Evaluation of marginal gap at the composite/enamel interface in Class II composite resin restoration by SEM after thermal and mechanical load cycling (An in vitro comparative study)

Background: This study compared in vitro the marginal adaptation of three different, low shrink, direct posterior composites Filtekâ„¢ P60 (packable composite), Filtekâ„¢ P90 (Silorane-based composite) and Sonic fillâ„¢ (nanohybrid composite) at three different composite/enamel interface regions (occlusal, proximal and gingival regions) of a standardized Class II MO cavity after thermal changes and mechanical load cycling by scanning electron microscopy. Materials and methods:Thirty six sound human maxillary first premolars of approximately comparable sizes were divided into three main groups of (12 teeth) in each according to the type of restorative material that was used: group (A) the teeth were restored with Filtekâ„¢ P6

... Show More
View Publication Preview PDF
Publication Date
Thu Nov 21 2024
A study to compare the cleaning efficiency of different irrigation systems for macro debris removal in instrumented canals (An in vitro study)

Background: Irrigation of the canal system permits removal of residual tissue in the canal anatomy that cannot be reached by instrumentation of the main canals so the aim of this study was to compare and evaluate the efficiency of conventional irrigation system, endoactivator sonic irrigation system,P5 Newtron Satelec passive ultrasonic irrigation and Endovac irrigation system in removing of dentin debris at three levels of root canals and to compare the percentage of dentin debris among the three levels for each irrigation system. Materials and methods: Forty extracted premolars with approximately straight single root canals were randomly distributed into 4 tested groups of 10 teeth each. All canals were prepared with Protaper Universal ha

... Show More
View Publication Preview PDF
Publication Date
Sun Jan 01 2006
Journal Name
J Bagh College Of Dentistry
Assessment of diametral tensile strength and microhardness of Glass ionomer reinforced by different amounts of Hydroxyapatite

Back ground: Glass ionomer materials lack resistance to wear and pressure and are susceptible to moisture during the initial stages of setting and dehydration. So this study was done to assess diametral tensile strength and microhardness of glass ionomer reinforced by different amounts of hydroxyapatite. Materials and methods: In this study a hydroxyapatite material was added to glass monomer cement at different ratios: 10%, 15%, 20%, 25% and 30% (by weight). The diametral tensile strength test described by the British standard specification for zinc polycarboxylate cement was used in this study and the microhardness test was performed using Vickers microhardness testing machine and the microhardness values were calculated and statistical c

... Show More
View Publication Preview PDF
Publication Date
Tue Jan 01 2008
Journal Name
J Bagh College Of Dentistry
Assessment of consistency and compressive strength of glass ionomer reinforced by different amount of hydroxyapatite

Background: Glass ionomers have good biocompatibility and the ability to adhere to both enamel and dentin. However, they have certain demerits, mainly low tensile and compressive strengths. Therefore, this study was done to assess consistency and compressive strength of glass ionomer reinforced by different amount of hydroxyapatite. Materials and Methods: In this study hydroxyapatite materials were added to glass ionomer cement at different ratios, 10%, 15%, 20%, 25% and 30% (by weight). The standard consistency test described in America dental association (ADA) specification No. 8 was used, so that all new base materials could be conveniently mixed and the results would be of comparable value and the compressive strength test described by

... Show More
View Publication Preview PDF
Publication Date
Mon Mar 13 2017
Comparative Study of The Amount of Apically Extrusion Of Debris During Root Canal Preparation Using Wave Oneâ„¢, Trushape 3Dâ„¢, Hyflexâ„¢ CM and One Shapeâ„¢ Instrumentation Systems (An In Vitro Study)

Background: Many types of instruments and techniques are used in the instrumentation of the root canal system. These instruments and techniques may extrude debris beyond the apical foramen and may cause post-instrumentation complications. The aim of this study was to evaluate the amount of apically extruded debris resulted by using 4 types of nickel-titanium instruments (WaveOne, TRUShape 3D conforming files, Hyflex CM, and One Shape files) during endodontic instrumentation. Materials and methods: Forty freshly extracted human mandibular second premolar with straight canals and a single apex were collected for this study. All teeth were cut to similar lengths. Pre-weighted glass vials were used as collecting containers. Samples were randoml

... Show More
Crossref (3)
Crossref
View Publication Preview PDF
Publication Date
Thu Nov 21 2024
X-ray diffraction and biocompatibility of glass ionomer cement reinforced by different ratios of synthetic hydroxyapatite

Background: This study was done to assist X-ray diffraction and biocompatability of glass ionomer cement reinforced by different ratios of Hydroxyapatite. Materials and Methods: The powder of glass ionomer cement reinforced by different ratios of Hydroxyapatite were used to get X-ray diffraction pattern by X-ray diffraction machine, While for biocompatibility test, A polyethylene tubes containing glass ionomer cement reinforced by different ratios of Hydroxyapatite were implanted on the dorsal submucosal site of Rabbit's tissues and histological slide were prepared for histopathological study. Results: X-ray diffraction test showed that all elements of glass ionomer cement reinforced by different ratios of Hydroxyapatite were react with eac