Cadmium oxide (CdO) thin films were deposited using the sequencing ion layer adsorption and reaction (SILAR) method. In this study, the effect of the pH value of an aqueous solution of cadmium acetate at a concentration of 0.2 mol of the cadmium oxide film was determined. The solution source for the cadmium oxide film was cadmium ions and an aqueous ammonia solution. The CdO films were deposited on glass substrates at a temperature of 90 ℃. The cadmium oxide film thickness was determined by the weight difference method at pH values ​​(7.2, 8.2). X-ray diffraction (XRD) and scanning electron microscopy (SEM) showed that the size of the crystals increased with the increase in the solution (pH). While the UV-visible spectra of the fil

The studies on unbonded post-tensioned concrete members strengthened with Carbon Fiber Reinforced Polymers (CFRPs) are limited and the effect of strengthening on the strain of unbonded pre-stressed steel is not well characterized. Estimating the flexural capacity of unbound post-tensioned members using the design methodology specified in the design guidelines for FRP strengthening techniques of bonded post-tensioned members does not provide a reliable evaluation. This study investigates the behavior of unbonded post-tensioned concrete members with partial strand damage (14.3% and 28.6% damage) and strengthened with CFRP laminates using a near-surface mounted technique with and without U-wrap anchorages. The experimental results show

The aim of the research is to measure the length between the variable the efficiency of the tax examiner with its dimensions represented by (scientific questions, practical process (experience), training and development, impartiality and independence, ethics of the profession) and the approved variable discovering the artificial adaptation of profits, and the degree of arrangement of those dimensions its importance and priority, and the research problem has been identified  In a main question that is there any effect of copying the images of the image examiner in discovering the adaptation, the financial statements and reports of the companies (X, Y) and the banks (A, B) were relied on in the interpretation of the results, t

This paper describes the first occurrence of the monogenetic trematode Silurodiscoides
mediacanthus (Achmerow, 1952) in Iraq from gills of the cyprinid fish Barbus luteus from
Diyala river, Diyala province, Iraq. The description and measurements of this parasite were
given. In addition, key for the identification of the three species of Silurodiscoides, so far
recorded from freshwater fishes of Iraq, is included.

In this work, varying compositions of SiO₂ micro filler were added
with the Polyvinyl Chloride (PVC) and samples have been prepared
using film casting technique. The results have been analyzed and
compared for PVC samples with (1 wt%, 3 wt%, 5 wt% and 10 wt%)
SiO2 micro filler. Mechanical characteristics such as tensile strength,
elongation at break and Young`s modulus were measured for all the
samples, where the tensile strength was increased from 8.39 Mpa for
purified PVC to 16 Mpa for 3% SiO₂/PVC composite. Also, thermal
conductivity measurement values illustrated that composite materials
have a good thermal insulation at 10 wt. %, thermal conductivity was
decreased from 0.1684 W/m.

Background: Poly (methylmethacrylate) is the most widely used material in denture fabrication. The characteristics of acrylic resin which support microorganism development can threaten the oral health of denture users. This study was assigned to prepareand incorporate Ag-Zn zeolite powder into heat cured denture base material as antimicrobial material and to investigate its effect on some properties of heat cured acrylic denture base materials. Materials and methods: Sliver –zinc zeolite was prepared by ion exchange method and characterized then incorporated into poly (methylmethacrylate) powder in0.5% by weight. Specimens were constructed and divided into 6 groups according to the using tests; each group was subdivided into 2 groups

Background: The geriatric patients wearing removable partial dentures are increasing in proportion. At the same time, the root caries prevalence accompanied by gingival recession is increasing. A variety of vehicles can deliver fluoride into the oral cavity, including fluoride mouth-rinse, fluoride dentifrice, topical fluoride, and fluoride-releasing restorative materials, all of which effectively prevent root caries and suppress recurrent caries. This study aimed to evaluate the effect of sodium fluoride addition on some mechanical properties of heat cure acrylic denture base material. Material and method: A total of 90 samples were prepared in this study, then divided into three main groups according to the type of test used (hardness, te

Labrotary experiment was conducted to study the effect of different levels of nematode population densities of Meloidogyne spp on seed germination percentage and seedling characteristics of Vigna sinensis, Ahelmoschus esculentus, Cicer arietinum, Helianthus annuus and Rap-hanus sativus. Four different levels of nematode populat-ion densities ranged from 1 to 4 prepared from radish in-fected roots and used as inoculating agent to infect all seed types in the experiment Seed germination percentage of Vigna sinensis and Ablemoschus eseulentus were highly reduced (at 0.01 level of significance) with increased nematode population level from 1 to 4. Seedling length of the remaining seed types were significantly reduced (at 0.01 level of signif