Iron-Epoxy composite samples were prepared by added
different weight percentages (0, 5, 10, 15, and 20 wt %) from Iron
particles in the range of (30-40μm) as a particle size. The contents
were mixed carefully, and placed a circular dies with a diameter of
2.5 cm. Different mechanical tests (Shore D Hardness, Tensile
strength, and Impact strength ) were carried out for all samples. The
samples were immersed in water for ten weeks, and after two weeks
the samples were take-out and drying to conducting all mechanical
tests were repeated for all samples. The hardness values increased
when the Iron particle concentration increased while the Impact
strength is not affected by the increasing of Iron particles
c

Wheat straw was modified with malonic acid in order to get low cost adsorbent have a good ability to remove copper and ferric ions from aqueous solutions, chemical modification temperature was 120°C and the time was 12 h. Parameters that affect the adsorption experiments were studied and found the optimum pH were 6 and 5 for copper and iron respectively and the time interval was 120 min and the adsorbent mass was 0.1 g. The values for adsorption isotherms parameters were determined according to Langmuir [qmax were 54.64 and 61.7 mg/g while b values were 0.234 and 0.22 mg/l] , Freundlich [Kf were 16.07 and 18.89 mg/g and n were 2.77 and 3.16], Temkin [B were 0.063 and 0.074 j/mol and At were 0.143 and 1.658 l/g] and for Dubinin-Radushkev

The specifications of lubricating oil are fundamentally the final product of materials that have been added for producing the desired properties. In this research, spherical nanoparticles copper oxide (CuO) and titanium oxides (TiO₂) are added to SAE 15W40 engine oil to study the thermal conductivity, stability, viscosity of nano-lubricants, which are prepared at different concentrations of 0.1%, 0.2%, 0.5%, and 1% by weight, and also their pour point, and flash point as five quality parameters. The obtained results show that CuO nanoparticles in all cases, give the best functionality and effect on engine oil with respect to TiO₂. With 0.1 wt. % concentration, the thermal conductivity of CuO/oil and TiO₂/

Off-nucleus isotropic magnetic shielding (σiso(r)) and multi-points nucleus independent chemical shift (NICS(0-2 Å)) index were utilized to find the impacts of the isomerization of gas-phase furfuraldehyde (FD) on bonding and aromaticity of FD. Multidimensional (1D to 3D) grids of ghost atoms (bqs) were used as local magnetic probes to evaluate σiso(r) through gauge-including atomic orbitals (GIAO) at density functional theory (DFT) and B3LYP functional/6-311+G(d,p) basis set level of theory. 1D σiso(r) responses along each bond of FD were examined. Also, a σiso(r) 2D-scan was performed to obtain σiso(r) behavior at vertical heights of 0–1 Å above the FD plane in its cis, transition state (TS) and trans forms. New techniques fo

Coblatcomplex has been prepared by reaction between C16H19N3O3S (L) as ligand and metal salt (II). The prepared complex were characterized by infrared spectra, electromic spectra, magnetic susceptibility, molar conductivity measurement and metal analysis by atomic absorption and (C.H.N) analysis. From these studies tetrahedral geometry structure for the complex was suggested. The photodegredation of complex were study using photoreaction cell and preparednanoTiO2 catalyst in different conditions (concentration, temperatures, pH).The results show that the recation is of a first order with activation energy equal to (6.6512 kJ /mol).

Supra nanoparticles (submicron) of Chicken bones fibers were used (before and after treated with citric acid solution) as additives  to dental composite with the weight ratios (1%, 2% and 4%). The main mechanical tests represented by hardness, wear resistance and compression strength was carried out on the improvement dental composites.

The addition of treated supra nanoparticles Chicken thigh bones with particles size (300 nm) by weight ratio (1%) to ordinary dental composite resin , significantly improves all of its mechanical properties, in addition to the increase the value of the its  glass transition temperature from  43^oC  to 45.4 ^oC. The techniques X-ray diffraction (XRD), Energy Dispersive Spectr

Coblatcomplex has been prepared by reaction between C16H19N3O3S (L) as ligand and metal salt (II). The prepared complex were characterized by infrared spectra, electromic spectra, magnetic susceptibility, molar conductivity measurement and metal analysis by atomic absorption and (C.H.N) analysis. From these studies tetrahedral geometry structure for the complex was suggested. The photodegredation of complex were study using photoreaction cell and preparednanoTiO2 catalyst in different conditions (concentration, temperatures, pH).The results show that the recation is of a first order with activation energy equal to (6.6512 kJ /mol).

The semiconductor ZnO is one of II – VI compound group, it is prepare as thin films by using chemical spray pyrolysis technique; the films are deposited onto glass substrate at 450 °C by using aqueous zinc chloride as a spray solution of molar concentration 0.1 M/L. Sample of the prepared film is irradiating by Gamma ray using CS 137, other sample is annealed at 550°C. The structure of the irradiated and annealed films are analyzed with X-ray diffraction, the results show that the films are polycrystalline in nature with preferred (002) orientation. The general morphology of ZnO films are imaged by using the Atomic Force Microscope (AFM), it constructed from nanostructure with dimensions in order of 77 nm.
The optical properties o

The approach of green synthesis of bio-sorbent has become simple alternatives to chemical synths as they use for example plant extracts, plus green synthesis outperforms chemical methods because it is environmentally friendly besides has wide applications in environmental remediation. This paper investigates the removal of ciprofloxacin (CIP) using green tea nano zero-valent iron (GT-NZVI) in an aqueous solution. The synthesized GT-NZVI was categorized using SEM, AFM, BET, FTIR, and Zeta potentials techniques. The spherical nanoparticles were found to be nano zero-valent, with an average size of 85 nm and a surface area of 2.19m2/g. The results showed that the removal efficiency of ciprofloxacin depends on the initial pH (2.5-10),

The specific activity of 29 soil samples collected from Fuel
Fabrication Facility FFF at AL-Tuwaitha site, 20 km south of
Baghdad were determined using HPGe detector in a low background
configuration, it's relative efficiency of 40%, and resolution of 2keV
for the 1332 keV gamma ray emission of 60Co. The range of activity
concentrations of 226Ra, 232Th and 40K were between (12.56-31.96),
(10.2-18.4) and (47.47-402.1) Bq/kg respectively. In order to assess
any radiological hazard to human health, the absorbed gamma dose
rate D in air at 1m above the ground surface was calculated in the
range (18.87 to 36.46) nGy/h; the outdoor annual effective dose
equivalent AEDE was evaluated to vary from 0.0039 to 0.0076