Fatigue failure is almost considered as the predominant problem affecting automotive parts under dynamic loading condition. Thus, more understanding of crack behavior during fatigue can strongly help in finding the proper mechanism to avoid the final fracture and extent the service life of components. The main goal of this paper is to study the fracture behavior of low carbon steel which is used mostly in automotive industry. For this purpose, the fractography of samples subjected to high and low stress levels in fatigue test then was evaluated and analyzed. Hardness and tensile tests were carried out to determine the properties of used steel. Also, the samples were characterized by microstructure test and XRD analysis to examine the con

In the case where a shallow foundation does not satisfy with design requirements alone, the addition of a pile may be suitable to improve the performance of the foundation design. The lack of in-situ data and the complexity of the issues caused by lagging in the research area of pile foundations are notable. In this study, different types of piles were used under the same geometric conditions to determine the load-settlement relationships with various sandy soil relative densities. The ultimate pile capacity for each selected pile is obtained from a modified California Bearing Ratio (CBR) machine to be suitable for axial pile loading. Based on the results, the values of Qu for close-ended square pile were increased by 15

This study focuses on the modeling of manufactured damper when used in steel buildings. The main aim of the manufactured dampers is to protect the steel buildings from the damaging effects that may result due to earthquakes by introducing an extra damping in addition to the traditional damping.
Only Pure Manufactured Dampers, has been considered in this study. Viscous modeling of damping is generally preferred in structural engineering as it leads to a linear model then it has been used during this study to simulate the behavior of the Pure Manufactured Damper.
After definition of structural parameters of a manufactured damper (its stiffness and its damping) it can be used as a structural element that can be added to a mathematica

Abstract

        The research to have a clear perceptions about the knowledge value added to assess the knowledge resources of the Iraqi private banks, depending on the value added methodology of the proposed defined (Housel & Bell, 2001), which assumes that the  knowledge value added come through synergetic relationship between knowledge resource and information technology, trying to the possibility of mainstream theory and its application in the Iraqi environment and interpretation of results, and on this basis was launched search of a research problem took root synergetic nature of the relationship between knowledge (human)  resource and

With growing global demand for hydrocarbons and decreasing conventional reserves, the gas industry is shifting its focus in the direction of unconventional reservoirs. Tight gas reservoirs have typically been deemed uneconomical due to their low permeability which is understood to be below 0.1mD, requiring advanced drilling techniques and stimulation to enhance hydrocarbons. However, the first step in determining the economic viability of the reservoir is to see how much gas is initially in place. Numerical simulation has been regarded across the industry as the most accurate form of gas estimation, however, is extremely costly and time consuming. The aim of this study is to provide a framework for a simple analytical method to esti

The inhibition ability of the new derivative (quinolin-2-one), namely (1-{[5-(2-Chloro-phenylazo)-2- hydroy-benzylidene]-amino}-4,7-dimethyl -6-nitro- 1H-quinolin-2-one (CPHAQ2O)) towards carbon steel corrosion in (3.5% NaCl) and (0.5M HCl) solutions were evaluated by potentiodynamic polarization at different inhibitor concentrations. Polarization curves showed that the evaluated compound acted as mixed inhibitors, and the adsorption of the evaluated inhibitor obeys the Langmuir adsorption isotherm in both salt and acid solutions. The results revealed that the percentage inhibition efficiency (%IE) in the salty solution (90.55%) is greater than that in the acidic solution (77.62%). The surface changes of the carbon steel and the film per

Background: Osteoporosis is a skeletal defect manifested by a reduction of bone strength as a result of reduced bone mass to the extent that there is a higher risk of fracture even on minor trauma. Hysterectomy in a premenopausal woman is a well known cause of ovarian failure resulting in an increased risk of osteoporosis.

Objective : To clarify bisphosphonate's preventive effect on osteopenia and osteoporosis in premenopausal women after hysterectomy.

Type of the study: Cross –sectional study.

Method:  84 premenopausal females post hysterectomy aged between 40 – 50 years, were enrolled in this randomized controlled double blinded trail a

 Background: The normal decline in systolic blood pressure during recovery phase of treadmill exercise dose not occur in most patients with coronary artery disease, in others recovery values systolic blood pressure may even exceed the peak exercise value. Objectives: Treadmill exercise test parameters indicating the presence and extent of coronary artery disease have traditionally included such as exercise duration, blood pressure and ST-segment response to exercise. The three –minute systolic blood pressure ratio is another important indicator of presence and significance of coronary artery disease is useful and obtainable measure that can be applied in all patients who are undergoing stress testing for evaluation of suspected is