Background: The present study was carried out to compare shear bond strength of sapphire bracket bonded to zirconium surface after using different methods of surface conditioning and assessment of the adhesive remnant index. Materials and methods: The sample composed of 40 zirconium specimens divided into four groups; the first group was the control, the second group was conditioned by sandblast with aluminum oxide particle 50 μm, the third and fourth group was treated by (Nd: YAG) laser (1064nm)(0.888 Watt for 5 seconds) for the 1st laser group and (0.444 Watt for 10 seconds) for the 2nd laser group. All samples were coated by z-prime plus primer. A central incisor sapphire bracket was bonded to all samples with light cure adhesive res

The current research aims to determine the relationship of the impact of the components of the financing structure, especially financing through debts, as well as the earnings per share in the value of the shares of companies listed in the Iraq Stock Exchange. The research sample and identifying the strength of the combined effect of the ratio of financing through debt and earnings per share in maximizing The market value of the firm and the real value, as well as the variation between these relationships according to model of the real value of the companies and the market value of the research sample companies. The research community is represented by the Iraq Stock Exchange, while a conditional deliberate sample

The research is conducted on target of investigating the role of growth strategy via diversification in value maximization of a firm in terms of controversies literatures had witnessed. Using a descriptive approach for analyzing and verifying the harmony of variables of research and their conceptualized logic , it could be reached to many conclusions agreed in their essence upon that the related diversification has the major role in value maximization of a firm and the wealth of its owners .                       

  The relationship between the vision of the scenario and the director is represented in the second search for new mechanisms and possibilities that possess the direct effect and synonyms of the vision of the scenario, so he works on investing them in achieving his ideas and visions with more effectiveness and flexibility to achieve creative potentials, without resorting to the installations and expressive structures themselves that have exhausted their meaning, and lost their luster due to Its prevalence and familiarity on the one hand, and its activation on the other hand to achieve modernity at the level of aromas, after the director takes a method or approach that has privacy and exclusivity, and based on the foregoing, getting

Aim: surface modification of titanium using fiber laser 1064 nm to enhance the bond strength to resin cement. Material and Methods: thirty titanium discs of 0.6 cm x 0.3 cm (diameter and thickness respectively) were categorized after preparation into three groups (n=10) as follows: control group with no surface treatment and two test groups were treated with fiber laser after estimation the appropriate parameters in the pilot study which are 81 ns pulse duration, 30,000 Hz frequency, 50 µm spot size and 10,000 mm/s scanning speed and different average power values (10 W and 20 W) depending on the tested group. Titanium discs surface characterization was performed by scanning electron microscope (SEM), a

The importance of the current research lies in the importance of teaching competencies and the ability of the teacher to deal and success in his educational career. The research aimed to identify the degree of teaching competencies according to Hermann model of physical education teachers in Baghdad governorate. The descriptive method using the survey method was used on a randomly selected sample of 462 teachers and 314 school principals. After the completion of the survey, the Hermann scale forms were distributed to the teachers. The forms of the teaching competency scale were distributed to their school principals as the direct supervisors of the teachers' evaluation. After completing the survey, the results of each scale were classified

This work deals with thermal cracking of three samples of extract lubricating oil produced as a by-product from furfural extraction process of lubricating oil base stock in AL-Dura refinery. The thermal cracking processes were carried out at a temperature range of 325-400 ºC and atmospheric pressure by batch laboratory reactor. The distillation of cracking liquid products was achieved by general ASTM distillation (ASTM D -86) for separation of gasoline fraction up to 220 ºC from light cycle oil fraction above 220 ºC. The comparison between the conversions at different operating conditions of thermal cracking processes indicates that a high conversion was obtained at 375°C, according to gasoline production. According to gasoline produ

The catalytic cracking of three feeds of extract lubricating oil, that produced as a by-product from the process of furfural extraction of lubricating oil base stock in AL-Dura refinery at different operating condition, were carried out at a fixed bed laboratory reactor. The initial boiling point for these feeds was 140 ºC for sample (1), 86 ºC for sample (2) and 80 ºC for sample (3). The catalytic cracking processes were carried out at temperature range 325-400 ºC and initially at atmospheric pressure after 30 minutes over 9.88 % HY-zeolite catalyst load. The comparison between the conversion at different operating conditions of catalytic cracking processes indicates that a high yield was obtained at 375°C, according to gasoline pr