Background: One of the most common problem associated with the used of soft denture lining material is microorganisms and fungal growth especially Candida albicans, which can result in chronic mucosal inflammation. The aim of this study was to evaluate the influence of chlorhexidine diacetate (CDA) salt Incorporation into soft denture lining material on antifungal activity; against Candida albicans, and the amount of chlorhexidine di-acetate salt leached out of soft liner/CDA composite. Furthermore, evaluate shear bond strength and hardness after CDA addition to soft liner Materials and methods: chlorhexidine diacetate salt was added to soft denture lining material at four different concentrations (0.05%, 0.1% and 0.2% by weight). Four hund

Background: Antimicrobial agents have been considered as having potential for the prevention of dental caries. This study aimed to test the effect of different concentrations of cardamom and black tea extracts on the sensitivity and growth of salivary mutans streptococci in comparison to chlorhexidine gluconate (0.2%) in vitro. Materials and methods: In this study. Mutans streptococci were isolated from saliva of 34 healthy people (aged between 22-40yrs). The bacteria was isolated, purifiedand diagnosed according to morphologicalcharacteristic and biochemical tests. Aqueous extracts of cardamom and black tea were prepared. Different concentrations of extracts were prepared and estimated in gm/ 100ml deionized water. The agar diffusion techn

The study included adding antimony oxide to mixtures of coating metal surfaces (Enameling), after it was selected ceramic materials used in the coating metal pieces of the type of steel and cast iron in two layers. The first is called a ground coat and the second is a cover coat.
Ceramic materials layer for ground coat have been melted down in
platinum crucible at a temperature of 1200oC to prepare the glass
mixture (Frit). It was coated on metals at a temperature of 780oC for
two minutes, while the second layer was prepared glass mixture
(Frit) at a temperature of 1200oC, but was coated at a temperature of
760oC for two minutes.
Underwent tests crystalline state of powders (Frits) and enameled samples using X-ray di

Co-crystals are new solid forms of drugs that could resolve more than one problem associated with drugs formulations like solubility, stability, bioavailability, mechanical and tableting properties. A preliminary theoretical study for estimating the possible bonding between the co-crystal components (paracetamol and naproxen) was performed using the ChemOffice program. The results revealed a high possibility for bonding between paracetamol and naproxen and indicated the ability of molecular mechanics study to predict the co-crystal design.

       In this work, four different methods were used for the preparation of three different ratios 1:1, 2:1, and 1:2 of paracetamol:naproxen co-crystals. The four

The aim: to evaluate combined microscopy techniques for determining the morphological and optical properties of methadone hydrochloride (MDN) crystals. Materials and methods: MDN crystal formation was optimized using a closed container method and crystals were characterized using polarized light microscope (PLM), scanning electron microscopy (SEM) and confocal microscopy (CM). SEM and CM were used to determine MDN crystal thickness and study its relationship with crystal retardation colours using the Michel-Levy Birefringence approach. Results: Dimensions (mean±SD) of diamond shaped MDN crystals were confirmed using SEM and CM. Crystals were 46.4±15.2 Vs 32.0±8.3 µm long, 28.03±8.2 Vs 20.85±5.5 µm wide, and 6.62±