In the current endeavor, a new Schiff base of 14,15,34,35-tetrahydro-11H,31H-4,8-diaza-1,3(3,4)-ditriazola-2,6(1,4)-dibenzenacyclooctaphane-4,7-dien-15,35-dithione was synthesized. The new symmetrical Schiff base (Q) was employed as a ligand to produce new complexes comprising Co(II), Ni(II), Cu(II), Pd(II), and Pt(II) metal-ions at a ratio of 2:1 (Metal:ligand). There have been new ligands and their complexes validated by (FTIR), (UV-visible), 1H-NMR, 13C-NMR, CHNS, and FAA spectroscopy, Thermogravimetric analysis (TG), Molar conductivity, and Magnetic susceptibility. The photostabilization technique to enhance the polymer was also used. The ligand Q and its complexes were mixed in 0.5% w/w of polyvinyl chloride in tetrahydrofuran (THF). The photo stabilization of polymer films was studied at 25 °C under irradiation of light λ 380–250 nm with intensity of 7.75 × 10−9 ein dm−3 s−1. The photostabilization activity of these compounds was determined by monitoring the hydroxyl, carbonyl, and polyene indexes, weight loss method with irradiation time. The ICO, IPO and IOH index values increased with irradiation time, this increase depends on the type of additives. The surface morphology for these films was studied during irradiation time. This project is highly intriguing for the ecosystem in regards to the decrease in the consumption of plastic.
A series of 4-(methylsulfonyl)aniline derivatives were synthesized in order to obtain new compounds as a potential anti-inflammatory agents with expected selectivity against COX-2 enzyme. In vivo acute anti-inflammatory activity of the final compounds 11–14 was evaluated in rat using an egg-white induced edema model of inflammation in a dose equivalent to 3 mg/Kg of diclofenac sodium. All tested compounds produced significant reduction of paw edema with respect to the effect of propylene glycol 50% v/v (control group). Moreover, the activity of compounds 11 and 14 was significantly higher than that of diclofenac sodium (at 3 mg/Kg) in the 120–300 minute time interval, while compound 12 expressed a comparable effect to that of di
... Show More
(10)
(10)
In this work, thiadiazole derivatives were prepared by taking advantage of active sites in (2-amino-5-mercapto-1, 3, 4-thiadiazole) as a starting material base. The main heterocyclic compounds (1, 3, 4-thiadiazole, oxazole) etc, 2-amino-5-mercapto-1,3,4-thiadiazole compound (1) was prepared by cyclic closure of thiosemicarbazide compound with anhydrous sodium carbonate and carbon disulfide. Oxidation of (1) via hydrogen peroxide, to have (2) which was treated with chloro acetyl chloride to get (3). Preparation of thiazole ring (4) was from reacting of (3) with thiourea. Synthesis of diazonium salts (5) from compound (4) using sodium nitrite and HCl. Compound (5) reacted with different ester compounds to prepare a new azo compounds (6–8).C
... Show More
(4)
(2)
The magnetic properties of a pure Nickel metal and Nickel-Zinc-Manganese ferrites having the chemical formula Ni0.1(Zn0.4Mn0.6)0.9Fe2O4 were studied. The phase formation and crystal structure was studied by using x-ray diffraction which confirmed the formation of pure single spinel cubic phase with space group (Fd3m) in the ferrite. The samples microstructure was studied with scanning electron microstructure and EDX. The magnetic properties of the ferrite and nickel metal were characterized by using a laboratory setup with a magnetic field in the range from 0-500 G. The ferrite showed perfect soft spinel phase behavior while the nickel sample showed higher magnetic loss an
... Show More
Background: The Initial (primary) stability is one of the factors that play an important role in the success of the dental implants. The purpose of this study was to evaluate the initial stability of dental implant with horizontal plate by using five analytical tests: insertion torque, removal torque, resonance frequency analysis, push-in test and pull-out test. Materials and methods: Two different lengths of dental implants (5mm and 10mm) were tested in this study; each dental implant was 4mm in diameter with a square threads shape of 1mm pitch and 0.5mm depth. The crestal area was 4.2mm diameter contained a right angle margin circumferential ring while the apical area was tapered with two self-tapping grooves. In this study, the initial s
... Show MoreIn :the _pr sent _paper we report ths. ynthesis ·of a new li:ga!!d..
[f4LJ [{'2 {1-'[(2-hyd•:0xy-.ben:zy1i.den·e)..,bxcJrazanci}:etby-l }benzerieÂ
J,5 t;rtiol .aad its complexes ·w-ith '('Mlif(1 J Fev 1 ), ed(J'l), and. :f.::I:g 01>-)
The ligand \VS preP..ated rin tWo steps' • fp I t}Je nrst stea -soJutiQil Qf
-saUcyla[deeyeq. ip methatt:oJ . re3ctcd lU1der reflux
... Show MoreThree types of metal carboxylates (Ho,Tb and Dy) stearates were LLSed as thennal stabi lizers for PVC. Infrared spectra (1500-1900
|
cm.1
were studied for PVC films stabilized with these metal
carboxylatcs. Two types of oxygen were round -containing products that were formed during the thermal degradation .On the other hand , the presence &nb
... Show More
(1)
(25)
(13)
The work concerned with studying the effect of (SiO2) addition as a
filler on the adhesive properties of (PVA). Samples were prepared as
sheets by using casting method. The mechanical properties showed
that increase in tensile strength from (34MPa) to (68MPa) when
(SiO2) added to (PVA). The adhesive strength showed that joint
properties depend upon specific adhesive characteristic of material
(PVA) and (SiO2\PVA)composites at different concentrations (1.5%,
2.5%, 3.5%, 4.5wt%), the cohesive strength of the adhesive material,
the joint design, and adherent type (Sponge Rubber(SR), Natural
leather (NL), Vulcanized Rubber(VR), and Cartoon). The results
proved the tensile strength increased with (SiO2) ratio, so