The impact of a Schiff base namely 2-((thiophen-2-ylmethylene)amino)benzenethiol  to corrode mild steel in 1 M HCl  resolved was evaluated using different weight loss technique and scanning electron microscopy (SEM).different weight measurements to expand that the 2-((thiophen-2-ylmethylene) amino) benzenethiol  inhibits  the corrosion of mild steel through adsorbing  of  top for mild steel and block the active locality. The inhibitive impacts of 2-((thiophen-2-ylmethylene)amino)benzenethiol  increase with increasing concentration and decrease with increasing temperature. SEM to checking revealed that the alloy surface was quite unaffected and formed protective film on its surface. The investigated

The study included adding antimony oxide to mixtures of coating metal surfaces (Enameling), after it was selected ceramic materials used in the coating metal pieces of the type of steel and cast iron in two layers. The first is called a ground coat and the second is a cover coat.
Ceramic materials layer for ground coat have been melted down in
platinum crucible at a temperature of 1200oC to prepare the glass
mixture (Frit). It was coated on metals at a temperature of 780oC for
two minutes, while the second layer was prepared glass mixture
(Frit) at a temperature of 1200oC, but was coated at a temperature of
760oC for two minutes.
Underwent tests crystalline state of powders (Frits) and enameled samples using X-ray di

The effect of different doping ratio (0.3, 0.5, and 0.7) with thickness in the range 300nmand annealed at different temp.(Ta=RT, 473, 573, 673) K on the electrical conductivity and hall effect measurements of AgInTe2thin film have and been investigated AgAlxIn(1-x) Te2 (AAIT) at RT, using thermal evaporation technique all the films were prepared on glass substrates from the alloy of the compound. Electrical conductivity (σ), the activation energies (Ea1, Ea2), Hall mobility and the carrier concentration are investigated as a function of doping. All films consist of two types of transport mechanisms for free carriers. The activation energy (Ea) decreased whereas electrical conductivity increases with increased doping. Results of Hall Effect

  This study included prepared samples of epoxy reinforced by the novolac , aluminum , glass powder and epoxy reinforced by aluminum , glass powder and epoxy alone .They are used as reinforced materials of volum fraction amounting 40% .  The mechanical properties inclouded ( tensile , compressive and wear) where the wear test inclouded different applied loads (5,10,15) . From the results showed the epoxy reinforced by aluminum and glass powder has higher compressive strength (56.91) Mpa and higher tensile strength (132.2) Mpa .But the epoxy alone has higher wear rate and the epoxy reinforced by aluminum and glass powder which have higher elasticity of modulus from the tensile test (315.7) Mpa

Methotrexate (MTX)is a multiple therapeutic drug, it's used in treatment of ectopic pregnancy, neoplastic disease, autoimmune disorders, and inflammatory conditions. It’s associated with a spectrum of side effect that includes damage to the (liver, kidney, lung and bone marrow). MTX has been associated with fetal malformations in( nervous, skeletal, gastrointestinal, and cardiac) system, and even fetal death. The study was conducted to test the effect of two doses of MTX (5and 10mg/kg) on the development of the mice liver during two gestational age (day11 and day 17) of pregnancy.18 healthy female mice were divided into three groups ,first group (control) was injected with normal saline ,second group injected with 5mg/kg and third grou

  Tomato (Lycopersicon esculentum Mill) and cucumber (Cucumis sativus L.)  seeds were imbided with water at 10°c or 4°c for 4, 8, and 16 hours before planting to study germination rate, mean germination time, and final germination percentage as well as electrolyte leakage from chilled seeds. Seeds imbided more water at 10°c compared to that at 4°c. Coefficient velocity of germination and final percent of germination decreased with the decrease of temperature and increasing time of imbibition. Germination percent under laboratory conditions was higher than that under field conditions. Also, it was found that tomato seeds were more sensitive to chilling imbibition. Electrolyte leakage increased as temperature of imbib

This study sought to determine malformation caused by Ochratoxin-A (OTA) on mouse embryos. Twenty adult female white Swiss mice (mus msculus) were divided into four groups, with five females per group, and with one male placed with two females in a cage. Avaginal plug was observed in the early morning and the day of mating was considered as day of pregnancy followed by the first day of pregnancy. Three sub lethal concentrations of OTA were applied to the respective groups (other than the control), 1mg/kg, 2mg/kg and 4mg/kg. The animals were given 0.1 ml per 10 gm body weight per concentration of OTA once a day during days 7-14 of pregnancy. The control group animals were given distilled water. The pregnant mice were dissected, and the embry

The study of green colour in glass has a special importance on the glass quality, specially the effect of ferrous oxides content of the limestone. Results obtained that there was a reduction in green colour when different ferrous oxide contents in the limestone were added in glass production, limestone sources from two quarries, and the first contains 0.67% ferrous oxide and the second posses less ferrous oxide.

Reduction of green colour showed higher transmittance12% and it could be suggested that reduction of ferrous oxides content in the limestone is of special importance on the optical properties of glass.

The sintering behavior of Alumina was investigated by adding TiO2. The addition of TiO2 lowered the sintering temperature of the Alumina compared with those of pure Alumina. The result suggests that TiO2 acts as an activator for sintering of Alumina. Water absorption, apparent porosity and density were examined for both pure and TiO2 added to Alumina samples. The variations of sintering behavior were discussed in terms of shrinkage, porosity, water absorption and density. Thermal shock resistance was also examined. In term of this work, the way of improving the thermal shock resistance in oxide- based materials by adding reactive Titania powder to the Alumina samples. The laboratory results showed an improvement in thermal shock resistance