Reflection cracking in asphalt concrete (AC) overlays is a common form of pavement deterioration that occurs when underlying cracks and joints in the pavement structure propagate through an overlay due to thermal and traffic-induced movement, ultimately degrading the pavement’s lifespan and performance. This study aims to determine how alterations in overlay thickness and temperature conditions, the incorporation of chopped fibers, and the use of geotextiles influence the overlay’s capacity to postpone the occurrence of reflection cracking. To achieve the above objective, a total of 36 prism specimens were prepared and tested using an overlay testing machine (OTM). The variables considered in this study were the thickness of the

Reflection cracking in asphalt concrete (AC) overlays is a common form of pavement deterioration that occurs when underlying cracks and joints in the pavement structure propagate through an overlay due to thermal and traffic-induced movement, ultimately degrading the pavement’s lifespan and performance. This study aims to determine how alterations in overlay thickness and temperature conditions, the incorporation of chopped fibers, and the use of geotextiles influence the overlay’s capacity to postpone the occurrence of reflection cracking. To achieve the above objective, a total of 36 prism specimens were prepared and tested using an overlay testing machine (OTM). The variables considered in this study were the thickness of the

Glass Ionomer Cement (GIC) is one of the important dental temporary filing materials. The aim of this study is to evaluate the effect of adding 3, 5 and 7 wt. % of TiO₂ microparticles to conventional GIC powder (Riva Self Cure) on mechanical properties and its effect on absorption and solubility processes. TiO₂ particles additives improved compressive strength and biaxial flexural strength, where the compressive strength increased with increasing in the added ratio, while the highest value of the biaxial flexural strength was at 3 wt.%. The addition of TiO₂ particles improved the surface Vickers microhardness values, with highest value at 5 wt. %. On other hand TiO₂ addition im

Nanoferrite materials have been synthesized by sol-gel auto combustion method. The effect of doping different percentages of Y₂O₃ (0.34 µm) on the physical and mechanical properties of selected mixed ferrite [(Li_2.5Fe_0.5) 0.9(Co₄Fe₂O₄) _0.1] by adding 10% Cobalt ferrite was studied. Physical properties (i.e. .density, porosity and water absorption) were affected by the doping, where the density increased about 32% at 6 wt% Y₂O₃, while porosity has a drastically decreased about 80% at 6% Y₂O₃ and has a correlation effect on the mechanical properties(Splitting  tensile strength and Vicker

 In this research, we studied the effect of (β-rays) on the optical properties of pure  (PMMA) films prepared by using casting technique, and the optical properties for these  films was studied before and after irradiation  by recording the Absorption and Transmission spectra  for a range of wavelength range (190-1100) nm. and then the absorption and Transmission and the reflectivity, extinction coefficient, refractive index, and real and imaginary parts of dielectric constant was studied

The objective of this study was to investigate and find the relationships between human semen osmolality and oxidative stress with semen quality. Semen analysis was determined to evaluate semen quality and fertility. The concentration of semen malondialdehyde (MDA) was measured to assess oxidative stress. For this purpose, one hundred seventy healthy adult males were used in this study. The study was conducted from September 2018 to November 2019 in the Infertility care and in vitro fertilization center (IVF) and the Biology department of the College of Science at Salahaddin University in Erbil city. A significant positive correlation was observed between the total sperm motility, grade activity, and sperm motility index with semen osmol

Experts have given much attention on the use of waste in asphalt paving because of its significance from a sustainability perspective. This paper evaluated the performance properties of asphalt concrete mixes modified with Crumb Rubber (CR) as a partial replacement for two grade sizes of fine aggregate (2.36, and 0.3 mm) at six replacement rates: 0%, 2%, 4%, 6%, 8%, and 10% by weight. Asphalt concrete mixes were prepared at their Optimum Asphalt Content (OAC) and then tested for their engineering properties. Marshall properties, fatigue, rutting, ideal CT index test, Scanning Electron Microscopy (SEM), and Energy-Dispersive X-ray (EDX) spectroscopy were deployed to examine the crystalline structure and elemental composition of the C

In this study porcelain was prepared by using composition consisting of raw materials with in following fractions , 50% kaolin , 25% feldspar, and 25% silica( SiO2) tested by XRay diffraction (XRD) method .Study the effect additives at different concentration from zirconia (ZrO2) (2,5,10,15,20) Wt% on some physical properties of porcelain, the sample is prepared by the conventional manufacturing method , It is found that some physical properties of porcelain changes considerably with the substituent sample, It was found that the increase of zrconia (ZrO2) additive of all our sample produce. Increasing in dielectric constant and bulk density and decreasing with open porosity and dielectric loss tangent