Effect of Chlorococcum humicola alcoholic algae extract was studied on the growth of, Pseudomonas aeruginosa, and Klebsiella pneumonia, which were isolated from contaminated water. The extract of Ch. humicola showed a high efficiency in reducing the numbers of the two types of bacteria. . The removal rate of K. pneumonia were 0.0, 48.4 and 57.0, The removal rate of P. aeruginosa were 63.1, 79.8 and 82.9% after24,48, 72 h respectively. The results improved that the K. pneumonia is more sensitive than P. aeruginosa for algae extract concentrations used in study ,and the beast effective time is 24h for the two bacterial species The aim of the study was to eliminate microorganisms using the Alcoholic algae extract. Especially P. aeruginosa and

This study comprised three traverses extending parallel through the Northern, Central and Southern Mahmudiya districts, and perpendicular to the course of the Euphrates River. They were identified to collect (15) soil samples and some water samples as distributed within the land cover classes of the study area. Those classes were determined by visual interpretation and supervised classification for Landsat (TM) images obtained in August/2007. The digital classification was based on Maximum Likelihood method using six spectral bands excluding the thermal band. Chemical and physical laboratory analysis for the soil characteristics was performed to determine the types of land degradation in the study area.
The results showed that the hig

The parasite E.histolytica was first isolated from a stool sample, and then cultivated and maintained in vitro using Locke-egg medium (LEM) and Liver infusion agar medium (LIAM) . Then, the effect of some types of erythrocytes (human and sheep), on the growth and activity of the parasite in the two culture media was investigated. The parasite was able to ingest and lysis erythrocytes of human and sheep that were supplemented to the culture media and such manipulation was able to augment the reproduction rate of the cultivated E. histolytica, however, such consequence was media- and concentration-dependent. The reproduction rate was significantly increased (66.0, 57.5 and 58.6%, respectively) in LEM medium containing human erythrocytes ty

Background: Bilosomes are lipid vesicles that exhibit flexibility and deformability. They consist of phospholipids and amphiphilic bile salts. Compared to the normal vesicular systems such as liposomes and niosomes, bilosomes provide several notable advantages, including simplified manufacturing, cost-effectiveness, and enhanced stability.

Aim: The main objective of the present work was to evaluate the effect of different bile salts on the physical properties that include entrapment efficiency, vesicle size, and polydispersity index(PDI). In addition, in vitro drug release for nisoldipine (NSD) loaded bilosomes was evaluated.

The effects of shot peening treatment (SPT) were studied at (10,20, and 30) minutes on the rotating bending fatigue behavior and the behavior of the alloy steel DIN 41Cr4 vibrations. The hardness test, tensile test, constant amplitude fatigue tests, and the vibration measurements were performed on samples with and without cracks at room temperature (RT), also, the fracture surface was examined and analyzed by a Scanning Electron Microscope (SEM). The results of the investigations, for example, Stress to Number of cycles to failure (S-N) curves, fatigue strength improvement factor of 5% to 10%, the decreasing percentage of maximum Fast Fourier Transform (FFT) acceleration of the shot-peened condition were compared to untr

Cooling towers is one of the most important unit in industry, they are used to dispose heat from cooling media used in the integrated units. The choice of the cooling media plays recently an important rule due to fresh-water scarcity. The use of saline as a cooling media become of growing interest, but the corrosion problem has to be taken in consideration. In this study the simultaneous effect of cooling tower operation parameters on the corrosion rate of mild-steel is considered. The role of NaCl content is found to be pronounced more than the working solution temperature and flowrate. The corrosion of mild-steel in these studied factors had shown an interesting result especially with the NaCl% content. Firstly, there was an increase in t

The aim of this research is to calculate mass transfer coefficient, k_d, during cathodic protection of low carbon steel in neutral seawater (3.5% W/V NaCl in distilled water with pH = 7). Two types of cathodic protection were used:

First: Sacrificial anode cathodic protection (SACP) were a pipeline of steel carrying seawater  using zinc as a sacrificial anode and with variable temperatures ranged (0 – 45^oC) and volumetric flow rate ranged (5 – 900 lit/hr). It was found that the k_d increases with increasing temperature and volumetric flow rate of seawater, where k_d ranged (0.24×10^-6 – 41.6×10^-6 m/s).

Second: Impressed current cathodic pr

The inhibitive power of Polyvinyl Alcohol (PVA) was investigated toward the corrosion of carbon steel in 0.2N H₂SO₄ solution in the temperature range of 30-60˚C and PVA concentration range of 150-2000 ppm.

   The corrosion rate was measured using both the weight loss and the electrochemical techniques. The weight loss results showed that PVA could serve as a corrosion inhibitor but its inhibition power was found to be low for the corrosion of carbon steel in the acidic media. Electrochemical analysis of the corrosion process of carbon steel in an electrochemical corrosion cell was investigated using 3-Electrode corrosion cell. Polarization technique was used for carbon steel corrosion in 0.2N H

The inhibitor property of curcuma longa L. extract in different concentrations of simulated refinery wastewater (0.05% - 2% wt) and at various temperatures (30, 35 and 40 ˚C) was investigated using weight loss method. The results showed that the presence of about 1.2 % (v/v) of curcuma extract gave about 84% inhibition indicating its effectiveness on mild steel corrosion in simulated refinery wastewater, besides the adsorption process on the mild steal surface obeyed the Langmuir adsorption isotherm.