Two new nonsymmetrical mesogenic homologous series of terminal substituent ether (series [Vn]) and carboxy (series [VIn]) incorporating azobenzene and 1,3,4-oxadiazole group were synthesized. Both series have been All compounds thus isolated were purified and characterized by elemental analysis, Fourier Transform Infrared Spectroscopy, 1H NMR, along with thermal analysis and texture observation using Differential Scanning Calorimetry (DSC) and Polarizing Optical Microscopy (POM), respectively. All compounds of the first series exhibited liquid crystalline properties. The homologues [V1]-[V3] display a nematic mesophase, the compounds [V4]-[V7] exhibit a dimorphism behavior, nematic (N) and smectic A (SmA) mesophases, the compounds [V8] and

The compounds 3-[4̄-(4˭-methoxybenzoyloxy) benzylideneamino]-2-thioxo-imidazolidine-4-one(3)aand 4-(1-(5-oxo- 2-thioxoimidazolidin-1-ylimino)ethyl)phenyl acetate(3)b were prepared from the reaction of aromatic aldehyde or ketone(1)a,bwith thiosemicarbazide to give aryl thiosemicarbazones(2)a,b ,followed by cyclization with ethylchloroacetate in the presence of fused sodium acetate. Treatment the compounds(3)a,bwith 4- hydroxybenzenediazoniumchloride yielded the correspondings4-((4-((4-hydroxyphenyl)diazenyl)-5-oxo-2- thioxoimidazolidin-1-ylimino)methyl)phenyl 4-methoxybenzoate(4)aand4-(1-(4-((4-hydroxyphenyl)diazenyl)-5-oxo-2- thioxoimidazolidin-1-ylimino)ethyl)phenyl acetate(4)b.The new 2-thioxo-imidazolidin-4-one with esters (5-7)a,b sy

The compounds 3-[4̄-(4˭-methoxybenzoyloxy) benzylideneamino]-2-thioxo-imidazolidine-4-one(3)aand 4-(1-(5-oxo- 2-thioxoimidazolidin-1-ylimino)ethyl)phenyl acetate(3)b were prepared from the reaction of aromatic aldehyde or ketone(1)a,bwith thiosemicarbazide to give aryl thiosemicarbazones(2)a,b ,followed by cyclization with ethylchloroacetate in the presence of fused sodium acetate. Treatment the compounds(3)a,bwith 4- hydroxybenzenediazoniumchloride yielded the correspondings4-((4-((4-hydroxyphenyl)diazenyl)-5-oxo-2- thioxoimidazolidin-1-ylimino)methyl)phenyl 4-methoxybenzoate(4)aand4-(1-(4-((4-hydroxyphenyl)diazenyl)-5-oxo-2- thioxoimidazolidin-1-ylimino)ethyl)phenyl acetate(4)b.The new 2-thioxo-imidazolidin-4-one with esters (5-7)a,b sy

Abstract

In this manuscript, a simple new method for the green synthesis of platinum nanoparticles (Pt NPs) utilizing F. carica Fig extract as reducing agent for antimicrobial activities was reported. Simultaneously, the microstructural and morphological features of the synthesized Pt NPs were thoroughly investigated. In particular, the attained Pt NPs exhibited spherical shape with diameter range of 5-30 nm and root mean square of 9.48 nm using Transmission Electron Microscopy (TEM) and Atomic Force Microscopy (AFM), respectively. Additionally, the final product (Pt NPs) was screened as antifungal and antibacterial agent against Candida and Aspergillus species as well as Gram-positive Staphyllococcus aureus and G

In this search, Ep/SiO2 at (3, 6, 9, 12 %) composites is prepared by hand Lay-up method, to measure the change in the thermal conductivity and Impact Strength of epoxy resin before and after immersion in H2SO4 Solution with a 0.3N for 10 days. The results before immersion decreases with the increase of the weight ratios of the reinforcement material (SiO2), It changed from (82.6×10-2 to 38.7×10-2 W/m.°C) with change weight ratios from (3 to 12) % respectively, but after immersion time in the chemical solution where it was (65.6×10-2 W/m.°C) at the weight ratios (6 %) and became (46.6 × 10-2 W/m.°C) after immersion in sulfuric acid. The results of the Impact strength decreased by increasing the percentage weight ratio, it changed f

Laser etching may be an alternative to acid etching of enamel and dentin. Several characteristics of irradiated dental hard tissues have been considered advantageous, microscopically rough surfaces without demineralization, open dentinal tubules without smear layer production and dentin surface sterilization. The aim of this study is to determine and compare histology the microleakage in class V cavity restored with a light cured composite after conditioning the samples(tooth surface) with 1-acid etching, 2-Q-switched Nd:YAG Laser etching and finally 3- acid and laser etching. Materials and methods: Twenty four non carious human extracted teeth were used in this study. The samples were equally grouped into four groups of six teeth each.

Steps were taken to obtain the Kojic acid crystals from local fungal isolation A. flavus WJF81 by separating the fermentation products from the fungus mycelium from the production plant at the centrifuge at a speed of 5000 cycles for 10 minutes. The extraction was followed by ethyl acetate then supernatant concentrate by using rotary evaporator, and dried with heat oven 37ºC. Long, yellowish, pristine acid crystals were obtained that examined the optical microscope with a magnification force of 10x and 40x. The melting point of kojic acid was determined between 152.9-153.5 °C Results of the diagnosis of Kojic acid by applying High pressure liquid chromatography HPLC technique showed that the acid was at one peak, which was close to the