In this paper, magnesium oxide nanoparticles (MgO NPS) have been prepared and characterized and its concentration effect has been studied on polymers surface (MgO NPS). The results showed that the degradation of poly methyl methacrylate increased when using such metal oxide. The results also showed that the metal oxide increased the degradation of poly methyl methacrylate. X-ray diffraction, scanning electron microscopy, atomic force microscopy were used to study the morphological characteristics and size of nano MgO particles analysis.  Films were prepared by mixing the different masses of MgO NPS (0.025, 0.05, 0.1, 0.2 and 0.4) % with a polymer solution ratio (W/V) 7 %. Photo-

Sheets of Epoxy (EP) resin with addition of TiO2 of grain size (1.5μm, and 50nm) and weight percentage (1%, 3%, and 5%) were prepared. Discs of 20mm diameter and 3mm thickness were cut for dielectric measurements. Dielectric properties (dielectric constant, dispassion factor and electrical conductivity) over the frequency range 102 -106 Hz were measured.
Comparison was made between the effect of micro and nano particles of TiO2 on the dielectric properties of EP composites with different weight percentage. Epoxy composites with micro sized particles of TiO2 were observed to have the better values of dielectric properties.

Effluent from incompetent wastewater treatment plants (WWTPs) contains a great variety of pollutants so support water treatments are essential. The present work studies the removal of phosphate species from aqueous solutions by adsorption on to spherical Calcined Sand -Clay mixture (CSCM) used a natural, local and low-cost adsorbent. Batch experiments were performed to estimate removal efficiency of phosphate. The adsorption experiments were carried out as function of pH, dose of adsorbent, initial concentration, temperature and time of adsorption. The efficient removal was accomplished for pH between 10 and 12. The experimental results also showed that the removal of phosphate by (CSCM) was rapid (the % removal 98.9%, 92%, 90%, 89% in 6

Background: 37% phosphoric acid (PA) is the traditional enamel etching technique prior to bracket ‎adhesion, yet it has been implicated in numerous enamel injuries. The purpose of the current study was to create a calcium phosphate (CaP) etching paste in a ‎‎simplified capsule ‎formula that can underpin clinically ‎adequate bracket bond strength ‎without jeopardizing the ‎integrity of enamel upon ‎the debracketing procedure. Materials and Methods: micro-sized hydroxyapatite (HA) powder was mixed with 40% PA solution to prepare ‎experimental acidic CaP paste. Sixty human premolars were ‎assigned into two groups of 30 each. ‎Enamel conditioning was accomplished using 37% PA-gel‎ for control group and CaP paste for e

Objectives: To review the failure rates of molar tubes and the effect of molar tube base design, adhesive type, and bonding technique on the failure rates of molar tubes. Data: The revolution of molar bonding greatly impacted fixed orthodontic appliance treatment by reducing chair-side time and improving patient comfort. Even with the many advantages of molar bonding, clinicians sometimes hesitate to use molar tubes due to their failure rates. Sources: Internet sources, such as Pubmed and Google Scholar. Study selection: studies testing the bond failure rate of molar tubes. Conclusions: The failure rate of the molar tubes can be reduced and the bond strength of the molar tubes can be improved by changing the design of the molar tube base

Background: This in vitro study compares a self-etch primer (SEP) to an etch-and-rinse (EaR) for bonding sapphire brackets by evaluation of the enamel etch-pattern, shear bond strength, amount of remnant adhesive and enamel surface damage following thermal and fatigue cyclic loading. Material and Methods: Ceramic (sapphire) brackets were bonded to 80 extracted human premolars using two enamel etching protocols: conventional EaR using 37% phosphoric acid (PA) gel (control), and a SEP (Transbond Plus). Each group was subdivided into two subgroups (n=20 teeth) according to the time of bracket debonding: after 24 h water storage or following 5000 thermo-cycles plus 5000 cycles fatigue loading, to determine the shear bond strength (SBS), adhesiv

The waste sorting and recycling plant in the district of al- Mahmudiya (Yusufiya) is the only laboratory in Baghdad governorate. It is the only one in Iraq that collects and recycles waste. After sorting, we have packages of raw materials (aluminum cans, glass bottles, plastic bottles, Nylon bags) as well as natural fertilizers (food residues and others) and a sanitary landfill with specifications that meet international standards; However, the absence of a structure for the management of the plant (manager, assistant manager, accountant, etc.) in addition to the non-supply of waste on a daily and continuous basis and the lack of cooperation of the Municipality of Baghdad with the management of the plant led to delay in the work

In this work, Soda Lime Glass (S.L.G.) powder was used ,as
fluxe in traditional porcelain instead of feldspar. Two ceramics
porcelain were compared; commercial or traditional porcelain that
content of 50wt % kaolin, 25wt % quartz, and 25wt % feldspar.
Feldspar mass was substituted by scraps soda lime glass yielding a
new porcelain composition, to determine the softening points and
then the effect of glass addition on porcelain firing process.
Eight samples, for each patch, were prepared and 8wt % water
was added. The resulting composite blends were then die pressed at
2N, to produce disk specimens with diameter of 1.5 cm, and then
they were sintered at (1000, 1100, 1200, 1250,1300,1350,1400 and
1450) ˚C,

Background: Metabolic syndrome MS a cluster of disorders comprising obesity (central and abdominal), dyslipidaemias, glucose intolerance, insulin resistance (or hyperinsulinaemia) and hypertension – is highly predictive of type 2 diabetes mellitus and cardiovascular disease. It should be emphasized that the metabolic syndrome is a syndrome and not a disease. The aim of this study is to evaluate the levels of serum phosphate in different levels in subjects with metabolic syndrome MS and Correlation between serum phosphate levels with metabolic syndrome components. The study was carried out at the National diabetes Center (NDC) /AL-Mustansiryia University ,the period from (Desmber.2011 – May 2012) One hundred forty (140) Iraqi indivi