Through an experimental program of eighteen specimens presented in this paper, the bond strength between reinforcing bar and rubberized concrete was produced by adding waste tire rubber instead of natural aggregate. The fine and coarse aggregate was replaced in 0%, 25%, and 50% with the small pieces of a waste tire. Natural aggregate replacement ratio, rebar size, embedded rebar length, the rebar yield stress of rebar, cover, and concrete compressive strength were studied in this investigation. Ultimate bond stress, bond stress-slip response, and failure modes were presented. The experimental results reported that a reduction of 19% in bond strength was noticed in 50% replaced rubberized concrete compared with convention

Many researchers tried to prevent or reduce moisture damage and its sensitivity to temperature to improving the performance of hot mix asphalt because it is decreasing the functional and structural life of fixable pavement due to the moisture damage had exposed to it.

The main objective of this study is to inspect the effect of (fly ash “3%, 6%, 12%”, hydrated lime”5%, 10%, 20%” and silica fumes”1%, 2%, 4%) referring to previous research by the net weight asphalt cement as a modified material on the moisture and temperature sensitivity of hot mix asphalt. This was done using asphalt from AL-Nasiria refinery with penetration grade 40-50, nominal maximum size (12.5) mm (surface course) of aggregate and on

Background: White spot lesion considered as irreversible tooth demineralization presenting challenge to orthodontists during treatment schedules, fluoride was the most successfully used measure to overcome this challenge. Materials and method: A total of forty sound human permanent premolars were used in the present study and categorized into four groups, in one group the teeth were bonded with stainless steel brackets using Resin-modified glass ionomer cement (RMGIC) and the other three groups the teeth were bonded with light cured composite Resilience® (Ortho technology Co., USA). Group A; Acidulated phosphate fluoride (APF) topical gel (Mfg by DEEPAK PRODUCTS, INC, USA), fluoride ion 1.23% applied on examine area for four minute. Gro

Background: The Streptococcus genus are the predominant bacteria in the mouth and the Streptococcus sanguinis is one of them which performing a primary function for expansion of dental biofilm. Gingival and periodontal disorders are caused by dental biofilm, today, there is a necessity to discover naturally presenting antibacterial compounds from herbs with less side effects as a substitutive to the commonly handled chlorohexidine. Thus, the purpose of this study was to assess the antibacterial activity of thymus vulgaris oil on Streptococcus sanguinis bacteria In vitro. Materials and Methods: Human supragingival plaque samples were taken from 10 subjects, then morphological and microscopical examination, bioch

Background: To evaluate the effect of antierosive agents (10% Nano-Hydroxyapatite (NHA), 10% Casein Phophopeptide-Amorphous Calcium Phosphate (CPP-ACP), and combination of 10% NHA and 10% CPP-ACP) on loss of minerals from enamel surface of permanent teeth treated with antierosive agents when exposed to an acidic beverage and investigate the morphological changes of treated enamel surface after demineralization with cola based beverage under Scanning Electron Microscope (SEM). Materials and Methods: Sixty maxillary first premolars were randomly divided into four groups, 15 teeth for each group. Group I treated with 10% NHA, Group II treated with 10% CPP-ACP, Group III treated with 10% NHA and 10% CPP-ACP, and Group IV did not treat with any

Background: The aim of this study was to evaluate the push-out bond strength of four different obturation materials to intraradicular dentin and to determine the failure mode. Materials and method: forty straight palatal roots of the maxillary first molars teeth were used in this study, the roots were instrumented using crown down technique and rotary EndoSequence system, the roots were randomly divided into four groups according to the materials used for obturation (n=10).Group (1): AH Plus sealer and gutta-percha. Group (2): Activ GP glass ionomer sealer and Activ GP gutta-percha (Activ GP system). Group (3): Bioceramic sealer and Bioceramic gutta-percha. Group (4): GuttaFlow2 sealer and gutta-percha. For all groups single cone obturatio

Background: The aim of this study was to determine phototoxic effect of visible blue light on anaerobic periodontal pathogens namely Aggregatibacter actinomycetemcomitans and Porphyromonas gingivalis. Materials and methods: Strains of Aggregatibacter actinomycetemcomitans and Porphyromonas gingivalis were isolated from pockets of systemically healthy patients aged between 35-55 years old with pocket depths of 5-6 mm, the bacteria cultured on special blood Agar plates solid media, then subjected to visible blue light emitted from commercially available light cure devise (LED curing light); that emits blue light (400-500nm) of 1000mw energy at different periods of time exposures, then the CFU of each plate was measured by direct colony count