The study was conducted to determine the effect of of cumin (Cuminum cyminum) and ginger (Zingiber officinale) powder on performance in Japanese quails. 630 bird (7 birds for each treatment) nine weeks of age were used. Experiment was continued for 12 weeks divided to six periods and the birds distributed randomly on nine combinations of cumin and ginger, three levels of each plant powder namely, 0, 0.5 and 1%. T1 (Control) contain the slandered diet (0% of cumin and 0% of ginger), T2: (0% of cumin and 0.5% of ginger), T3: (0% of cumin and 1% of ginger), T4: (0.5% of cumin and 0% of ginger), T5: (0.5% of cumin and 0.5% of ginger), T6: (0.5% of cumin and 1% of ginger), T7: (1% of cumin and 0% of ginger), T8: (1% of cumin and 0.5% of ginger),

Background: The cells of periodontium contain many intracellular enzymes like (alkaline phosphatase ALP) that are released outside into the saliva and gingival crevicular fluid (GCF) after destruction of periodontal tissue. The aim of study was to determine the activity of this enzyme in saliva and its relation to the salivary flow rate, PH and clinical periodontal parameters in patients with chronic periodontitis. Subject, Materials and methods: Sample population consist of 75 individuals ;divided into four groups , the first group (15):control subject, the second group (20):mild chronic periodontitis, the third group(20) moderate chronic periodontitis and the fourth group (20) sever chronic periodontitis, Measurements of plaque index (PL

In this study, the upgrading of Iraqi heavy crude oil was achieved utilizing the solvent deasphalting approach (SDA) and enhanced solvent deasphalting (e-SDA) by adding Nanosilica (NS). The NS was synthesized from local sand. The XRD result, referred to as the amorphous phase, has a wide peak at 2Θ= (22 - 23º) The inclusion of hydrogen-bonded silanol groups (Si–O–H) and siloxane groups (Si–O–Si) in the FTIR spectra. The SDA process was handled using n-pentane solvent at various solvent to oil ratios (SOR) (4-16/1ml/g), room and reflux temperature, and 0.5 h mixing time. In the e-SDA process, various fractions of the NS (1–7 wt.%) have been utilized with 61 nm particle size and 560.86 m²/g surface area in the presence of

Copper Zinc Sulphide (Cu0.5Zn0.5S) alloy and thin films were fabricated in a vacuum. Nano crystallized (CZS) film with thick 450±20 nm was deposit at substrates glasses using thermal evaporation technique below ~ 2 × 10− 5 mbar vacuum to investigated the films structural, morphological and optical properties depended on annealing temperatures ( as-deposited, 423, 523 and 623) K for one hour. The influences annealed temperature on structurally besides morphologically characteristics on these films were investigated using XRD and AFM respectively. XRD confirms the formation a mixed hexagonal phase of CuS-ZnS in (102) direction with polycrystalline in nature having very fine crystallites size varying from (5.5-13.09) nm. AFM analys

In this study, the upgrading of Iraqi heavy crude oil was achieved utilizing the solvent deasphalting approach (SDA) and enhanced solvent deasphalting (e-SDA) by adding Nanosilica (NS). The NS was synthesized from local sand. The XRD result, referred to as the amorphous phase, has a wide peak at 2Θ= (22 - 23º) The inclusion of hydrogen-bonded silanol groups (Si–O–H) and siloxane groups (Si–O–Si) in the FTIR spectra. The SDA process was handled using n-pentane solvent at various solvent to oil ratios (SOR) (4-16/1ml/g), room and reflux temperature, and 0.5 h mixing time. In the e-SDA process, various fractions of the NS (1–7 wt.%) have been utilized with 61 nm particle size and 560.86 m²/g surface area in the presence of 12 m

The influence of fiber orientation and water absorption on fatigue crack growth resistance for cold cure acrylic (PMMA) reinforced by chopped and woven -glass-fibers were investigated. A weight of 2 g for chopped fibers and the same weight for woven -glass-fibers (one layer) were used to prepare samples. Some of these samples would storage in dry condition; the others were immersed in water for 15 days. Fatigue test was carried out. The results shows that, for PMMA, the initial bending stress for dry specimen was 3.392 N/cm2 and the number of cycles were 1364, the initial bending stress for wet samples was 4.20 N/cm2, and the number of cycles was 2411. The samples would cut in two pieces because of the cracks would propagated fast during