In this study, pure SnO₂ Nanoparticles doped with Cu were synthesized by a chemical precipitation method. Using SnCl₂.2H₂O, CuCl₂.2H₂O as raw materials, the materials were annealed at 550°C for 3 hours in order to improve crystallization. The XRD results showed that the samples crystallized in the tetragonal rutile type SnO₂ stage. As the average SnO₂ crystal size is pure 9nm and varies with the change of Cu doping (0.5%, 1%, 1.5%, 2%, 2.5%, 3%),( 8.35, 8.36, 8.67, 9 ,7, 8.86)nm respectively an increase in crystal size to 2.5% decreases at this rate and that the crystal of SnO₂ does not change with the introduction of Cu, and S

Four metal complexes of Schi base ligand were prepared. To characterize both the ligand and the metal complexes, various techniques were employed, including elemental analysis, FT-IR spectroscopy, UV-Vis spectroscopy, molar conductivity measurements, magnetic moment determination, melting point, mass spectroscopy, 1H-NMR and 13C-NMR spectroscopy. The results showed that the metal complexes formed have the formula [M(L)2Cl2]Cl(n).H2O, where LD Schi base ligand and MDCr(III), Rh(III), Pt(IV) and Au(III), n D 1, 2. Based on spectroscopic analysis, coordination with metal ions involves the ’N’ donor atom of N atoms of the imine and the N-H amid group, and four complexes are suggested to have a six-coordinated octahedral structure. Molar c

Background: Morphological and histological examination of the testes can provide a suitable insight into the health of the reproductive system. Aim: The objective of the current study was to investigate the morphological and histological features of the testes of local pigeons (Columba livia domestica) at mature and immature stages of age. Methods: Two groups of collected specimens underwent macroscopic and microscopic investigation to evaluate and compare the main general properties of their testes. Results: The findings indicated that the testis has an oval shape in both pre-puberty and post-puberty stages, situated on the inner side of the kidney towards the caudal extreme of the lungs. However, the left testis was bigger than those on t

Poly [2-methoxy-5-(2-ethylhexyloxy)-1, 4-phenylenevinyl] (MEH-PPV) thin films were created in this study using both spin coating and drop casting processes. MEH-PPV thin films generated by Ferric Chloride (FeCl3) doping (0.03, 0.06, 0.09, and 0.12 wt%) were studied for some physical features using Fourier-Transform Infrared Spectroscopy (FTIR), Field Emission Scanning Electron Microscopy (FE-SEM), and Energy Dispersive X-ray Spectroscopy (EDX). An FTIR test showed that there was no chemical reaction that occurred between Ferric Chloride (FeCl3) and MEH-PPV, but rather a physical one, that is, an organic material composite occurred. As for FE-SEM, the pure sample MEH-PPV formed uniformly, but when FeCl3 was added by weight, we have differ

ABSTRACT: Thin film of CdS has been deposited onto clean glass substrate by using Spray pyrolysis technique. Results of Morphological (AFM) studied; electrical properties and optical conductivity studied are analysis. AFM results show a crystalline nature of the films. From the conductivity measurement at different temperatures, the activation energy of the films was calculated and found to be between 0.188 - 0.124 eV for low temperature regions, and between 1.67-1.19eV for high temperature regions. Hall measurements of electrical properties at room temperature show that the resistivity and mobility of CdS polycrystalline films deposited at 400 C0, were 3.878x103 . cm and 1.302x104cm2/ (V.s), respectively. The electrical conductivity of th