Introduction: The present study was performed to evaluate the influence of a 1064 nm fiber laser on shear bond strength (SBS) at the interface of titanium and resin cement. Methods: Forty titanium discs of 6 mm × 3 mm (diameter and thickness respectively) were categorized into four groups (n=10): control group without any surface treatment and three groups treated with a fiber laser with 81 ns pulse duration, 30 kHz frequency, 10000 mm/s scanning speed, 0.05 mm spot size, and different average power values (3, 5 and 7 W) depending on the tested group. Titanium disc characterization was performed by the scanning electron microscope (SEM) and surface roughness tester. Phase analysis was achieved using an X-ray diffractometer (XRD). F

Polymer matrix composites are suitable materials for medical applications, such as denture base resin polymethyl methacrylate (PMMA). This includes light weight and high strength. This paper describes the effect of selected weight fractions (1, 2, 3, 4 & 5) % wt of nano(Alumina AL2O3, Zirconia ZrO2, Hydroxyapatite HA and Halloysite nanoClay) reinforcements on the biopolymer matrix (PMMA). Some tribology tests were used to evaluate the prepared system (impact strength, hardness surface, and wear rate) tests. The samples were fabricated by (Hand Lay-Up) with different particle reinforcement percentages. All tests were accomplished at room temperature, and samples were developed according to the ASTM standard. The weight fraction of (4% for AL

Some methods recommended abroad to control the oriental hornet, Vespa orientalis L., attacking the honey bee, Apis mellifera L., colonies were tested, with some modifications, for the first time under the Iraqi conditions. One of these methods was carried out by covering the hive entrance with a piece of queen excluder to prevent the hornet from entering the hive. Also, the position of hive stand was reversed to deprive the hornet from using the flight board as a stage for waiting and creeping toward the defending bees. The second method was carried out by fixing a cardboard cone as a bee passage at the hive entrance to hinder the entry of the hornet into the hive. Both of these methods were found to be unsuccessful to

Radiation measuring devices need to periodic calibration process to examine their sensitivity and the extent of the response. This study is used to evaluate the radiation doses of the workers in the laboratories of the Directorate of Safety as a result of the use of point sources in calibrating of the devices in two ways, the first is the direct measurement by the FAG device and the others using RESRAD and RAD PRO programs. The total doses values using FAG were (2.57 μSv/y, 102.3 μSv/y and 20.75 μSv/y for TLD laboratory, Gamma spectroscopy analyses (GSA) laboratory and equipment store respectively, and the total doses that calculated using RESRAD and RAD PRO were 1.518 μSv/y, 76.65 μSv/y and 21.2 μSv/y for the above laboratories. t

This paper investigated the treatment of textile wastewater polluted with aniline blue (AB) by electrocoagulation process using stainless steel mesh electrodes with a horizontal arrangement. The experimental design involved the application of the response surface methodology (RSM) to find the mathematical model, by adjusting the current density (4-20 mA/cm2), distance between electrodes (0.5-3 cm), salt concentration (50-600 mg/l), initial dye concentration (50-250 mg/l), pH value (2-12 ) and experimental time (5-20 min). The results showed that time is the most important parameter affecting the performance of the electrocoagulation system. Maximum removal efficiency (96 %) was obtained at a current density of 20 mA/cm2, distance be

KA Hadi, AH Asma’a, IJONS, 2018 - Cited by 1

Al-Si alloys which are widely used in engineering applications due to their outstanding properties can be modified for more enhancements in their properties. Current work investigated the ability of these alloys to be modified by casting them through the addition of nanoparticles. So, Multi-wall carbon nanotubes (CNT) and titanium carbide ceramic particles (TIC) with size of (20 nm) were added with different amounts started from (0.5 up to 3%) weight  to cast alloy A356 that was considered to be the base metal matrix, then stirred with different speeds of (270, 800, 1500, 2150) rpm at 520 °C for one minute. The results showed change in microstructure’ shape of the casted alloys from the dendritic to spherical gra