The process for preparing activated carbon (AC) made from tea residue was described in this paper. Investigated were the physicochemical characteristics and adsorption efficiency of the produced AC. Activation with potassium hydroxide (KOH) and carbonization at 350 °C are the two key steps in the manufacturing of AC. The activated carbon was used to adsorb Tetracycline (TC). Different parameters were studied at room temperature to show their effects on the adsorption efficiency of TC. These parameters are the initial concentration of adsorbate TC, solution acidity pH, time of adsorption, and adsorbent dosage. The prepared active carbon was characterized using Fourier transform infrared spectroscopy (FTIR), scanning electron microsc

The process for preparing activated carbon (AC) made from tea residue was described in this paper. Investigated were the physicochemical characteristics and adsorption efficiency of the produced AC. Activation with potassium hydroxide (KOH) and carbonization at 350 °C are the two key steps in the manufacturing of AC. The activated carbon was used to adsorb Tetracycline (TC). Different parameters were studied at room temperature to show their effects on the adsorption efficiency of TC. These parameters are the initial concentration of adsorbate TC, solution acidity pH, time of adsorption, and adsorbent dosage. The prepared active carbon was characterized using Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (

The synthesis of zeolite NaX from locally available kaolin has been studied. The operating conditions for zeolite NaX production from kaolin with good crystallinity were as follows; a gel formation step of metakaolin in alkaline medium in presence of additional silica to crystallize the zeolite was achieved at 60 oC for 1 hr,and with stirring. In ageing step of the reactants at room temperature for 5 days and crystallization step at 87±2 oC for 24 hr. The catalytic activity of catalyst prepared from local kaolin was studied by using cumene cracking as a model for catalytic cracking and compared with standard HY zeolite and HX zeolite catalysts. The activity test was carried out in a laboratory continuous flow unit with fixed bed re

The synthesis of zeolite NaX from locally available kaolin has been studied. The operating conditions for zeolite NaX production from kaolin with good crystallinity were as follows; a gel formation step of metakaolin in alkaline medium in presence of additional silica to crystallize the zeolite was achieved at 60 oC for 1 hr,and with stirring. In ageing step of the reactants at room temperature for 5 days and crystallization step at 87±2 oC for 24 hr. The catalytic activity of catalyst prepared from local kaolin was studied by using cumene cracking as a model for catalytic cracking and compared with standard HY zeolite and HX zeolite catalysts. The activity test was carried out in a laboratory continuous flow unit with fixed bed reactor

This work deals with the separation of benzene and toluene from a BTX fraction. The separation was carried out using adsorption by molecular sieve zeolite 13X in a fixed bed. The concentration of benzene and toluene in the influent streams was measured using gas chromatography. The effect of flow rate in the range 0.77 – 2.0 cm3/min on the benzene and toluene extraction from BTX fraction was studied. The flow rate increasing decreases the breakthrough and saturation times. The effect of bed height in the range 31.6 – 63.3 cm on benzene and toluene adsorption from BTX fraction was studied. The increase of bed height increasing increases the break point values. The effect of the concentration of benzene in the range 0.0559 – 0.2625g/

In the present work, the surface properties of mixed binary surfactants containing sodium dodecylbenzene sulfate (SDBS) and Tween 80 (TW80) surfactants in aqueous solutions were studied at temperature 293 K using surface tension measurements. The critical micelle concentration (cmc) magnitude for both individual surfactants and their mixtures were established the obtained results revealed  that the magnitude of cmc of the mixtures are less than the magnitude of individual surfactants and decrease with the increase in Tween 80 percent in solution which indicate the nonideal  mixing of the two surfactants. The values of molecular interaction parameters  and the mole fraction of surfactants in the micelle (X1) were calculated

The faujasite type Y zeolite catalyst was prepared from locally available kaolin. For prepared faujasite type NaY zeolite X-ray, FT-IR, BET pore volume and surface area, and silica/ alumina were determined. The Xray and FT-IR show the compatibility of prepared catalyst with the general structure of standard zeolite Y. BET test shows that the surface area and pore volume of prepared catalyst were 360 m2 /g and 0.39 cm3 /g respectively.
The prepared faujasite type NaY zeolite modified by exchanging sodium ion with ammonium ion using ammonium nitrate and then ammonium ion converted to hydrogen ion. The maximum sodium ion exchange with ammonium ion was 53.6%. The catalytic activity of prepared faujasite type NaY, NaNH4Y and NaHY zeolites

This study was conducted to prepare protein concentrates from AL-Zahdidate’s pits by using alkaline methods where the chemical composition of the pits were (7.30, 1.04, 5.80, 8.68 and 77.19) % for each of the moisture, ash, protein, fat and carbohydrates respectively and the chemical composition of the concentrate protein was (6.62, 4.10, 26.70, 0.93, and 58.65) % respectively. The content of protein concentrate from the metallic elements (144.07, 25.11, 15.02, 0.49, 0.59, 0.27, 0.22 and 234.6) mg/ 100 g each of potassium, magnesium, calcium, iron, manganese, copper, zinc and phosphorus respectively. The results of SDS-PAGE showed five bands with weights molecular ranged between 11000-70000 Dalton. Give the biscuit which contain protei