Batch reactive distillation was studied in packed bed column. Esterification of methanol with acetic acid to produce methyl acetate and water with homogenous sulfuric acid as a catalyst was considered. This system was chosen because the reaction is reversible and the boiling point of reactant and products are different.
The reaction was carried out with and without distillation column and shows that the reactive distillation is more efficient from the conventional process (reactor and then separation). The conversion of acetic acid and concentration of methyl acetate increase by (30.43% and 75.14%) respectively at the best condition (reflux ratio 2, feed mole ratio 2 and batch time 90 minute).
The influence of various parameters, s

Background: The marginal fit is the most characteristic that closely related to the longevity or success of a restoration, which is absolutely affected by the fabrication technique. The objective of present in vitro study was to evaluate the effect of four different CAD/CAM systems on the marginal fit of lithiµm disilicate all ceramic crowns. Materials and Methods: Adentoform tooth of a right mandibular first molar was prepared to receive all ceramic crown restoration with deep chamfer finishing line (1mm) and axial reduction convergence angle of 6 degree, dentoform model duplicated to have Nickel-Chromiµm master die. Thirty two stone dies produce from master die and distributed randomly in to four groups (8 dies for each group) accor

Thin films of pure tin mono-sulfide SnS and tin mono-sulfide for (1,2,3,4)% fluorine SnS:F with Thicknesses of (0.85 ±0.05) ?m and (0.45±0.05) ?m respectively were prepared by chemical spray pyrolysis technique. the effect of doping of F on structural and optical properties has been studied. X-Ray diffraction analysis showed that the prepared films were polycrystalline with orthorhombic structure. It was found that doping increased the intensity of diffraction peaks. Optical properties of all samples were studied by recording the absorption and transmission spectrum in range of wave lengths (300-900) nm. The optical energy gap for direct forbidden transi

Solid dispersion is an attractive tool of pharmaceutical technology used to improve the physical properties of drugs. Among these properties is to enhance the solubility of the drugs.
Rebamipide is a poorly soluble drug of class IV of biopharmaceutical classification system (BCS).
Rebamipide is used as potent antiulcer, mucoprotective drug, by stimulating the generation of prostoglandine enhanced mucosal protection.
Rebamipide was formulated as a solid dispersion using different polymers such as pluronic F-127, PEG6000, PVP K30, and TPGS by using different preparation methods solvent evaporation, fusion, and kneading methods.
It was seen that rebamipide was successfully dispersed in a homogenous solid dispersion matrix by sol

In this work, 332 Al alloy was prepared and reinforced with (0.5% and 1%) nano-Al₂O₃ particles. The prepared unreinforced and reinforced 332 Al alloy with nano-Al₂O₃ were solution heat treated (T6) at 510 ̊C and aged at 225 ̊C with different times (1, 3, and 5 h). Hardness test was performed on all the prepared alloys. All prepared alloys were dry slided under different applied loads (5, 10, 15, and 20 N) against steel counterface surface using pin on disk apparatus. The results showed that refinement effect was observed after addition of nano-Al₂O₃ particles and a change in silicon morphology after performing the solution heat treatment. The results also showed that har

In this research the a-As flims have been prepared by thermal evaporation with thickness 250 nm and rata of deposition r_d(1.04nm/sec) as function to annealing temperature (373 and 473K), from XRD analysis we can see that the degree of crystalline increase with T_a, and I-V characteristic for dark and illumination shows that forward bias current varieties approximately exponentially with voltage bias. Also we found that the quality factor and saturation current dependence on annealing temperatures.

In this research the a-As flims have been prepared by thermal evaporation with thickness 250 nm and rata of deposition (1.04nm/sec) as function to annealing temperature (373 and 373K), from XRD analysis we can see that the degree of crystalline increase with , and I-V characteristic for dark and illumination shows that forward bias current varieties approximately exponentially with voltage bias. Also we found that the quality factor and saturation current dependence on annealing temperatures.