Objective: The purpose of this work was to develop and optimize the emulgel formulation of piroxicam with two types of gelling agent chitosan and xanthan gum. The release profiles of prepared formulas were investigated. In addition, the rheology and stability of the best formula were investigated.Methods: Emulsified piroxicam was prepared to use oleic acid, tween 80 and PG with a ratio (3:10:10). In xanthan based emulgel, the xanthan gum (1% and 1.5%) was spread as powder on emulsified piroxicam with stirring until emulgel was formed. In chitosan-based emgels, Chitosan gel was added to emulsified piroxicam and stirring until the Emulgel was constructed. Chitosan gels were prepared by incorporating different concentration, 2%, 3%, 6% w/v of chitosan in 1% v/v of glacial acetic acid in distilled water. In vitro release of piroxicam from different formulas was conducted in 300 ml phosphate buffer pH 7.4, at a speed of 120 rpm at 37±2°C. The amount of the drug released from the bases was determined spectrophotometrically at 504 nm. Viscometer Myr. Vr 3000 was used to measure the viscosity of the prepared formulas. The prepared formulas were stored in well-stoppered polyvinyl chloride (PVC) plastic containers in the dark for 6 mo at room temperature. They were checked for drug content, viscosity, and pH change bimonthly throughout the period.Results: The results showed that the dissolution increases significantly with increasing the concentration of xanthan. Chitosan has significant synergized the enhancements of xanthan gum in the release. Rheological behaviour of the selected formula containing chitosan (2%) and xanthan gum (1.5) had shear thinning in nature showing a decrease in viscosity at the increasing shear rates. The selected formula was stable 6 mo at 40˚C/75% RH and 4˚C. The formula found was yellow viscous creamy preparation with the smooth homogenous appearance. The pH and the drug release was also found to be stable under storage conditions.Conclusion: Piroxicam release can be improved by preparing emulgel which stable and have good rheologic properties.
The aim of this research is to benefit from recycl the aircraft waste oils which is discarded in sewage network, to be used in preparation of greases for industrial purposes and to reduce the environmental pollution. In this research synthetic greases were prepared with special specifications by mixing the waste oils after treating with (silica gel as adsorbent agent, and filtration to precipitate impurities then heated to 110 C? to get rid of water) bentonite produced in Iraq which is available and cheap with existence of high density polyethylene at specific conditions of ( heating and mixing) . The best weight proportion were reached, then paraffin wax and additives were added to improve the properties of grease and give the
... Show MorePolyvinyl alcohol, (PVA) was prepared using polyvinyl acetate emulsion (manufactured by Al-Jihad factory,
That-Al-Sawary Company) as a local raw material. In this investigation, polyvinyl acetate emulsion was converted to
solid form by coagulation the polymer from its emulsion using sodium sulphate salt as coagulant aid, then alcoholyzed
the solid polyvinyl acetate in methanol using sodium hydroxide as catalyst, polyvinyl alcohol produced by this method is
a dry, white to yellow powder.
Three affecting variables on the degree of hydrolysis of PVA were studied, these variable are Catalyst to
polymer weight ratio in the range of 0.01 – 0.06, reaction time in the range of 20 – 90 min, and reaction temperature in
the
Abstract: In this research, nanofibers have been prepared by using an electrospinning method. Three types of polymer (PVA, VC, PMMA) have been used with different concentration. The applied voltage and the gap length were changed. It was observed that VC is the best polymer than the other types of polymers.
In this research, nanofibers have been prepared by using an electrospinning method. Three types of polymer (PVA, VC, PMMA) have been used with different concentration. The applied voltage and the gap length were changed. It was observed that VC is the best polymer than the other types of polymers.
4-methylaniline and its Schiff base derivative were intercalated into the Bentonite clay interlayers in a solid state reaction followed by a condensation reaction to produce two organo-clay composites. X-ray diffraction was used to identify the changes in basal spacing of montmorillonite layers which exhibited noticeable alteration before and after the formation of the composites. FT-IR spectra, on the other hand, were utilized for identifying the structural compositions of the prepared materials as well as the formation of the intercalated Schiff base derivative. The surface morphology of the composites was examined by Scanning Electron Microscopy SEM and Atomic Force Microscope AFM, which reflected some differences in the surface of prepa
... Show MoreThe utilization of recycled brick tile powder as a replacement for conventional filler in the asphalt concrete mix has been studied in this research. This research evaluates the effectiveness of recycled brick tile powder and determines its optimum replacement level. Using recycled brick tile powder is significant from an environmental standpoint as it is a waste product from construction activities. Sixteen asphalt concrete samples were produced, and eight were soaked for a day. Samples contained 5% Bitumen, 2% to 5% brick tile powder, and conventional stone dust filler. The properties of samples were evaluated using the Marshall test. It was observed that the resistance to stiffness and deformation of asphalt concrete
... Show MoreIn the present study, multi-walled carbon nanotubes (MWCNTs) with outside diameters of< 8 nm and 20−30 nm were covalently functionalized with β-Alanine using a novel synthesis procedure. The functionalization process was proved successful using Raman spectroscopy, FTIR, and TEM. Utilizing the two-step method with ultrasonication, the MWCNTs treated with β-Alanine (Ala-MWCNTs) with weight concentrations of 0.025%, 0.05%, 0.075%, and 0.1% were dispersed in distilled water to prepare water-based nanofluids. The aqueous colloidal dispersions of pristine MWCNTs were unstable. While for Ala-MWCNTs and after> 50 days from preparation, higher colloidal stability was obtained up to relative concentration of 0.955 and 0.939 for the 0.075-wt% samp
... Show MoreBecause of the conservation problems causes by the existence of water hyacinth (W.H) as an watery plant in water bodies of Iraq, our study aimed to make use of (W.H) by isolation of microcrystalline cellulose, and a new method of preparation of Nano crystalline cellulose. Microcrystalline cellulose was produced using base bleaching method by sodium hypochlorite [NaOCl] to remove unorganized region of cellulose and lignin to create particles comprising of micro crystal and preparing of Nano crystalline cellulose from microcrystalline cellulose by acid hydrolysis and ultrasonic treatment. The Nano crystalline and microcrystalline cellulose characterized by AFM, FTIR, XRD and TGA. FT-IR spectra of microcrystalline cellules and Nano cr
... Show More