Several schottky diodes were fabricated from polyaniline/ Carbon nanotube (single and multiwalled) composites. These composites were synthesized with different concentration and two carbon nanotubes types, Single and Multi-Walled Carbon Nanotubes (SWCNT & MWCNT). Aluminum and silver paste were chosen as schottky and ohmic contact respectively. physical and electrical were used to studied these composite by using Atomic Force Microscopy (AFM) and electrical measurements. The Root Mean Square RMS surface roughness of the composite samples was found to be around 4nm. The currentvoltage characteristic were measurements for all samples in the bias range ±15V at room temperature. The results shows the increasing in carbon nanotubes concentration

There are no single materials which can withstand all the extreme operating conditions in modern technology.  Protection of the metals from hostile environments has therefore become a technical and economic necessity.  

In this work, for enhancing their wear-resistance, boride layers were deposited on the surface of low carbon steel by a pack cementation method at 850 °C for (2, 4, and 6) h using vacuum furnace. The boronizing process was achieved using different concentration of boron source (20, 25, and 30) % wt. into coating mixture to optimize the best conditions which ensure the higher properties with lower time. The coating was characteristic by X ray diffraction (XRD), and it is confirmed t

Overlapped have been prepared from epoxy resin material added to carbon Nanotube and percentages weight (0.1, 0.05, 0.01) % Studied the mechanical properties of the composite (bending, tensile an d hardness) has been found that the Flexural and tensile modulus of the composites were higher than the pure epoxy resin this may be due to the high mechanical strength of carbon nano tube (CNT). The hardness of the epoxy carbon Nanotube composites increased and the reason is due to increased overlap and stacking between the additives and material basis, which reduces the movement of polymer molecules leading to increased resistance to scratching material and cutting, will become more resistance to plastic deformation.

The Electro-Fenton oxidation process is one of the essential advanced electrochemical oxidation processes used to treat Phenol and its derivatives in wastewater. The Electro-Fenton oxidation process was carried out at an ambient temperature at different current density (2, 4, 6, 8 mA/cm²) for up to 6 h. Sodium Sulfate at a concentration of 0.05M was used as a supporting electrolyte, and 0.4 mM of Ferrous ion concentration (Fe²⁺) was used as a catalyst. The electrolyte cell consists of graphite modified by an electrodepositing layer of PbO₂ on its surface as anode and carbon fiber modified with Graphene as a cathode. The results indicated that Phenol concentration decreases with an increase in current dens

It has been a well-known practice to use seeds and the essential oil of Carum copticum as a strongly  antiseptic ,  antispasmodic ,  aromatic  , bitter ,  diaphoretic  ,  digestive  ,  diuretic , expectorant  and tonic. Also used for cure influenza, asthma, and rheumatoid arthritis. To our knowledge it will be the first time to use the seeds of this herb as a urinary tract stone lithotripsy.This research aimed to the use of these seeds as a lithotripsian against different types of urinary stones and determine the efficiency of these preparation against which types of stone.A liquid solution was prepared from dissolving the seeds powder in cow milk and then concentration this prep

Background: Thalassemia is a hereditary anemia resulting from defects in hemoglobin production. ?- thalassemia caused by decrease in the production of ?- globin chains affect multiple organs and is associated with cranio-oro-facial deformity which include prominent cheek bones and protrusive premaxilla with depression of the nasal bridge often referred to as “rodent or chip-munk face” with small mandible and Cl.II skeletal relationship. This study aimed to investigate cephalometric craniofacial parameters (skeletal) of ?- thalassemic major patients by using computed tomography and to compare findings with a group of healthy patients in the same age group. Subject, Materials and Method: The study included (40) patients with ?- thalassemi

Photocatalytic degradation of methylene blue was studied using CdS and ZnS as catalyst. The photocatalytic activity of the specimen was studied by exposing to UV-radiation. The result shows that the degradation efficiency of the dye for CdS micro-particles was 92% after 7 hours and for ZnS micro-particles was 88.29% for the same time interval.