This study presents the effect of laser energy on burning loss of magnesium from the holes' drilled in aluminum alloy 5052. High energy free running pulsed Nd:Glass laser of 300 µs pulse duration has been used to perform the experiments. The laser energy was varied from 1.0 to 8.0 Joules, The drilling processes have been carried out under atmospheric pressure and vacuum inside a specially designed chamber. Microhardness of the blind drilled holes has been investigated .The results indicated that the magnesium loss could be manipulated by adjusting the focusing conditions of the laser beam. Almost, the obtained holes were free of cracks with low taper and low sputter deposition. .The holes performed under atmospheric conditions have high

Aim: surface modification of titanium using fiber laser 1064 nm to enhance the bond strength to resin cement. Material and Methods: thirty titanium discs of 0.6 cm x 0.3 cm (diameter and thickness respectively) were categorized after preparation into three groups (n=10) as follows: control group with no surface treatment and two test groups were treated with fiber laser after estimation the appropriate parameters in the pilot study which are 81 ns pulse duration, 30,000 Hz frequency, 50 µm spot size and 10,000 mm/s scanning speed and different average power values (10 W and 20 W) depending on the tested group. Titanium discs surface characterization was performed by scanning electron microscope (SEM), a

Obesity-related deaths continue to rise, and thus losing weight in overweight and obese patients is critical to prevent complications. Anredera cordifolia (Ten,) Steenis, species of succulent plant of the genus Basellaceae, is widely used in herbal medicine to decrease body weight. This study evaluated the potential benefits of Anredera cordifolia ethanol extract to reduce body weight in high-fat diet-induced obesity rat model. This was an experimental with post-test only control group design study involving 36 obese rats. They were divided into two groups: three control groups (K1, K2, K3) and three treatment groups (P1, P2, P3). All the groups were induced with high-fat diet, except K1 control group that received a standard di

Many reports confirm ulcers as an adverse effect of drugs such as nicorandil and aspirin. The exact responsible mechanisms of ulceration have until now not proved. Mucosal ulcers associated with the onset of ulcer are manifested by an increase in proinflammatory cytokine, excessive prostaglandin, and up-regulation of Endothilin-1 level, which directly impacts the release of leptin. These, released locally within mucosal tissues, have played a role in controlling the extent of local inflammatory responses and processes of mucosal repair.
This study was designed to find out the correlation of plasma leptin and prostaglandin levels as a possible mechanism of oral ulcer formation as an adverse effect of nicorandil. The effect of nicorandi

Fisetin is a plant flavonoid found in strawberries and other fruits and vegetables such as apples, persimmons, and onions. It has many pharmacological effects like anti-inflammatory, antioxidant, cardioprotective, neuroprotective, and anti-carcinogenicity which are attributed to its ability to reduce oxidative stress which considers the main reason for different disease conditions. Genotoxicity refers to the genetic material destruction within the cell which can be caused by different chemicals as well as radiation. The present study evaluates the effect of orally-administered fisetin daily for seven constitutive days on genotoxicity induced by cyclophosphamide in rats’ bone marrow and spleen cells. Results showed that fisetin exh

The paper include studies the effect of solvent of dye doped in polymeric laser sample which manufactured in primo press way, which is used as an active (R6G) tunable dye lasers. The remarks show that, when the viscosity of the solvent (from Pure Water to Ethanol), for the same concentration and thickness of the performance polymeric sample is increased, the absorption spectrum is shifts towards the long wave length (red shift), & towards short wave length (blue shift) for fluorescence spectrum, also increased the quantum fluorescence yield. The best result we obtained for the quantum fluorescence yield is (0.882) with thickness (0.25mm) in Ethanol solvent in concentration (2*10-3mole/liter), while when we used the Pure Water as a solvent,

In this work, oral lesions belong to 17 patients, 7 males and 10 females. Their ages range between 15 and 45 years. Follow up was conducted after one day, 7 days, 14 days, one month, and finally 3 months postoperatively. The study lasted for 1.5 year. Surgical diode laser with wavelength of 810 ± 20 nm, with two power levels of 10 and 15 W were used in contact and in non-contact mode via optical fiber. The postoperative outcome revealed; greater haemostatic capability, dry, sealed wound and noticeable lack in pain sensation

     In this study, cadmium oxide (CdO) was deposited on glass bases by thermal chemical spraying technique at three concentrations (0.05, 0.1, 0.15) M and then was irradiated by CO₂ laser with 10.6 μm wave length and 1W power. The results of the atomic force microscope AFM test showed that the surfaces of these CdO thin films were homogenous and that the laser irradiated effect resulted in decreasing the roughness of the surface as well as the heights of the granular peaks, indicating a greater uniformity and homogeneity of the surfaces. The optical properties were studied to determine laser effect. The results of optical tests of these thin films showed that the photoluminescence spectra and absorption s

Effect of the thermal annealing at 400oC for 2 hours and Argon laser radiation for half hour on the optical properties of AgAlS2 thin films, prepared on glass slides by chemical spray pyrolysis at 360oC with (0.18±0.05) μm thickness .The optical characteristics of the prepared thin films have been investigated by UV/Vis spectrophotometer in the wavelength range (300 – 1100)nm .The films have a direct allow electronic transition with optical energy (Eg) values decreased from (2.25) eV for untreated thin films to (2.10) eV for the annealed films and to (2.00) eV for the radiated films. The maximum value of the refractive index (n) for all thin films are given about (2.6). Also the extinction coefficient (K) and the real and imaginary d