The goal of the current study was to research the changes in hematological parameters: WBC count, RBCs count, Hb, PCV, neutrophil, lymphocyte, and monocyte in albino mice infected with Aspergillus fumigatus by intraperitoneal injection after induced immunosuppression by intraperitoneal injection of cortisone. The current research also examined an attempt to reduce the infection load by treating Solanum aculeastrum. The result shows higher decreased significance (P≤0. 05) in RBCs, Hb, and PCV after being infected with A. fumigatus 7. 1 ± 0. 8, 11. 3 ± 0. 5 and 41. 5 ± 2. 4, respectively, while the total WBC count, neutrophil, lymphocyte, and monocytes were increased significantly (P≤0. 05) after treatment with S. aculeastrum i

In this work, 332 Al alloy was prepared and reinforced with (0.5% and 1%) nano-Al₂O₃ particles. The prepared unreinforced and reinforced 332 Al alloy with nano-Al₂O₃ were solution heat treated (T6) at 510 ̊C and aged at 225 ̊C with different times (1, 3, and 5 h). Hardness test was performed on all the prepared alloys. All prepared alloys were dry slided under different applied loads (5, 10, 15, and 20 N) against steel counterface surface using pin on disk apparatus. The results showed that refinement effect was observed after addition of nano-Al₂O₃ particles and a change in silicon morphology after performing the solution heat treatment. The results also showed that har

The optical properties for the components CuIn(SexTe1-x)2 thin films with both values of selenium content (x) [0.4 and 0.6] are studied. The films have been prepared by the vacuum thermal evaporation method with thickness of (250±5nm) on glass substrates. From the transmittance and absorbance spectra within the range of wavelength (400-900)nm, we determined the forbidden optical energy gap (Egopt) and the constant (B). From the studyingthe relation between absorption coefficient (α) photon energy, we determined the tails width inside the energy gap.
The results showed that the optical transition is direct; we also found that the optical energy gap increases with annealing temperature and selenium content (x). However, the width of l

loaded reinforced concrete circular short columns. An experimental investigation into the behavior
of 24 short reinforced concrete columns with and without steel fibers was carried out. The columns
had a circular section (200 mm diameter and 900 mm long). Test variables include concrete
strength, spacing of spiral reinforcement, and inclusion of steel fibers. The axial stress and axial
strains were obtained and used to evaluate the effects of the presence of steel fibers. It was found
that the addition of steel fibers slightly improves the load carrying capacity of the tested columns
whereas it significantly enhances the ductility of these specimens. Test results also indicated that for
the same confinement parameter

This study was conducted to study the cytogenetic effect of both alcoholic and water extracts of propolis on mice. Three different samples of propolis were collected from three different regions of Iraq (Najaf, Arbil and Baghdad) to be used in this study. The cytotoxic effect of two different doses of each extracted sample was measured by employing cytogenetic analysis which included (mitotic index (MI), chromosomal aberrations (CAs), micronucleus index (MN) and sperm abnormalities). Results showed that significant increase in MI and significant reduction in MN, CAs and sperm abnormalities percentage were seen after treatment with both alcoholic and water extract of the three samples when compared with negative control, and alcoholic extrac

Epoxy (EP) – Silica (SiO2) composites are well known composites used in microelectronic industry . So it is important to study their dielectric behavior under different conditions such as
the presence carbon black (UV absorber) and immersion in the water for 30 days .
Dielectric properties were calculated over the frequency range 102 – 106 Hz for epoxy composites with different weight % of micrometer 1.5μm SiO2 particles (60%, 65% and 70wt%) modified with 0.5wt% silane coupling agent to improve adhesion between EP and SiO2 phases .