Because of the quick growth of electrical instruments used in noxious gas detection, the importance of gas sensors has increased. X-ray diffraction (XRD) can be used to examine the crystal phase structure of sensing materials, which affects the properties of gas sensing. This contributes to the study of the effect of electrochemical synthesis of titanium dioxide (TiO₂) materials with various crystal phase shapes, such as rutile TiO₂ (R-TiO₂NTs) and anatase TiO₂ (A-TiO₂NTs). In this work, we have studied the effect of voltage on preparing TiO₂ nanotube arrays via the anodization technique for gas sensor applications. The results acquired from XRD, energy dispersion spectro

Pt (IV) complexes were synthesized from 4-Aminoantipyrine (4-AAP) as a primary ligand, and sodium pyrophosphate as a secondary ligand using metal: ligand in (1:1) mole ratio with molecular formula [Pt (4-AAP)Cl4],[Pt (4-AAP)(Pyph)Cl2]. These complexes were characterized by elemental microanalysis (C.H.N), (A.A), [I.R, (U.V–Vis), mass spectroscopy], along with molar conductivity, chloride contents and melting point measurements. The ligands (4-AAP) and (Pyph) gave octahedral geometry with Pt (IV) rapid, simple, sensitive and validated spectrophotometric method has been described for the determination of platinum (IV) using 4-aminoantipyrine. The complex product was quantitatively measured at 385nm and the reaction conditions were studie

This work presents a design for a pressure swing adsorption process (PSA) to separate oxygen from air with approximately 95% purity, suitable for different numbers of columns and arrangements. The product refill PSA process was found to perform 33% better (weight of zeolite required or productivity) than the pressure equalization process. The design is based on the adsorption equilibrium of a binary mixture of O₂ and N₂ for two of the most commonly used adsorbents, 5A & 13X, and extension from a single column approach. Zeolite 13X was found to perform 6% better than zeolite 5A. The most effective variables were determined to be the adsorption step time and the operational pressure. Increasing the adsorption step

The present experimental work is conducted to examine the influence of adding Alumina (Al₂O₃) nanoparticles and Titanium oxide (TiO₂) nanoparticles each alone to diesel fuel on the characteristic of the emissions. The size of both Alumina and Titanium oxide nanoparticles which have been added to diesel fuel to obtain nano-fuel is about 20 nm and 25 nm respectively. Three doses of (Al₂O₃) and (TiO₂) were prepared (25, 50, and 100) ppm. The nanoparticles mixed with gas oil fuel by mechanical homogenous (manual electrical mixer) and ultrasonic processor. The study reveals that the adding of Aluminum oxide (Al₂O₃) and Titanium oxide (TiO₂) to g

In this work, silver nanoparticles (AgNPs) were biosynthesized from leaves of Ziziphus mauritiana Lam. jujube plant in Iraq and tested against fungal pathogens. Extract of leaves of Z. mauritiana mixed with 10-3 M AgNO3exposed to slight sunlight for 3 days. Characterization of AgNPs was done using UV-visible spectroscopy, SPM (scanning probe microscopy) and atomic force microscopy (AFM). The change of solution color from pale brown to dark brown and the exhibited maximum peak at 445 nm accepted as an indicator to biosynthesized AgNPs. Aqueous extract of Ziziphus mauritiana is considered as biological reduced and stabilized agent for Ag+ to Ag0. AFM showed the formation of irregular shapes of AgNPs. The biosynthesized silver nanoparticles ha

Nanoparticles of Pb_1-xCd_xS within the composition of 0≤x≤1 were prepared from the reaction of aqueous solution of cadmium acetate, lead acetate, thiourea, and NaOH by chemical co-precipitation. The prepared samples were characterized by UV-Vis spectroscopy(in the range 300-1100nm) to study the optical properties, AFM and SEM to check the surface morphology(Roughness average and shape) and the particle size. XRD technique was used to determine the crystalline structure, XRD technique was used to determine the purity of the phase and the crystalline structure, The crystalline size average of the nanoparticles have been found to be 20.7, 15.48, 11.9, 11.8, and 13.65 nm for PbS, Pb_0.75Cd_0.25S,