In this study, thin flms containing titanium dioxide (TiO₂), iron (III) oxide (Fe2O3) and cerium oxide (CeO2), with varying Fe2O3:CeO2 concentrations ranging from 0 to 30 wt% and 10 wt% gold nanoparticles (AuNPs), were prepared on glass using chemical spray pyrolysis. The structural, morphological, and sensing properties of the prepared thin flms were examined. XRD analysis revealed that a phase transformation occurred based on the dopant concentration: flms with x = 0 or 0.1 formed a polycrystalline anatase structure, whereas those with intermediate concentrations (x = 0.15 or 0.20) were amorphous. At higher doping concentrations (x = 0.25, 0.30), the structure developed a hematite Fe2O3, CeO2 and Au phase. Morphologicall

In this work, magnesium aluminate spinel (MA) (MgO 28 wt%, Al2O3 72 wt%) stoichiometric compound , were synthesized via solid state reaction (SSR) Single firing stage, and the impact of sintering on the physical properties and thermal properties as well as the fine structure and morphology of the ceramic product were examined. The Spinel samples were pressed at of (14 MPa) and sintering soaking time (2h). The effect of adding oxide titania (TiO2) was studied. The obtained powders were calcined at a temperature range of 1200 and 1400 °C. The calcined samples spinel were characterized by XRD, it showed the presence of developed spinel phase end also showed that the best catalyst is titania. The SEM image showed the high sintering temperat

In this research study the effect of fish in alternating electrical properties at room temperature copper oxide membranes and fish prepared in a manner different thermal spraying chemical on a thin glass bases and heated

Rare-earth metal oxides (REMOs) exhibit distinctive properties, among which cerium oxide (CeO2) displays numerous industrial, technological, and medical applications. However, the inclusion of hafnium (Hf) at the cerium (Ce) site to form the (Ce1-ₓHfₓO2) lattice system at a concentration of x = 0.25 would have an impact on enhancing the physical properties of the simulated configuration. Density functional theory (DFT) was used to perform the calculations, supported by the Hubbard correction factor (U). The generalized gradient approximation (GGA-PBE) was employed to analyze the electronic, structural, optical, and mechanical properties at hydrostatic pressures (P = 0, 25, 50, 75, and 100 GPa). The ground state geometry of the pristine

In this work, pure and Ag-doped nickel oxide (NiO) thin films were deposited on glass substrates with different dopant concentrations (0.1, 0.2, 0.3 and 0.4 wt.%) by pulsed-laser deposition (PLD) technique at room temperature. These films were annealed at temperature of 450 °C. The structural and optical properties of the prepared thin films were studied. It was found that annealing process has lead to increase the transmittance of the deposited films. Also, the transmittance was found to increase with doping concentration of silver in the deposited NiO films. The optical energy gap was decreased from 3.5 to 3.2 eV as the doping concentration was increased to 0.4 %.

In this work, two cone-inverted cylindrical and cross-hybrid dielectric resonator antennas are stacked and excited by the coaxial probe method with an operating standard resonant frequency of 5.438 GHz. A drawback of these standard Dielectric Resonator Antennas (DRAs) is their narrow bandwidth. For good antenna performance, a stacked DR geometry and a thick dielectric substrate having a low dielectric constant are desired since this provides large bandwidth, better radiation power, reduces conductor loss and nonappearance of surface waves. Many approaches, such as changing the shape of the dielectric resonator, have been used to enhance bandwidth. Using DRA, having the lowest dielectric constant, increases the bandwidth and the electroma

The dielectric permittivityεand ac conductivityσac of CuInSeTe thin films were measured at temperatures in the range of 303–453 K and frequencies in the range of 100 Hz–10 MHz. It is found that the ac activation energy estimated from the Arrhenius equation is 0.1004 eV which increases with substrate temperature and decreases with the increase of frequency. The exponentsshows a progressive increase withTs. The results are explained in terms of structural difference by the effect ofTs and thermal treatment.

Epoxy (EP) – Silica (SiO2) composites are well known composites used in microelectronic industry . So it is important to study their dielectric behavior under different conditions such as
the presence carbon black (UV absorber) and immersion in the water for 30 days .
Dielectric properties were calculated over the frequency range 102 – 106 Hz for epoxy composites with different weight % of micrometer 1.5μm SiO2 particles (60%, 65% and 70wt%) modified with 0.5wt% silane coupling agent to improve adhesion between EP and SiO2 phases .