Rare earth elements (Cerium, Lanthanum and Neodymium) doped CdS thin films are prepared using the chemical Spray Pyrolysis Method with temperature 200 oC. The X-ray diffraction (XRD) analysis refers that pure CdS and CdS:Ce, CdS:La and CdS:Nd thin films showed the hexagonal crystalline phase. The crystallite size determined by the Debye-Scherrer equation and the range was (35.8– 23.76 nm), and it was confirmed by field emission scanning electron microscopy (FE-SEM). The pure and doped CdS shows a direct band gap (2.57 to 2.72 eV), which was obtained by transmittance. The room-temperature photoluminescence of pure and doped CdS shows large peak at 431 nm, and two small peaks at (530 and 610 nm). The Current – voltage measurement in da

Thin filis have been prepared from the tin disulphide (SnS2 ), the pure and the doped with copper (SnS2:Cu) with a percentages (1,2,3,4)% by using ahemical spray pyrolysis techniqee on substrate of glass heated up to(603K)and sith thicknesses (0.7±0.02)?m ,after that the films were treated thermally with a low pressure (10-3mb) and at a temperature of (473K) for one hour. The influence of both doping with copper and the thermal treatment on some of the physical characteristics of the prepared films(structural and optical) was studied. The X-ray analysis showed that the prepared films were polycrystalline Hexagonal type. The optical study that included the absorptance and transmitance spectra in the weavelength range (300-900)nm

CdS and CdS:Sn thin films were successfully deposited on glass
substrates by spray pyrolysis method. The films were grown at
substrate temperatures 300 C°. The effects of Sn concentration on the
structural and optical properties were studied.
The XRD profiles showed that the films are polycrystalline with
hexagonal structure grown preferentially along the (002) axis. The
optical studies exhibit direct allowed transition. Energy band gap
vary from 3.2 to 2.7 eV.

This work used the deposition method to synthesize nickel oxide nanoparticles. The materials mainly used in this study were nickel sulfate hexahydrate (as a precursor) and NaOH (as a precipitant). The properties of the nanopowder were characterized by XRD, FE-SEM, EDX, and VSM. The obtained results confirmed the presence of nickel oxide nanoparticles with a face-centered cubic (FCC) structure with a lattice constant (a=4.17834 Å). Scherer and Williamson-Hall equations were used to calculate the crystallite size of about (30.5-35.5) nm. The FE-SEM images showed that the particle shape had a ball-like appearance with a uniform and homogeneous distribution and confirmed that the particles were within the nanoscale. The presence of oxygen a

ZnO nanostructures were synthesized by hydrothermal method at different temperatures and growth times. The effect of increasing the temperature on structural and optical properties of ZnO were analyzed and discussed. The prepared ZnO nanostructures were characterized by X-ray diffraction (XRD), UV–Vis. absorption spectroscopy (UV–Vis.), Photoluminescence (PL), and scanning electron microscopy (SEM). In this work, hexagonal crystal structure prepared ZnO nanostructures was observed using X-ray diffraction (XRD) and the average crystallite size equal 14.7 and 23.8 nm for samples synthesized at growth time 7 and 8 hours respectively. A nanotubes-shaped surface morphology was found using scanning electron microscopy (SEM). The optic

New 2-amino thiazole ,oxodiazole, sulphonilamide and diazin derivatives of N-(α-chloro aceto)-3-(tolyl imino)-5-bromo-2-oxo-indole(2) have been synthesized .The preparation process started by the reaction of 5-bromo isatin with  P-toluidine in the presence of glacial acetic acid and dimethylformamide(DMF) as a solvent to give  3-(tolyl imino)5-bromo-1H-indole-2-one.(1), Compound (1) with sodium hydride  in dimethylformamide(DMF) at 0C0 gave a suspension of the sodium salt of Schiff base derivative and subsequent reaction with monochloroacetylchloride obtained  the intermediate compound(2).Compound(2) was  reacted with different reagents  in four routes.The first route involved direct reaction with substituted  2-aminobenzothiazole u

New biscarboxylato zwitterionic ligands, namely bis(N-carboxylatoethyl)-4,4 -dipyridinum) L1 and bis(Ncarboxylatopropyl)-)-4,4 -dipyridinum) L2, were synthesized from the reaction of 4,4 -dipyridine with 3-bromopropanoic acid and 4-bromobutanoic acid, respectively. The reaction of these ligands and the azido coligand with some metal ions resulted in the formation of polymeric complexes of general formulae [Cr2(Ln)(N3)4]Cl2·H2O and [M2(Ln)(N3)4] xH2O, where (M = Mn(II), Fe(II), Co(II), Ni(II), Cu(II), Zn(II) and Cd(II); n = 1, 2; x = 1, 1, 1, 1, 0, 1, and 1, respectively.) The oxygens of the carboxylato group are coordinated to the metal ion in a bidentate fashion. The mode of bonding and overall geometry of the complexes were determin

Using an electrochemical polymerization technique at room temperature, poly nicotine amide (PNA) was produced from the monomer nicotine amide (NA) in aqueous solution. The structure of polymer layer generated on the stainless steel surface (316 L) (working electrode) is investigated by Fourier Transmission Infrared Region (FT-IR). The anti-corrosion activity of polymer coating on the stainless steel (SS 316 L) is investigated by electrochemical polarization in 0.20M solution of HCl at 293-323K. The graphene -modified polymer film-coated SS had greater protection efficiency (PE percent) when compared to Nano ZnO -modified polymer film-coated SS. For the corrosion process of SS 316 L, kinetic and thermo-dynamic parameters of activation are