The durability of asphalt concrete is highly dependent on the geometry and mineralogy of coarse aggregates, yet their combined influence on mechanical and moisture resistance properties is still not fully understood. This study evaluates the effects of coarse aggregate geometry, specifically flat and elongated particle ratios and angularity, as well as mineral composition (quartz versus calcite), on asphalt mixture durability. The durability of mixtures was evaluated through Marshall properties as well as moisture susceptibility indicators, including the tensile strength ratio (TSR) and index of retained strength (IRS). Statistical analyses (ANOVA and t-tests) were also conducted to confirm the significance of the observed effects.

Tin dioxide doped silver oxide thin films with different x content (0, 0.03, 0.05, 0.07) have been prepared by pulse laser deposition technique (PLD) at room temperatures (RT). The effect of doping concentration on the structural and electrical properties of the films were studied. Atomic Force Measurement (AFM) measurements found that the average value of grain size for all films at RT decrease with increasing of AgO content. While an average roughness values increase with increasing x content. The electrical properties of these films were studied with different x content. The D.C conductivity for all films increases with increasing x content. Also, it found that activation energies decrease with increasing of AgO content for all films.

(Cu1-x,Agx)2ZnSnSe4 alloys have been fabricated with different Ag content(x=0, 0.1, and 0.2) successfully from their elements. Thin films of these alloys have been deposited on coring glass substrate at room temperature by thermal evaporation technique under vacuum of 10-5Torr with thickness of 800nm and deposition rate of 0.53 nm/sec. Later, films have been annealed in vacuum at (373, and 473)K, for one hour. The crystal structure of fabricated alloys and as deposited thin films had been examined by XRD analysis, which confirms the formation of tetragonal phase in [112] direction, and no secondary phases are founded. The shifting of main polycrystalline peak (112) to lower Bragg’s angle as compared to Cu2ZnSnSe4 angle refers to incorpora

Background: Bone mineral density (BMD) has been assessed using Dual-Energy X-ray absorptiometry (DEXA). This procedure is considered to be of vital importance in assessing the general condition of individuals concerning their skeletal mineralization. BMD is measured according to the results of the DEXA examination of the vertebral column and pelvis. Although diabetes mellitus (D.M.)is known to affect BMD, the information regarding this relationship is not currently particularly clear. Objective: This study concentrates on the point that the assessment of BMD for the vertebral column is insuffi-cient to give a realistic and correct picture of the mineralization of the remaining part of the skeleton. Besides, this study elicited a gen

Two field experiments were conducted during the spring seasons of 2000,2001.The aim was to study the effect of hardening to drought tolerance on moisture percentage in root and stem of sunflower plant during growth stages . Asplit-split plots design was used with three replications.The main plots included irrigation treatments:irrigation to100%(full irrigation),75and50%of available soil water.The sub plots were the cultivars Euroflor and Flame.The sub-sub plots represented four seed soaking treatments :Control(unsoaked),soaking in water ,Paclobutrazol solution(250ppm),and Pix solution(500ppm). The soaking continued for 24 hours then seeds were dried at room temperature until they regained their original weight. Amount of water

Alloys of InxSe1-x were prepared by quenching technique with
different In content (x=10, 20, 30, and 40). Thin films of these alloys
were prepared using thermal evaporation technique under vacuum of
10-5 mbar on glass, at room temperature R.T with different
thicknesses (t=300, 500 and 700 nm). The X–ray diffraction
measurement for bulk InxSe1-x showed that all alloys have
polycrystalline structures and the peaks for x=10 identical with Se,
while for x=20, 30 and 40 were identical with the Se and InSe
standard peaks. The diffraction patterns of InxSe1-x thin film show
that with low In content (x=10, and 20) samples have semi
crystalline structure, The increase of indium content to x=30
decreases degree o

The research current (Comment formal for Hruvijat in contemporary Iraqi porcelain). In an attempt to study the Arab character that inspired the Iraqi artist of all intellectual its terms of reference and stylistic by taking advantage of the cultural heritage and the rebuilding of the character to create a system ride of relationships that focus on structural body ceramic body ideas and multiple implications are invested in the structural fabric of the products of contemporary ceramic .vdila for ways to achieve and processing techniques and transmission of functional specificity (blogging) and cosmetic particularly to semantics derive from the content and expresses itself templates ceramic raw materials and by building works of art in pla

Loratadine is a long acting non-sedating anti-histaminic agent that was developed for the treatment of seasonal allergic rhinitis, whose anti-histaminic action is more effective than the other anti-histaminic drugs available commercially. This project was carried out to prepare an acceptable suspension through studying the release of drug in presence of different types and concentrations of suspending agents such as polysorbate 40, xanthan gum, sodium carboxymethylcellulose (NaCMC), aluminum magnesium silicate (veegum) and sodium alginate. The effects of these suspending agents were studied at pH 1.2 (0.1N HCl) and 37 Ù’C. The results showed that the release rate of loratadine in the presence of these suspending agents was dependent o

The purpose of this study is to investigate the biostimulation effect of 532 nm CW laser on the metabolism of Saccharomyces cerevisiae yeast. Cells were irradiated by 532 nm Nd:YAG laser using 0.153 W/cm2 power density at 30, 45, 60,180 and 300 seconds exposure times in their respective orders. Intrafluorescence parameters were measured by detection the autofluorescence intensity, proliferation rate and Imaging the fluorescent mitochondria using confocal laser scanning microscope. The results showed that the 30 and 45 second exposure times seem to have stimulated changes in the cells that led to increase proliferation, viability and mitochondrial activity. Autofluorescence of cells increased after 45 and 60 seconds exposure time. After 3