The research dealt with the effect of Kut Barrage on the geomorphological processes and the natural environment system in the course of the Tigris between the cities of Al-Ahrar and Kut in central Iraq. It was clear from the research the contribution of Kut Barrage in changing the surface runoff system between the front and back of the barrage, as well as changing the type of processes and the prevailing geomorphic forms, as the sedimentation activates the front of the barrage and erosion at its back, which affected the change in the morphology of the river, sediment retention at the front of the barrage, the burial of the bottom and reducing the validity of the stream. This also affects the efficiency of the barrage’s work and coastal er

This study is concerned with the effect of adding two kinds of ceramic materials on the mechanical properties of (Al-7%Si- 0.3%Mg) alloy, which are zirconia with particle size (20μm > P.S ≥ 0.1μm) and alumina with particle size (20μm > P.S ≥ 0.1μm) and adding them to the alloy with weight ratios (0.2, 0.4, 0.6, 0.8 and 1%). Stirring casting method has been used to make composite material by using vortex technique which is used to pull the particles to inside the melted metals and distributed them homogenously.

After that solution treatment was done to the samples at (520ºC) and artificial ageing at (170ºC) in different times, it has been noticed that the values of hardness is increased with the aging time of the o

Pure cadmium oxide films (CdO) and doped with zinc were prepared at different atomic ratios using a pulsed laser deposition technique using an ND-YAG laser from the targets of the pressed powder capsules. X-ray diffraction measurements showed a cubic-shaped of CdO structure. Another phase appeared, especially in high percentages of zinc, corresponding to the hexagonal structure of zinc. The degree of crystallinity, as well as the crystal size, increased with the increase of the zinc ratio for the used targets. The atomic force microscopy measurements showed that increasing the dopant percentage leads to an increase in the size of the nanoparticles, the particle size distribution was irregular and wide, in addition, to increase the surfac

Three-dimensional nonlinear thermal numerical simulations are conducted for the friction stir welding (FSW) of AA 7020-T53. Three welding cases with tool (rotational and travel) speeds of 900rpm-40mm/min, 1400rpm-16mm/min and 1400rpm-40mm/in are analyzed. The objective is to study the variation of transient temperature in a friction stir welded plate of 5mm workpiece thickness. Based on the experimental records of transient temperature at several specific locations during the friction stir welding process for the AA 7020-T53, thermal numerical simulation is developed. The numerical results show that the temperature field in the FSW process is symmetrically distributed with respect to the welding line, increasing travel speed decreasing tran

Background: Lack of durability of the bond of the dental adhesive systems to tooth structure is one of the most important problems in tooth colored restorative work. This in vitro study was performed to evaluate the effect of 2% chlorhexidine gluconate(CHX) on dentin bond strength by using total etch adhesive system at twenty-four hours and three months of water storage. Material and methods:A flat dentin surface was prepared for forty sound human maxillary premolar teeth which were acid etched with 36% phosphoric acid gel after being divided randomly into four groups of ten teeth each according to storage time and CHX application, theCHX was applied for 60 seconds before adhesive application for groups I and III which were tested after twe

In this work, varying compositions of SiO₂ micro filler were added
with the Polyvinyl Chloride (PVC) and samples have been prepared
using film casting technique. The results have been analyzed and
compared for PVC samples with (1 wt%, 3 wt%, 5 wt% and 10 wt%)
SiO2 micro filler. Mechanical characteristics such as tensile strength,
elongation at break and Young`s modulus were measured for all the
samples, where the tensile strength was increased from 8.39 Mpa for
purified PVC to 16 Mpa for 3% SiO₂/PVC composite. Also, thermal
conductivity measurement values illustrated that composite materials
have a good thermal insulation at 10 wt. %, thermal conductivity was
decreased from 0.1684 W/m.

Background: The aim of this in vitro study was to evaluate and compare the effect of preheating microleakage among three different filler size composites which include Filtek^tm Z250 micro hybrid, Z250^xt Nano hybrid and nanocomposite Z350^xt.  in Class II cavity preparation .

Materials and methods: sixty maxillary first premolars were prepared with class II cavities. Samples were divided into three groups according to material used    group A (FiltekZ250 micro hybrid). Group B(Z250^xt Nano hybrid). Group C (nanocomposite Z350^xt)and each group divided into two subgroups of ten teeth according to temperature of  composite:

Background: Poly (methylmethacrylate) is the most widely used material in denture fabrication. The characteristics of acrylic resin which support microorganism development can threaten the oral health of denture users. This study was assigned to prepareand incorporate Ag-Zn zeolite powder into heat cured denture base material as antimicrobial material and to investigate its effect on some properties of heat cured acrylic denture base materials. Materials and methods: Sliver –zinc zeolite was prepared by ion exchange method and characterized then incorporated into poly (methylmethacrylate) powder in0.5% by weight. Specimens were constructed and divided into 6 groups according to the using tests; each group was subdivided into 2 groups

This study was carried out at Poultry Research Station, State Board of Agricultural Research, Ministry of Agriculture for the period from 27 September 2014 to 9 November 2014 to evaluate the Supplementation of different levels of Conjugated Linoleic Acid (CLA) on productive performance of broiler. Four hundred eighty chicks (Ross-308),one day old were randomly distributed to four dietary treatments for 42 days of age with 3 replicates/vtreatment (40 bird/replicate). Experimental treatments were as follow; T1 (Control diet) without supplement, while the treatment T2,T3 and T4  were Supplemented with 1, 1.5, 2 g CLA /kg diet  respectively. The results showed significant (P ≤ 0.05) increased in mean of body weight, weight gain, ave