Three  types of  metal  carboxylates  (Ho,Tb  and  Dy) stearates were LLSed  as thennal stabi lizers for PVC. Infrared spectra (1500-1900

cm.1

were   studied   for  PVC   films   stabilized   with   these   metal

carboxylatcs.  Two types of oxygen  were round -containing  products that were formed during  the thermal degradation  .On the other hand , the  presence &nb

The aim of this work is to produce samples from Iraqi raw materials like Husyniat Bauxite (raw and burnt) and to study the effect of some additives like white Doekhla kaolin clays and alumina on that material properties were using sodium silica as a binding material. Five mixtures were prepared from Bauxite (raw and burnt) and kaolin clays, with an additive of (40) ml from sodium silica and alumina of (2.5, 5, 7.5,10 wt %) percentage as a binding material. the size grading was through sieving. The formation of all specimens was conducted by a measured gradually semi-dry pressing method under a compression force of (10) Tons and humidity ratio ranging from (5-10) % from mixture weight. Drying all specimens was done and then they were burn

Introduction: We aimed to evaluate the shear bond strength of acrylic denture teeth to flexible and heat-cured denture base material after surface treatments with argon plasma, chemical bonding agent (PALFIQUE universal), and combination. Methods: A total of 80 incisor acrylic denture teeth were treated with a argonplasma, chemical bond (PALFIQUE universal bond), and a combination with 10 samples for each group. The neck (gingival portion) of teeth was cut at a 45° angle, and the teeth were attached to heat-cured acrylic resin and flexible denture base material. All the specimens were stored in artificial saliva for 7 days in an incubator (37 °C). A shear

This research studies the effect of adding micro, nano and hybrid by ratio (1:1) of (Al2O3,TiO2) to epoxy resin on thermal conductivity before and after immersion in HCl acid for (14 day) with normality (0.3 N) at weight fraction (0.02, 0.04, 0.06, 0.08) and thickness (6mm). The results of thermal conductivity reveled that epoxy reinforced by (Al2O3) and mixture (TiO2+Al2O3) increases with increasing the weight fraction, but the thermal conductivity (k) a values for micro and Nano (TiO2) decrease with increasing the weight fraction of reinforced, while the immersion in acidic solution (HCl) that the (k) values after immersion more than the value in before immersion.

In this study the thermal conductivity of the epoxy composites were characterized as function of volume fraction, particle size of fillers and the time of immersion(30,60,90)days in water .Composites plates were prepared by incorporating (bi-directional) (0º-90º) glass fiber and silicon carbide (SiC) particles of (0.1,0.5,1)mm as particle size at (10%,20%,30%,40%) percent volume in epoxy matrix.
The composites shows slightly increase of the thermal conductivity with increasing volume fraction, particle size and increase with increasing the days of immersion in water. The maximum thermal conductivity (0.51W/m.K) was obtained before the immersion in water at 90 days for epoxy reinforcement by bi-directional glass fiber and SiC particl

This work involves the calculation of the cooling load in Iraqi building constructions taking in account the effect of the convective heat transfer inside the buildings. ASHRAE assumptions are compared with the Fisher and Pedersen model of estimation of internal convective heat transfer coefficient when the high rate of ventilation from ceiling inlet configuration is used. Theoretical calculation of cooling load using the Radiant Time Series Method (RTSM) is implemented on the actual tested spaces. Also the theoretical calculated cooling loads are experimentally compared by measuring the cooling load in these tested spaces. The comparison appears that using the modified Fisher and Pedersen model when large ventilation ra

Simple, economic and sensitive mathematical spectrophotometric methods were developed for the estimation 4-aminoantipyrine in presence of its acidic product. The estimation of binary mixture 4-aminoantipyrine and its acidic product was achieved by first derivative and second derivative spectrophotometric methods by applying zero-crossing at (valley 255.9nm and 234.5nm) for 4-aminoantipyrine and (peak 243.3 nm and 227.3nm) for acidic product. The value of coefficient of determination for the liner graphs were not less than 0.996 and the recovery percentage were found to be in the range from 96.555 to 102.160. Normal ratio spectrophotometric method 0DD was used 50 mg/l acidic product as a divisor and then measured at 299.9 nm with correlat

    Simple, economic and sensitive mathematical spectrophotometric methods were developed for the estimation 4-aminoantipyrine in presence of its acidic product. The estimation of binary mixture 4-aminoantipyrine and its acidic product was achieved by first derivative and second derivative spectrophotometric methods by applying zero-crossing at (valley 255.9nm and 234.5nm) for 4-aminoantipyrine and (peak 243.3 nm and 227.3nm) for acidic product. The value of  coefficient of determination  for the liner  graphs were  not less than 0.996 and the recovery percentage were found to be in the range from 96.555 to 102.160. Normal ratio spectrophotometric method 0DD was used 50 mg/l acidic product as a divisor