The complexes of Schiff base (6-[Hydroxy - benzylidene)-amino]-pyrimidine-2,4-diol ) (L) with Mn(II), Fe(II), Co(II) and Ni(II) were prepared. The Schiff base and complexes have been characterized by FT-IR, ¹H-NMR, UV-Vis, LC-mass spectra, magnetic moment, elemental microanalyses (C.H.N.), chloride containing, atomic absorption and molar conductance.

The Schiff base, metal salts and complexes were also screened for their bioactivity such as antibacterial and antifungal.

A hand lay-up method was used to prepare Epoxy/ metal composites. Epoxy resin (EP) was used as a matrix with metal particles (Al, Cu, and Fe) as fillers.
The preparation method includes preparing square panels of composites with different weight percentage of fillers (10, 20, 30, 40, and 50%). Standard specimens (88mm in diameter) for thermal conductivity tests were prepared to measure thermal conductivity kexp.The result of experimental thermal conductivity kexp, for EP/metal composites show that, kexp increase with increasing weight percentage, For EP/ Al and EP/Cu composites, and it have have maximum values of 0.33 and 0.35 W/m.K, respectively. While kexp for EP/ Fe composite show slight increase with maximum value of 0.186 W/m.K.

EP/ metal composites were prepared as adhesives between two steel rods. Epoxy resin (EP) was used as a matrix with metal as fillers (Al, Cu, Fe,).
The preparation method for tensile adhesion tests includes two steel rods with adhesive composites between the rods to measure adhesion strength Sad and adhesion toughness Gad.
Results of tensile adhesion tests show that EP/ metals composite have maximum strength Sad for certain weight percentage of metals 2.95 and 9MPa at 10% for EP/Al and EP/Cu composite and 8.2MPa at 40% for EP/Fe composites

This study was aimed to assess the impact of vermicompost, glutathione, and their interaction on beetroot (Beta vulgaris L.) growth, yield, and antioxidant traits. The experiment carried out at vegetable field of the College of Agricultural Engineering Sciences - University of Baghdad during fall season 2019. The experiment was conducted using factorial arrangement within Randomized Complete Block Design with two factors and three replicates (3X3X3). Applying vermicompost before cultivation represented the first factor (0, 15, 30 ton.ha-1), which symbolized (V0, V1, V2). Glutathione (0, 75, 150 mg.L-1) which symbolized (G0, G1, G2) represented the second factor. Results showed the superiority of secondary interaction treatment V2G2

    In this research, the study of thermal treating by laser, plasma glow discharge and tubular furnace on Ti-6Al-4V alloy coated with hydroxyapatite by methods of dip coating and electrophoretic deposition .A group of samples was coated by dip coating and another group was coated by electrophoretic deposition. The first group was treated by pulse laser 10 (mJ) as energy for samples from both coating with uniform distributed pulses on every single sample surface, The second thermal treating was made by plasma glow discharge in a locally made system with argon atmosphere, 600 Volt , and 6 cm distance between the electrodes, The third treating was made by tubular furnace in air atmosphere and 400 °C for 1 hour duration. T

The effect of approaching nozzle jet from the deposition surface
on structural, optical and morphology properties of copper oxide thin
films was studied. The film was prepared by homemade fully
computerized CNC spray pyrolysis deposition technique at
preparations speed (3, 4, 5, and 6 mm/sec). The repeated line mode
was used at deposition temperature equal 450 °C whereas the
spraying time was in the range of (15-30 min) according to the
deposition speed. The film exhibit polycrystalline structure with
preferred orientation along (-111), (022) and (011), (002) at a 2θ
value of (35.63o) and (38.8o) respectively. Optical band gaps were
recorded at these speed shows variance in value from (1.53-2.08 eV).
Fi

Piroxicam (PIR) is a nonsteroidal anti-inflammatory drug of oxicam category, used in gout, arthritis, as well as other inflammatory conditions (topically and orally). PIR is practically insoluble in water, therefore the aim is prepare and evaluate piroxicam as liquid self-nanoemulsifying drug delivery system to enhance its dispersibility and stability. The Dispersibilty and Stability study have been conducted in Oil, Surfactant and Co-surfactant for choosing the best materials to dissolve piroxicam. The pseudo ternary phase diagrams have been set at 1:1, 2:1, 3:1 as well as 4:1 ratio of surfactants and co-surfactants, also there are 4 formulations were prepared by using various concentrations of transcutol HP, cremophore EL and triacetin

             The synthesis of nanoparticles (GNPs) from the reduction of HAuCl₄ ^.3H₂O by aluminum metal was obtained in aqueous solution with the use of Arabic gum as a stabilizing agent. The GNPs were characterized by TEM, AFM and Zeta potential spectroscopy. The reduction process was monitored over time by measuring ultraviolet spectra at a range of λ 520-525 nm. Also the color changes from yellow to ruby red, shape and size of GNP was studied by TEM. Shape was spherical and the size of particles was (12-17.5) nm. The best results were obtained at pH 6.

A simple, precise, and sensitive spectrophotometric method has been established for the analysis of doxycycline. The method includes direct charge transfer complexation of doxycycline withp-Bromanil in acetonitrileto form a colored complex. The intensely colored product formed was quantified based on the absorption band at 377 nm under optimum condition. Beer’s law is obeyed in the concentration range of 1–50 μg.mL-1 with molar absorptivity of 1.5725x104 L.mol-1.cm-1, Sandell's sensitivity index (0.0283) μg.cm-2, detection limit of 0.1064 μg.mL-1, quantification limit 0.3224 μg.mL-1 and association constant of the formed complex (0.75x103). The developed method could find application in routine quality control of doxycycline and has

Production and characterization of methionine γ- lyase from Pseudomonas putida and its effect on cancer cell lines