Abstract Twelve isolates of bacteria were obtained from samples of different soils and water amended with 100µg/ml of five heavy metals chlorides (i.e: Aluminum Al+2, Iron Fe+2, Lead Pb+2, Mercury Hg+2 and Zinc Zn+2). Four isolates were identified as Bacillus subtilis and B. subtilis (B2) isolate was selected for this study according to their resistance to all five heavy metals chlorides. The ability of B. subtilis (B2) isolate for growing in different concentration of heavy metals chlorides ranging from 200-1200 µg/ml was tested. The highest conc. that B. subtilis (B2) isolate tolerate was 1000 µg/ml for Al+2, Fe+2, Pb+2, and Zn+2and 300 µg/ml for Hg+2 for 24hour. The effect of heavy metals chlorides on bacterial growth for 72 hrs was studied. B. subtilis (B2) isolate had not affected by presence of pbCl2 FeCl2and AlCl2 in growth media. However, it was slightly affected by ZnCl2 during incubation period while mercury causes no bacterial growth. The effect of temperature on bacterial growth in media with heavy metals was studied. B. subtilis (B2) isolate showed growth in temp. range (30-50) °C with the present of the four heavy metals chlorides Al+2, Fe+2, Pb+2and Zn+2 while there are no growth in the presence of Hg+2 at all temperatures. The effect of different pH values on growth of B. subtilis (B2) isolate in media with heavy metals was studied. Results showed the ability of B2 isolate for growing in different pH values 4,7,9 with presence of the four heavy metals chlorides Al+2, Fe+2, Pb+2and Zn+2 in all pH values at conc. 1000 µg/ml and unability for growing in media with 300 µg/ml Hg+2. The ability of B. subtilis (B2) isolate for removal of heavy metals chlorides was studied and showed that the highest Zn+2 removal ratios 75% then Fe+2removal ratio 71% while Pb+2 has the lowest removal ratio 37%.
(15)
(5)
The aqueous extract of Citrullius colocynthis dried seeds (160 ?g/ml) was in vitro evaluated for its effect on phagocytic index (PI) and lymphocyte transformation index (LTI) of blood cells obtained from 30 apparently healthy blood donors (15 males and 15 females). The PI was further in vivo evaluated in cells of peritone, spleen and liver of mice treated with the extract at a dose of 0.64 mg/kg. The results revealed that in in vitro study, phagocytic cells treated with the extract showed a significant increased percentage as compared with untreated cells (60.0 vs. 44.1%). Phagocytes obtained from peritone (44.1 vs. 30.0%) and spleen (45.6 vs. 39.6 %) of treated and untreated mice behaved in a similar manner, while liver phagocytes showed n
... Show More
(1)
Chitosan (CH) / Poly (1-vinylpyrrolidone-co-vinyl acetate) (PVP-co-VAc) blend (1:1) and nanocomposites reinforced with CaCO3 nanoparticles were prepared by solution casting method. FTIR analysis, tensile strength, Elongation, Young modulus, Thermal conductivity, water absorption and Antibacterial properties were studied for blend and nanocomposites. The tensile results show that the tensile strength and Young’s modulus of the nanocomposites were enhanced compared with polymer blend [CH/(PVP-co-VAc)] film. The mechanical properties of the polymer blend were improved by the addition of CaCO3 with significant increases in Young’s modulus (from 1787 MPa to ~7238 MPa) and tensile strength (from 47.87 MPa to 79.75 MPa). Strong interfacial
... Show More
Despite widespread agreement on the beneficial nature of hydrated lime (HL) addition to asphalt concrete mixes, understanding of the effect of HL particle size is still limited. Previous investigations have focused mainly on two different size comparisons, and so certain guidance for a practical application cannot yet be produced. This study investigates three distinct sizes of HL, in the range of regular, nano, and sub-nano scales, for their effects on the properties of modified asphalt concretes. Five different percentages of HL as a partial replacement of ordinary limestone filler in asphalt concrete mixes were studied for wearing course application purposes. Experimental tests were conducted to evaluate the mechanical properties
... Show More
(17)
(16)
(2)
(3)
(2)
(2)
The study included adding antimony oxide to mixtures of coating metal surfaces (Enameling), after it was selected ceramic materials used in the coating metal pieces of the type of steel and cast iron in two layers. The first is called a ground coat and the second is a cover coat.
Ceramic materials layer for ground coat have been melted down in
platinum crucible at a temperature of 1200oC to prepare the glass
mixture (Frit). It was coated on metals at a temperature of 780oC for
two minutes, while the second layer was prepared glass mixture
(Frit) at a temperature of 1200oC, but was coated at a temperature of
760oC for two minutes.
Underwent tests crystalline state of powders (Frits) and enameled samples using X-ray di