Background: The objectives of this study are to evaluate the effect of addition of Multi-Wall Carbon Nano Tubes (MWCNTs) of different concentrations (0.05 mg.mL-1,0.25 mg.mL-1,0.5 mg.mL-1and1 mg.mL-1) on dimethyl sulphoxide DMSO and distilled water (DW) on tooth enamel. It intends to evaluate enamel microhardness in (Kg. m-2) pre and post the application of Multi-Wall Carbon Nano Tubes (MWCNTs). Materials and Methods: Thirty specimens prepared for the present study to measure the hardness of the enamel. Results: The results showed that a significant increase in the enamel microhardness for groups 0.05 mg/mL (group B), 0.25 mg/mL (group C), 0.5 mg/mL (group D) and 1 mg/mL (group E) compared with control group (group A) in dimethyl sulphoxi

The experiment was conducted in the old botanical garden belong to Biology Department/ College of Education for Pure Science - Ibn Al-Haitham/Baghdad University for growing season 2015-2016 to study the effect of irrigation with four concentrations of sodium chloride (0, 50, 100, 150) mM.L-1 and spraying with selenium in three concentrations (0, 10, 20) mgL-1 on growth of broad bean plant using clay pots. The experiment was design according to completely randomized design (CRD) with three replications. Results indicated that broad bean plant irrigated with saline water and increasing concentrations of sodium chloride in growth medium caused a significant decreased in the plant growth parameters (plant height, no. of compound leaves. Plant-1

In this study, Cobalt Oxide nanostructure was successfully prepared using the chemical spray pyrolysis technique. The cobalt oxide phase was analysed by X-ray Diffraction (XRD) and proved the preparation of two cobalt oxide phases which are Co3O4 and CoO phases. The surface morphology was characterized by Scanning Electron Microscope (SEM) images showing the topography of the sample with grain size smaller than 100 nm. The optical behavior of the prepared material was studied by UV-Vis spectrophotometer. The band gap varied as 1.9 eV and 2.6 eV for Co3O4 prepared from cobalt sulphate precursor, 2.03 eV and 4.04 eV for Co3O4 prepared from cobalt nitrate precursor, 2.04 eV and 4.01 eV for CoO prepared from cobalt chloride precursor where th

The aim of this work is studying the binary system ??'??? Ni?)with two ratios (y=36,80) by using casting method for preparing the samples.Magnetic and Mechanical properties have been studidt different httrea^nttem^rature.All the alloys were found a ferromagnetic behavior and sensitive to the heat treatment. Best properties were found at the heat treatment 1100 C°.A significant different results were found above 1100C° for lower magnetic and mechanical values. This is possibly due to the change on the degree of magnetic moment orders, in which most of the moments are started to remove from coupled ferromagnetically.?

This study was conducted to evaluate the efficacy of Saccharomyces cerevesiae as a growth promoting agent in tomato. Soaking the seeds in yeast suspension at 5 g/L for 12h increased germination percentage, root length, root fresh and dry weight, plant height, foliage fresh and dry weight, attained 88.5% ; 8.1 cm ; 84.3 mg ; 7.03 mg ; 10.75 cm ; 839 mg and 37.75 mg compared with 80% ; 5.33 cm ; 39 mg ; 4.8 mg ; 7.35 cm ; 608 mg and 25.5 mg in seedlings grown from non treated seeds respectively. Similar results were obtained with seedling from seeds soaked in S. cerevesiae filtrate for 12 hrs. with values of 77.5% ; 6.875 cm ; 91.5 mg ; 7.5 mg ; 9.5 cm ; 777 mg and 40.35 mg compared to 66% ; 5.8 cm ; 57.7 mg ; 5.03 mg ; 5.9 cm ; 493 mg