Improving the accuracy of load-deformation behavior, failure mode, and ultimate load capacity for reinforced concrete members subjected to in-plane loadings such as corbels, wall to foundation connections and panels need shear strength behavior to be included. Shear design in reinforced concrete structures depends on crack width, crack slippage and roughness of the surface of cracks.

This paper illustrates results of an experimental investigation conducted to investigate the direct shear strength of fiber normal strength concrete (NSC) and reactive powder concrete (RPC). The tests were performed along a pre-selected shear plane in concrete members named push-off specimens. The effectiveness of concrete compressiv

The aim of this work is to study the effect of mud compositions on it’s rheological behavior under high temperature conditions. Seventeen samples of five types of water base mud in which (fresh water bentonite mud. Lignosulphonate mud, gypsum mud, polymer mud, and salt saturated mud) were tested with different temperatures using the fann viscometer model 50-c. All the tested samples, except the fresh water bentonite mud, have the same trend reduction in both plastic viscosity and yield point with increasing temperature. Six rheological models has been adapted: Bingham plastic, power law, Casson model represent the laboratory data accurately  

In this paper, the behavior of spliced steel girders under static loading is investigated. A group of seven steel I-girders were tested experimentally. Two concentrated loads were applied to each specimen at third points and the load was increased incrementally up to the yield of the specimen. Two types of splices were considered; the bearing type and the friction-grip type splices. For comparison, an analytical study was made for the tested girders in which the finite element analysis program (Abaqus) was used for analysis. It was found that the maximum test load for spliced girders with bearing type splices was in the range of (34%) to (67%) of the maximum test load for the reference girder. For girders spliced by using friction-grip t

Preparation and Characterization of Maleate, Tartarate,and Phthalate Modified Pectin

The study aimed to evaluate the antimicrobial activity using different concentrations of aqueous and alcoholic extracts of dried lemongrass leaves. Chemical phytochemical tests were performed for aqueous and alcoholic extracts of lemongrass. Antimicrobials activity was tested using agar disc diffusion method against Escherichia coli and Staphylococcus aureus. The results of the study showed that the aqueous extract of dried lemon leaves was highly effective (P≤0.05) against S. aureus, as the inhibition diameter was 22 mm for 50 dilution, while the inhibition diameter decreased to 15 mm for concentration 100. As for the alcoholic extract only, the diameter of inhibition decreased significantly (P≤0.0

Local food samples investigated for the presence of pathogenic bacteria. Hash meat sample was used to isolate Escherichia coli and chicken meat (poultry) was used to isolate Salmonella typhi. Biochemical tests and API20E system used in order to identify these isolates. Two natural vinegar samples (dates & apple cider) were used in order to study its antibacterial activity against the two tested bacteria. Disc diffusion method was used, the results showed that two vinegar samples have antibacterial activity against the two tested bacteria. Date vinegar showed inhibition zone 19mm against E. coli & 9mm against S. typhi, while Apple cider vinegar showed diameter of inhibi

The importance of the present work falls on the pitting corrosion behavior investigation of 304 SS and 316 SS alloys in 3.5 wt%  of aqueous solution bearing with chloride and bromide anion  at different solutions temperature range starting from (20-50)^oC due to the pitting corrosion tremendous effect on the economic, safety and materials loss due to leakage. The impact of solution temperatures on the pitting corrosion resistance at 3.5wt% (NaCl and  NaBr) solutions for the 304 SS and 316 SS has been investigated utilizing the cyclic polarization techniques at the potential range -400 to1000 mV vs. SCE at 40 mV/sec scan rate followed by the surface characterization employing Scanning Electron&nbs

Emotional exhaustion considered one of the critical factors in the formation and composition of organizational behavior of individuals within organizations, as well as social behavior and psychological, and emotional exhaustion is one of the three components of burnout, as well as depersonalization (cynicism) and low achievement, the emergence of research relevant to this concept began at the beginning of the seventies of the twentieth century, then started to become clear features in the eighties it. This research aims to build intellectual framework for draining emotional exhaustion through highlight on most important philosophical contents, as well as review and analysis of some models associated with this concept, and then a