (HClO

    The ion-pair formation method has been applied for the spectrophotometric determination of Cimetidine and Erythromycin ethylsuccinate, in bulk samples and in dosage form. The methods are accurate, simple, rapid, inexpensive and sensitive depending on the extraction of the formed ion-pair with brompthymol blue (BTB) as a chromogenic reagent in chloroform, use phthalate buffer of pH 5.5 and 4.0 for Cimetidine and Erythromycin ethylsuccinate respectively.  The formed complexes show absorbance maxima at 427.5 nm and 414.5 nm for Cimetidine and Erythromycin ethylsuccinate respectively against reagent blank. The calibration graphs are linear in the ranges of 0.5-15 µg.mL-1 with detection limit of 0.222 µg.mL-1 for

     The change in the optical properties for samples of pure PVA and PVA /K2CrO4composite have been studied .The samples were prepared with different percentage (1,3,5,and 7)%wt of K2CrO4 by casting method technique .In this work ,we are study the absorption ,reflectance spectra ,absorption  coefficient, energy gap ,extinction coefficient ,and transmittance spectra as a function of wavelength range (200-800)nm ,Also  real and imaginary part of dielectric constant have been studied in the range of wave length .The results exhibit the optical properties change by the increase of K2CrO4 concentration, and the values of energy gap for indirect transitions decrease by the increase of the concentration of  K2CrO4

This paper deals with finite element modeling of the ultimate load behavior of double skin composite (DSC) slabs. In a DSC slab, shear connectors in the form of nut bolt technique studs are used to transfer shear between the outer skin made of steel plates and the concrete core. The current study is based on finite element analysis using ANSYS Version 11 APDL release computer program. Experimental programmes were carried out by the others, two simply supported DSC beams were tested until failure under a concentrated load applied at the center. These test specimens were analyzed by the finite element method and the analyses have shown that these slabs displayed a high degree of flexural characteristics, ultimate strength,

in this worl three types of complexed phenolic resins were prepared using various additives such as and improving the aim of this work higher mechanical properties this work is done

Compaction curves are widely used in civil engineering especially for road constructions, embankments, etc. Obtaining the precise amount of Optimum Moisture Content (OMC) that gives the Maximum Dry Unit weight g_dmax. is very important, where the desired soil strength can be achieved in addition to economic aspects.

In this paper, three peak functions were used to obtain the OMC and g_dmax. through curve fitting for the values obtained from Standard Proctor Test. Another surface fitting was also used to model the Ohio’s compaction curves that represent the very large variation of compacted soil types.

The results showed very good correlation between the values obtained from some publ

Microencapsulated of paraffin wax which acts as core material of phase change
material covered by polymer was prepared by using rabid (physical-chemical) with lower
energy (green) method. Prepolymer of condensed Melamine-Formaldehyde resin, was
solidified by heat effect gradually and surrounds the Paraffin wax as microcapsules. The
diameter of the prepared capsules was about (170-220) micron which has a proportion with
the prepolymer temperature, otherwise the thermal analysis appears as a best value of
enthalpy (ΔH) which was (12 J/gm) when the prepolymer temperature was (60˚C)