In this research, a novel thin film Si-GO10 and nanopowders Si-GO30 of silica-graphene oxide (GO) composite were prepared via the sol–gel method and deposited on glass substrates using spray pyrolysis. X-ray diffraction (XRD) results showed a relatively strong peak in the graphite layer that corresponds to the (002) plane. Transmission electron microscope (TEM) images showed that SiO2 nanoparticles were randomly distributed on the surface of GO plates, and the particle size in these nanopowders was below 50 nm. Field emission scanning electron microscopy (FESEM) analysis demonstrated that silica nanoparticles on the surface of GO plates exhibited almost spherical and rod-like nanoparticle shape, which in turn confirmed the formation of Si

In this research, a novel thin film Si-GO10 and nanopowders Si-GO30 of silica-graphene oxide (GO) composite were prepared via the sol–gel method and deposited on glass substrates using spray pyrolysis. X-ray diffraction (XRD) results showed a relatively strong peak in the graphite layer that corresponds to the (002) plane. Transmission electron microscope (TEM) images showed that SiO₂ nanoparticles were randomly distributed on the surface of GO plates, and the particle size in these nanopowders was below 50 nm. Field emission scanning electron microscopy (FESEM) analysis demonstrated that silica nanoparticles on the surface of GO plates exhibited almost spherical and rod-like nanoparticle shape, which in tur

A graphene-based supercapacitors (SC) were manufactured. The main objective of this research was to use as possible as environmentally, clean and natural materials for the SC electrodes, electrolytes and the separators. The SC consisted of a multi-layer graphene (MLG); as the electrode material, prepared by mixing graphene powder with water/acetone mixture, then the solution deposited on metal foils (aluminum and copper) by chemical spray technique, which is a simple and inexpensive technique to prepare the MLG films. The spraying time was (2 and 4 minutes) for making two MLG films with different thicknesses. The electrolytes were used is (lemon juice, table salt dissolved in water, and distillated water). The separators were a commercia

In this study, graphene oxide (GO) and reduced graphene oxide were synthesized by pulsed Nd:YAG laser with a fundamental wavelength (1064 nm) focused on the pure graphite target which was immersed in distilled water. Different pulse energies were applied in two cases; with and without magnetic field. The synthesized GO and rGO nanoparticles were characterized by UV-visible spectroscopy, X-ray diffraction (XRD), Fourier transform infrared (FTIR) spectroscopy and atomic force microscopy (AFM) with and without magnetic field. The data show the presence of a magnetic field which illustrated increasing oxygen functional groups of GO. This caused a change in the morphology of the surface of GO, increasing crystallite size from 12.19 nm to 71.2

A green and low-cost method was used to prepare graphene oxide (GO) and reduced graphene oxide (rGO) by chemical exfoliation of graphite powder by modified Hummers method, followed by reduction using ascorbic acid. X-ray diffractometry (XRD) and field emission scanning electron microscopy (FE-SEM) were used to analyze the structure and morphology of the synthesized materials. Fourier transform infrared spectroscopy (FTIR) and ultraviolet-visible spectroscopy were used to identify the formation of the GO and rGO

In this research tri metal oxides were fabricated by simple chemical spray pyrolysis technique from (Sn(NO₃)₂.20 H₂O, Zn(NO₃)₂.6 H₂O, Cd(NO₃)₂.4 H₂O) salts at concentration 0.1M with mixing weight ratio 50:50 were fabricated on silicon substrate n-type (111). (with & without the presence of grooves by the following diemensions (20μm width, 7.5μm depth) with thickness was about ( 0.1 ±0.05 µm) using water soluble as precursors at a substrate temperature 550 ºC±5, with spray distance (15 cm) and their gas sensing properties toward H₂S gas at different concentrations (10,50,100,500 ppmv) in air were investigated at room te

A simple, inexpensive, and home–built electrostatic spray deposition (ESD) system with stable cone-jet mode was used to obtain nickel oxide (NiO) thin films on glass substrates kept at temperature of 400°C. The primary precursor solution of 0.1 M concentration hydrated nickel chloride dissolved in isopropyl alcohol. The structural, optical and electrical parameters were studied. The optical absorbance spectra for the studied samples showed its maximum around 280 nm. On the other hand, thickness interferometry measurements on the tested samples showed that film thickness was around 400 nm. The optical energy gap of the prepared NiO samples was determined to be 3.75 eV and the maximum value of refractive index was determined to be 2.1 a

      Organic contaminants are used to be found in industrial wastewater treatment procedures, and heavy metal ion removal is difficult. Photo Fenton reaction activity was exploited in this study to decompose organic contaminants using a functional composite hydrogel. Polyacrylonitrile (PAN), Fe₃O₄ particles, and graphene oxide make up the hydrogel (GO). It is made from GO/ Fe₃O₄ and is made using the precipitation technique. GO is made from graphite using the Hummers process. And it has exceptional mechanical strength and Photo-Fenton activity as a result of various breakdown data that were influenced differently, such as H₂O₂ concentration, dye concentration, temper

In this paper, the pure graphene oxide and copper phthalocyanine-tetrasolfonic acid tetrasodium salt were used to prepare thin films by using the spin coating method. These chemical compounds have remarkable optical properties and are chemically used in the development of device sensors by increasing the mixing ratio. Three different mixing ratios were prepared at room temperature and 150^oC annealing temperature for three hours. The spectra of UV-VIS-IR absorption, photoluminescence, and Fourier-transformed infrared (FT-IR) were studied.