Objective: To evaluate and compare the effect of mechanical surface treatment (groove, aluminum oxide particles)
with 45 degree bevel type of joint on tensile bond strength of acrylic specimens repaired by two curing methods
(microwave and water both).
Methodology: Eighty specimens (80) were prepared from pink heat cure acrylic resin. They were divided into two
main groups (40 specimen repaired by microwave energy and 40 specimens repaired by water bath method).Each
group can be divided into four subgroups of ten according to the surface treatment. The control group A was left
intact, group B received no surface treatment, group C and D received surface treatment by (groove, 50 m aluminum
oxide particles). Specimens

Introduction: The current study investigated the use of acid-treated rice husks to remove heavy metals and organic pollutants from water containing heavy metals (R2C and Cd2) and organic pollutants (phenol and atrazine). Methods: The adsorption effect of acid-treated rice husks was compared with other adsorbents such as activated carbon, chitosan, and bentonite clay. Result: both acid-treated rice husks and activated carbon were highly efficient materials, and thus, rice husks were established as a cost-effective alternative. It was revealed that acid treatment of rice husks enhanced adsorption capacity by half, and lead removal was nearly doubled. The most effective pH value for optimizing organic pollutants and heavy metals while

    The main focus of research is on the nature of applications in the fields of science and technology, particularly nanotechnology. In this paper, a simple, non-toxic, inexpensive, and environmentally friendly green method was used to synthesize TiO₂ nanoparticles using the extraction of portulacaria afra plant leaves and TiCl₄ as a precursor. The synthesized titanium dioxide nanoparticles were characterized by scanning electron microscopy, atomic force microscopy, X-ray diffraction patterns, Fourier transform infrared spectroscopy, and Brunauer-Emmett-Teller analysis. The SEM image of TiO₂ nanoparticles showed a few spherical, non-agglomerated particles. The average diameter of the nanoparticles, ac

    Land forms are result from interaction between lithosphere, atmosphere, hydrosphere and biosphere. Lithosphere composed of lithologic units and the main units of the study area are: limestone, marl, marley limestone, sandstone, pebbly sandstone, mudstone, claystone and secondary gypsum in addition to Quaternary sediments. Landforms of the study area can be subdivided according to their origin into many units: 1- Structural- denudational: plateau, mesas, hills, cliffs and wadis; 2- Denudational: desert pavement and mushroom rock; 3-Mass movements; 4- Solution: lake, salt marsh, piping caves; 5- Springs; 6- Fluvial: terraces, alluvial fan, infilled wadi, flood plain; 7- Drainage units; 8-Evaporational: sabkha, secondary

The research includes the preparation of two nano polymer (   ,    ) through a grafted nano ceramic material (aluminum oxide      )(80 nm) by acrylic acid monomer. The latter was extended with two different ester monomers using free radical polymerization. The antibacterial activity of the prepared compounds) performed according to the agar diffusion method.  All compounds (1, 2, 3, 4, NP1, NP2) showed inhibition against bacterial

A laboratory experiment was carried out in the laboratories of College of Agricultural Engineering Sciences, University of Baghdad in 2017. Three factors were studied; Sorghum bicolor L. cultivars (Inqath, Rabeh and Buhoth70), primed and unprimed seed, and salt stress (0, 6, 9 and 12 dS.m−1). The aim was to improve germination and seedling growth under salt stress. The results showed significant superiority of Buhoth70 cultivar compared to others, significantly superiority of primed seed compared to the unprimed and significant negative impact as long as increasing levels of salt stress at germination ratio, plumule length, dry seedling weight and seedling vigor index. The interaction between cultivars, priming and salt stress showed that

The effect of temperature range from 298 K to 348 K and volume filler content ф on electrical properties of polyethylene PE filled with nickel Ni powders has been investigated. The volume electrical resistivity V  of such composites decreases suddenly by several orders of magnitude at a critical volume concentration (i.e. фc=14.27 Vol.%) ,whereas the dielectric constant   and the A.C electrical conductivity AC  of such composites increase suddenly at a critical volume concentration (i.e. фc=14.27 Vol.%).For volume filler content lower than percolation threshold ф<фc the resistivity decreases with increasing temperature, whereas the dielectric constant and the A.C electrical conductivity of

Cadmium sulfide (CdS) thin films with n-type semiconductor characteristics were prepared by flash evaporating method on glass substrates. Some films were annealed at 250 ^oC for 1hr in air. The thicknesses of the films was estimated to be 0.5µ by the spectrometer measurement. Structural, morphological, electrical, optical and photoconductivity properties of CdS films have been investigated by X-ray diffraction, AFM, the Hall effect, optical transmittance spectra and photoconductivity analysis, respectively. X-ray diffraction (XRD) pattern shows that CdS films are in the stable hexagonal crystalline structure. Using Debye Scherrerś formula, the average grain size for the samples was found to be 26 nm. The transmittance of the

The creation and characterisation of biodegradable blend films based on chitosan and polyvinyl alcohol for application in a range of packaging is described. The compatibility between the chitosan and PVA polymers was good. Composite films had a compact and homogeneous structure, according to the morphology analysis. The mechanical test result of PVA/CH at concentrations 5% showed, that The higher values of TS recorded in sample (p1, with 40 MPa) while the lower values appeared in sample (p9, with 22.09 MPa), the TS decreased gradually as the amount of PVA increased in blend film. While the blend film of pure Chitosan exhibits a poor mechanical strength which makes it a poor candidate for packaging but Blending CH with PVA together improved

The results of analyzing BVRI CCD photometry of the spiral galaxies NGC 7339, NGC 7537, and NGC 7541 are presented using the observations acquired with the 1.88m Kottamia telescope (Egypt). The overall structure of the galaxies is analyzed together with isophotal contour maps. The surface brightness profiles of the galaxies are decomposed to bulge and disk components by fitting a de Vaucouleurs law for the bulge and an exponential law for the disk to obtain photometric parameters for each component. The corrected total and absolute magnitudes and integrated color are also obtained and found to be close to the published values. The radial profiles of ellipticity, major-axis position angle, and color are also obtained and discussed.