In this work the structural, electrical and optical Properties of CuO semiconductor films had been studied, which prepared at three thickness (100, 200 and 500 nm) by spray pyrolysis method at 573K substrate temperatures on glass substrates from 0.2M CuCl2•2H2O dissolved in alcohol. Structural Properties shows that the films have only a polycrystalline CuO phase with preferential orientation in the (111) direction, the dc conductivity shows that all films have two activation energies, Ea1 (0.45-0.66 eV) and Ea2 (0.055-.0185 eV), CuO films have CBH (Correlated Barrier Hopping) mechanism for ac-conductivity. The energy gap between (1.5-1.85 eV).

The corrosion behavior of copper and carbon steel in 1M concentration of hydrochloric acid (HCl) and sulphuric acid (H2SO4) has been studied. The corrosion inhibition of copper and carbon steel in 1M concentration of hydrochloric acid (HCl) and sulphuric acid (H2SO4) by Ciprofloxacin has been investigated. Specimens were exposed in the acidic media for 7 hours and corrosion rates evaluated by using the weight loss method. The effect of temperature (from 283 ºK to 333 ºK), pH (from 1to 6), inhibitor concentration (10-4 to 10-2) has been studied. It was observed that sulphuric acid environment was most corrosive to the metals because of its oxidizing nature, followed by hydrochloric acid. The rate of metal dissolution increased with incre

Efficacy of Varnishes with: Bioactive Glass, Recaldent Technology and Silver Diamine Fluoride in Comparison with Sodium Fluoride on Tooth Surface Micro-hardness (an In Vitro Study)

Axial spondyloarthritis (axSpA) is a chronic rheumatic inflammatory disease affecting mainly the spine and sacroiliac joints. Since the copper-to-zinc ratio (Cu/Zn) indicates an inflammatory response, the change in ratio is expected to correlate with axSpA. This study compared levels of Cu/Zn in the serum of axSpA patients. Serum samples were obtained from 53 patients with axSpA divided according to biological treatment into cohorts A and B, and 28 healthy control as cohort C. Serum levels of Cu and Zn were determined first by a fully automated chemistry analyzer TC-Matrix Plus, then the ratio was obtained. The elevated serum Cu concentration means of cohort B (189.32 ± 13.808 µg/dL) compared to cohort A (168.85 ± 7.244 µg/dL) a

In this study, polymeric composites were prepared from unsaturated polyester as a base material with glass powder (fluorescent) in different weight ratios (4, 6, 8, 10,and 11%) as a support material and after comparison before and after reinforcement of the prepared composites, an increase was found. In the values ​​of mechanical properties (hardness, compressive strength), the shock resistance values ​​decreased, but an increase in temperature leads to an increase in the values ​​of shock resistance, as well as the values ​​of compressive strength And it reduces the hardness value.

In the present research, the electrical properties which included the ac-conductivity (σac), loss tangent of dielectric (tan δ) and real dielectric constant (ε’) are studied for nano polycarbonate in different pressures and frequencies as a function of temperature these properties were studied at selective temperature gradients which are (RT-50-100-150-250)°C. The results of the study showed that the values of dielectric constant and dissipation factor increase with increasing pressure and temperature and decreases by increasing frequency. And the results of electrical conductivity showed that it increases with increasing temperature, pressure and frequency.

Samples prepared by using carbon black as a filler material and phenolic resin as a binder. The samples were pressed in a (3) cm diameter cylindrical die to (250)MPa and treated thermally within temperature range of (600-1000)oC for two and three hours. Physical properties tests were performed, like density, porosity, and X-ray tests. Moreover vicker microhardness and electric resistivity tests were done. From the results, it can be concluded that density was increased while porosity was decreased gradually with increasing temperature and treating time. In microhardness test, it found that more temperature and treating time cause more hardness. Finally the resistivity was decreased in steps with temperature and treating time. It can be c

The present study aimed to explain the dose-dependent possible deleterious effects of 30 day administration of Tramadol on some hematological and biochemical parameters of laboratory male rats (Rattus norvegicus), the study consisted of eighteen adult male rats randomly divided into three equal groups (each of six). Group 1 (control) were treated by intraperitoneal injection of normal saline solution (0.2 ml), group two (low dose) was treated by intraperitonealy (i.p) injection of Tramadol at a dose of 50 mg/kg/day, group three (high dose) was treated by intraperitonealy injection of Tramadol at a dose of 100 mg/kg/day for 30 days. At the end of experimental period, rats were sacrificed. Blood were collected by cardiac puncture to inv

In this study porcelain was prepared by using composition consisting of raw materials with in following fractions , 50% kaolin , 25% feldspar, and 25% silica( SiO2) tested by XRay diffraction (XRD) method .Study the effect additives at different concentration from zirconia (ZrO2) (2,5,10,15,20) Wt% on some physical properties of porcelain, the sample is prepared by the conventional manufacturing method , It is found that some physical properties of porcelain changes considerably with the substituent sample, It was found that the increase of zrconia (ZrO2) additive of all our sample produce. Increasing in dielectric constant and bulk density and decreasing with open porosity and dielectric loss tangent