This study is concerned with the reality of total quality management and its role in achieving the excellence performance of the employees of the Institute of Technology / Baghdad, excellence performance is described by the extent to which the organization is able to invest the effort of the human resource to achieve its Objectives by adopting the principles of Total Quality Management (TQM) according to some of its basic dimensions in proportion to the reality and Possibilities Institute, the aim is to study to know the reality of total quality management ,and indicate the levels of excellence performance in the Institute of Technology / Baghdad,

n-Hexane conversion enhancement was studied by adding TCE (Trichloro-ethylene) on feed stream using 0.3%Pt/HY zeolite catalyst. All experiments were achieved at atmospheric pressure and on a continuous laboratory unit with a fixed bed reactor at a temperature range 240-270◦C, LHSV 1-3h-1, H2/nC6 mole ratio 1-4.
By adding 435 ppm of TCE, 49.5 mole% conversion was achieved at LHSV 1h-1, temperature of 270ºC and H2/nC6 mole ratio of 4, while the conversion was 18.3 mol% on the same catalyst without adding TCE at the same conditions. The activation energy decreased from 98.18 for pure Pt/HY zeolite to 82.83 kJ/mole by adding TCE. Beside enhancement the activity, selectivity and product distribution enhanced by providing DMB (Dimethyl b

Сатья посвящена выделению и описанию функциональных стилей русского языка. В работе будет предствлена стилистическая характеристика заимствованной лексики, которая в некоторых случаях заменяет собственно русские слова, что может приводить к затемнению смысла высказывания, эвфемизации его, кроме того, заимствования заполняют определенные стилистические книши, образовавшиеся в связи со структурны

Films of CdSe have been prepared by evaporation technique with thickness 1µm. Doping with Cu was achieved using annealing under argon atmosphere . The Structure properties of these films are investigated by X-ray diffraction analysis. The effect of Cu doping on the orientation , relative intensity, grain size and the lattice constant has been studied. The pure CdSe films have been found consist of amorphous structure with very small peak at (002) plane. The films were polycrystalline for doped CdSe with (1&2wt%) Cu contents and with lattice constant (a=3.741,c=7.096)A°, and it has better crystallinty as the Cu contents increased to (3&5wt%) Cu. The reflections from [(002), (102). (110), (112), and (201)]planes are more prominen