This paper attempted to study the effect of cutting parameters (spindle speed and feed rate) on delamination phenomena during the drilling glass-polyester composites. Drilling process was done by CNC machine with 10 mm diameter of high-speed steel (HSS) drill bit. Taguchi technique with L16 orthogonal layout was used to analyze the effective parameters on delamination factor. The optimal experiment was no. 13 with spindle speed 1273 rpm and feed 0.05 mm/rev with minimum delamination factor 1.28.                                       &

Background: Tooth wear is one of the most common problems in the older dentate population which results from the interaction of three processes (attrition, abrasion and erosion) and it affects all societies, different age groups, and all cultures. This study was achieved to evaluate the prevalence and distribution of tooth wear among institutionalized residents in Baghdad city\ Iraq. Subjects and Methods: This survey was accomplished on four private and one governmental institution in Baghdad city. One-hundred twenty three (61 males, 62 females) aged 50-89 years were participated in this study. The diagnosis and recording of tooth wear were according to criteria of Smith and Knight. Results: The prevalence of tooth wear was 100% with a mean

There were many ideas and opinions on the linkage between growth and economic reform  in both developed and developing countries. The relationship is, of course, existed. Therefore, this research comes to analyses it in the Iraqi economy. This study is based on a hypothesis that the economic reformation in Iraq leads to lag level of growth with the of high rates of inflation. However, the study is designed to be included five sections. It found a positive relationship between the economic reformation and slowing of economic growth, in which the specified hypothesis is not fit to the economic reality in Iraq after 2003                  &

The Iraqi political and social arena has been characterized, subjectively and objectively, by the weakness of leadership building. This has led to a leadership crisis, which is reflected in the quality of the outcome of the process of rebuilding the state in Iraq. Thus, this building process has lacked the simplest requirements and conditions of success. It has suffered from a major and obvious failure: the situation in Iraq has raised conflict leaders, not constructive leaders, and this confirms the existence of a cultural crisis in the production of conscious, aware leadership compatible with democratic action. The weakness of leadership in Iraq is reflected in a series of ongoing crises that require radical solutions in accordance with l

Three-dimensional cavity was investigated numerical in the current study filled with porous medium from a saturated fluid. The problem configuration consists of two insulated bottom and right wall and left vertical wall maintained at constant temperatures at variable locations, using two discretized heaters. The porous cavity fluid motion was represented by the momentum equation generalized model. The present investigation thermophysical parameters included the local thermal equilibrium condition. The isotherms and streamlines was used to examine energy transport and momentum. The meaning of changing parameters on the established average Nusselt number, temperature and velocity distribution are highlighted and discussed.

In this research the behavior of reinforced concrete columns with large side openings under impact loads was studied. The overall cross sectional dimensions of the column specimens used in this research were (500*1400) mm with total height of (14000) mm. The dimensions of side openings were (600*2000) mm. The column was reinforced with (20) mm diameter in longitudinal direction, while (12) mm ties were used in the transverse direction. The effect of eccentric impact loads on the horizontal and vertical displacement for this column was studied.                              &

This paper investigates the experimental response of composite reinforced concrete with GFRP and steel I-sections under limited cycles of repeated load. The practical work included testing four beams. A reference beam, two composite beams with pultruded GFRP I-sections, and a composite beam with a steel I-beam were subjected to repeated loading. The repeated loading test started by loading gradually up to a maximum of 75% of the ultimate static failure load for five loading and unloading cycles. After that, the specimens were reloaded gradually until failure. All test specimens were tested under a three-point load. Experimental results showed that the ductility index increased for the composite beams relative to the refe

This paper investigates the experimental response of composite reinforced concrete with GFRP and steel I-sections under limited cycles of repeated load. The practical work included testing four beams. A reference beam, two composite beams with pultruded GFRP I-sections, and a composite beam with a steel I-beam were subjected to repeated loading. The repeated loading test started by loading gradually up to a maximum of 75% of the ultimate static failure load for five loading and unloading cycles. After that, the specimens were reloaded gradually until failure. All test specimens were tested under a three-point load. Experimental results showed that the ductility index increased for the composite beams relative to the reference specim