The cost-effective carbon cross-linked Y zeolite nanocrystals composite (NYC) was prepared using an eco-friendly substrate prepared from bio-waste and organic adhesive at intermediate conditions. The green synthesis method dependent in this study assures using chemically harmless compounds to ensure homogeneous distribution of zeolite over porous carbon. The greenly prepared cross-linked composite was extensively characterized using Fourier transform infrared, nitrogen adsorption/desorption, Field emission scanning electron microscope, Dispersive analysis by X-ray, Thermogravimetric analysis, and X-ray diffraction. NYC had a surface area of 176.44 m2/g, and a pore volume of 0.0573 cm3/g. NYC had a multi-function nature, sustained at a long-

The azo dye (LH) was used to synthesize a series of complexes with Fe(III), Co(II), Ru(III), and Rh(III) metal ions. The ligand (LH) was synthesized by the condensation reaction between tryptamine and 2-hydroxyquinoline. Due to the presence of effective donor atoms (-N=N- azo and OH hydroxyl groups), the ligand was subsequently refluxed with various metal ions, leading to the formation of nonelectrolytic [M:L] (1:2). These compounds were characterized using 1H and 13C-NMR, FT-IR, UV–Vis, mass spectrometry, TGA, DSC, and C.H.N. analysis, along with conductivity, magnetic susceptibility, and metal and chlorine content measurements. The results indicated that the ligand acts as a bidentate, with the complexes adopting an octahedral geometry.

    The discharge of dyes into the water is a significant source of pollution, which is especially concerning given that textile mills are the primary contributor. Nanomaterial-based solutions to this issue have required extensive research and investigation due to their complex nature. In this research, novel nanoparticle were successfully synthesized using the leaves of the Eruca sativa plant. The nano was analyzed using scanning and transmission electron microscopy (SEM and TEM) measurements, and their crystal structure was determined using the X-ray diffraction technique (XRD). The incorporation of NPs resulted in an increase in the uptake of the Cibacron red dye. At a contact time of 30 minutes, observed a faster adsorption o

‎تم في هذه الدراسة ، تزيين ‏رقائق أكسيد الجرافين (‏GO‏) بجسيمات ‏كوبلتيت النيكل النانوية ‏NiCo2O4‎‏(‏NC‏) عن طريق الترسيب في ‏الموقع ، وتم استخدام المتراكب ‏المحضر (‏NC: GO‏) كسطح ماز لإزالة ‏صبغة الميثيل الخضراء ( ‏MG‏) من ‏المحاليل المائية. تم التحقق من ‏التغطية الناجحة لأوكسيد الجرافين ‏بجزيئات كوبلتيت النيكل النانوية ‏‏(‏NC‏) باستخدام دراسات ‏FT-IR‏ وحيود ‏الأشعة السينية (‏XRD‏). كانت أحجام  ‏الجسيم

Cadmium oxide (CdO) thin films were deposited using the sequencing ion layer adsorption and reaction (SILAR) method. In this study, the effect of the pH value of an aqueous solution of cadmium acetate at a concentration of 0.2 mol of the cadmium oxide film was determined. The solution source for the cadmium oxide film was cadmium ions and an aqueous ammonia solution. The CdO films were deposited on glass substrates at a temperature of 90 ℃. The cadmium oxide film thickness was determined by the weight difference method at pH values ​​(7.2, 8.2). X-ray diffraction (XRD) and scanning electron microscopy (SEM) showed that the size of the crystals increased with the increase in the solution (pH). While the UV-visible spectra of the fil

The adsorption of hexavalent chromium by preparing activated carbon from date seeds with zinc chloride as chemical activator and granular date seeds was studied in a batch system. The characteristics of date seeds and prepared activated carbon (ZAC) were determined and found to have a surface area 500.01 m²/g and 1050.01  m²/g , respectively and  iodine number of 485.78 mg/g and 1012.91  mg/g, respectively. The effects of PH value (2-12), initial sorbate concentration(50-450mg/L), adsorbent weight (0.004-0.036g) and contact time (30-150 min) on the adsorption process were studied . For Cr(VI) adsorption on ZAC, at 120 min time contact, pH solution 2 and 0.02  adsorbent  weight  will ach

The purpose of this research was to evaluate rice husk functionalized with Mg-Fe-layered double hydroxide (RH-Mg/Fe-LDH) as an adsorbent for the removal of meropenem antibiotic (MA) from an aqueous solution. Several batch experiments were undertaken using various conditions. Based on the results, the optimal Mg/Fe-LDH adsorbent with a pH of 9 and an M2+/M3+ ratio of 0.5 was associated with the lowest particle size (specifically. 11.1 nm). The Langmuir and Freundlich models were consistent with the experimental isotherm data (R2 was 0.984 and 0.993, respectively), and MA’s highest equilibrium adsorption capacity was 43.3 mg/g. Additionally, the second-order model was consistent with the adsorption kinetic results.

Green synthesis of bimetallic nanoparticles of Fe/Ni (G-Fe/Ni-NPs) and zeolite-5A supported (G-Z-Fe/Ni-NPs) as heterogeneous Fenton-like oxidation for the decolourisation of reactive red 120-dye (RR120) from the aqueous medium using green tea extract as a reducing agent. Zeolite-5A from local kaolin is prepared and characterised using the hydrothermal method and is used as a supporting material for Fe/Ni-NPs. (SEM), (EDX), (AFM), (XRD), (FT-IR), (BET). Its zeta potential were used to characterise G-Fe/Ni-NPs and G-Z-Fe/Ni-NPs. The decolourisation efficiency (Ed) of the RR120-dye using a heterogeneous Fenton-like for G-Fe/Ni-NPs and G-Z-Fe/Ni-NPs is 99.8% and 99.9%, respectively, under the optimum conditions: [H2O2] = 20 and 1 mmol/L