Objectives: The research aims to demonstrate the integration between Quantum Computing (QC) and Predictive Analysis (PA) and their role in reducing costs while achieving Sustainable Development Goals (SDGs). The study addresses the inefficiencies in calculating and measuring product costs under traditional systems and examines how QC and PA can enhance cost reduction and product quality to better meet customer needs. Additionally, the research seeks to strengthen the theoretical framework with practical applications, illustrating how this integration improves a company’s competitive position while promoting social, environmental, and economic sustainability.   Methods: The study employs a descriptive analytical approach, focusi

The effect of ethanol and methanol solvent, and their mixture has been studied on the absorption and fluorescence spectra of laser dye Rhodamine B at concentration of (10-4) Molar at room temperature. The molar absorption coefficient has been determined for mixture which was (3.223) at wave number (18181.8 cm-1), Also the Quantum Efficiency of the two solvents (ethanol and methanol) and their mixture have been calculated ,which was for mixture spectrum (38.94%) and it was larger comparing with other and solvents. The characteristics of spectrum has been determined by calculating (??) of absorption spectrum for the solvents and its mixture at maximum wave number ( ) cm-1 depending on solvent polarity and the transitions between molecular ene

Single mode-no core-single mode fiber structure with a section of tuned no-core fiber diameter to sense changes in relative humidity has been experimentally demonstrated. The sensor performance with tuned NCF diameter was investigated to maximize the evanescent fields. Different tuned diameters of of (100, 80, and 60)μm were obtained by chemical etching process based on hydrofluoric acid immersion. The highest wavelength sensitivity was obtained 184.57 pm/RH% in the RH range of 30% –100% when the no-core fiber diameter diameter was 60 μm and the sensor response was in real-time measurements

  A thermal evaporation technique was used to prepare ZnO thin films. The samples were prepared with good quality onto a glass substrate and using Zn metal. The thickness varied from (100 to 300) ±10 nm. The structure and optical properties of the ZnO thin films were studied. The results of XRD spectra confirm that the thin films grown by this technique have hexagonal wurtzite, and also aproved that ZnO films have a polycrystalline structure. UV-Vis measurement, optical transmittance spectra, showed high transmission about 90% within visible and infrared range. The energy gap is found to be between 3.26 and 3.14e.V for 100 to 300 nm thickness respectivly. Atomic Force Microscope AFM (topographic image ) shows the grain size incre

Chemical bath deposition was used to synthesize ZnO nanorods (NRs) on glass and fluorine^_doped tin oxide (FTO) substrates. X-ray diffraction was performed to examine the crystallinity of ZnO nanorod. Results showed that ZnO NRs had a wurtzite crystal structure. Field emission scanning electron microscopy images showed that glass sample had rod-like structure distribution with (50 nm) diameter and average length of approximately (700 nm), whereas the FTO-coated glass sample had 25 nm diameter and average length of approximately 950 nm. The direct optical transition band gaps of the glass and FTO^_coated glass samples were( 4 and 4.43 eV), respectively. The structural and optical properties of the synthesized ZnO p

Zinc Oxide transparent thin films (ZnO) with different thickness from (220 to 420)nm
±15nm were prepared by thermal evaporation technique onto glass substrates at 200 with
the deposition rate of (10 2) nm sec
-1
, X-ray diffraction patterns confirm the proper phase
formation of the material. The investigation of (XRD) indicates that the (ZnO) film is
polycrystalline type of Hexagonal and the preferred orientation along (002) plane. The Optical
properties of ZnO were determined through the optical transmission method using ultraviolet-visible spectrophotometer with wavelength (300 – 1100) nm. The optical band gap values of
ZnO thin films were slightly increased from (2.9 - 3.1) eV as the film thickn