In this study three inorganic nano additives, namely; CaCO3, Al2O3 and SiO2 were used to prepare nanocomposites of unsaturated polyester in order to modify their mechanical properties, i.e. tensile strength, elongation, impact and hardness. The results indicated that all the three additives were effective to improve the mechanical properties up to 4% by weight. The effectiveness of them follows the order : CaCO3 > Al2O3 > SiO2 This is due to their particle size in which CaCO3 (13nm), Al2O3 (20-30nm) and SiO2 (15-20nm).

The Ligand 2-(4-nitrophenyl azo)-2,4-dimethylphenol derived from 4-nitroaniline and 2,4-dimethylphenol was synthesized. The prepared ligand was identified by FT-IR and UV-Vis spectroscopic techniques. Treatment of the ligand with the following metal ions ( CuII , ZnII ,CdII and HgII) in aqueous ethanol with a 1:2 M:L ratio. Characterization of these compounds has been done on the basis of FT-IR and UV-Vis, as well as magnetic susceptibility and conductivity measurements. On the basis of physicochemical data tetrahedral geometries were assigned for the complexes.

In this study, composite materials were prepared using unsaturated polyester resin as binder with two types of fillers (sawdust and chopped reeds). The molding method is used to prepare sheets of UPE / sawdust composite and UPE / chopped reeds composite. The mechanical properties were studied including flexural strength and Young's modulus for the samples at normal conditions (N.C). The Commercial wood, UPE and its composite samples were immersed in water for about 30 days to find the weight gain (Mt%) of water for the samples, also to find the effect of water on their flexural strength and Young's modulus. The results showed that the samples of UPE / chopped reeds composite gained highest values of flexural strength (24.

One of the most important , compound which have active hydrogen is the compound possessing (thiol group) Biphenyl-4,4-dithiol is agood example utilized in a wide field for preparation mannich bases , avariety of new acetylenic mannich bases have been Synthesized and all proposed structure were Supported by FTIR , 1H – NMR, 13C-NMR , Elemental analysis and microbial study .

12 membered Schiff base macrocyclic ligands, 6,7,14,15-tetra phenyl-1,2,3,4, 4a,8a, 9,10, 11,12, 12a,16a-dodecahydro dibenzo [b,h] [1,4,7,10] tetraazacyclododecine L1, and 14 membered Schiff base macrocyclic ligands, 6,8,15,17-tetramethyl-1,2,3,4, 4a,7,9a, 10,11,12,13,13a,16,18a-tetra decahydro dibenzo[b,i] [1, 4,8,11] cyclotetradecine tetraaza L2, 7,16-bis(2,4- dichloro benz ylidene)-6,8,15,17-tetra methyl-1,2,3,4, 4a,7,9a, 10, 11,12, 13, 13a,16,18a-tetra deca hydro dibenzo [b,i] [1,4,8,11] tetra azacyclo tetra decine L3 and 6,8,15, 17-tetramethyl-1,2,3, 4,4a,9a,10, 11,12,13,13a,18a-dodecahydro dibenzo [b,i] [1,4,8, 11] tetraazacyclo tetradecine (7,16-diylidene) bis(methanylyli dene) bis (N,N-dimethylaniline) L4 were synthesized by condens

In this research , phthallic anhydride ring is opened with 4-methyl aniline and acetone as a solvent to results the compound [I] that reacted with dimethyl sulphate and anhydrous sodium carbonate formation to phathalate ester [II], while the acid hydrazide compound [III], was obtained from mixed the compound [II]with hydrazine hydrate, Synthesis four type of shiff bases[IV]a-d was synthesized from the reaction of acid hydrazide [III] with aromatic aldehyde or ketone , when reacted Shiff bases with phthalic anhydride or naphthalicanhydride,I get eight derivatives of oxazepine [V]a-d , [VI]a-d. The bacterial activity of the new compounds studied by four species of bacteria: Esherichia Coli, Enterobactecloacae (Gram negative) and staphylococcu

This thesis aims to study the effect of addition polymer materials on mechanical properties of self-compacting concrete, and also to assess the influence of petroleum products (kerosene and gas oil) on mechanical properties of polymer modified self-compacting concrete (PMSCC) after different exposure periods of (30 ,60 ,90 ,and 180 days).

Two type of curing are used; 28 days in water for SCC and 2 days in water followed 26 days in air for PMSCC.

The test results show that the PMSCC (15% P/C ratio) which is exposed to oil products recorded a lower deterioration in compressive strength's values than reference concrete. The percentages of reduction in compressive strength values of PMSCC (15% P/C ratio) was

In this work, yttrium oxide particles (powder) reinforced AL-Si matrix composites (Y2O3/Al-Si) and Chromium oxide particles reinforced AL-Si matrix composites (Cr2O3/AL-Si) were prepared by direct squeeze casting. The volume percentages of yttrium oxide used are (4, 8.1, 12.1, 16.1 vol %) and the volume percentages of the chromium oxide particles used are (3.1, 6.3, 9.4, 12.5 vol. %). The parameters affecting the preparation of Y2O3/Al-Si and Cr2O3/AL-Si composites by direct squeeze casting process were studied. The molten Al-Si alloy with yttrium oxide particles or with chromium oxide particles was stirred again using an electrical stirrer at speed 500 rpm  and the molten alloy was  poured  into the squeeze die cavity. Th