Optical and structural characteristics of pulsed DC magnetron sputtered Ce1- xTixOy coatings
...Show More Authors

This contribution investigates the impact of adding transition metal of Ti to CeOy samples at various concentrations referring to 0, 15.84, 24.46, 34.46, 36.23, 38.46, 45.38% and pure TiOy, correspondingly. The samples were fabricated by the magnetron sputtering technique. X-ray diffraction (XRD) configurations demonstrate the presence of α-Ce2O3 and Ce2O3 phases with increased Ti contents in the systems. X-ray photoelectron spectroscopy (XPS) experimentation confirms the purity of the S1-sample (CeO2) and the purity of the S8-sample (TiO2). Further XPS analysis reveals that Ti incorporation in the doped systems functions as a reducing agent because of the existence of α-Ce2O3 and Ce2O3 phases. Moreover, based on UV–vis spectroscopy results, the studied samples exhibit indirect optical energy band-gaps reduced from 2.6 to 2.35 eV with the increase of Ti concentrations of 0–45.38% in (S1-S7), respectively. In reference to bandgap 2.35 eV, a slight rise in band gaps was detected for S3 sample. However, an observable increase in the band gap of 2.9 eV occurred for S8 (pure TiO2). Optical analysis of the calculated energy loss parameters demonstrates that all the studied samples reveal small amounts of energy loss. Our results suggest that the improved optical properties of Ti-doped CeOy films could serve for various optical applications.

Publication Date
Tue Nov 01 2022
Journal Name
Optik
Optical and structural characteristics of pulsed DC magnetron sputtered Ce1−xTixOy coatings
...Show More Authors

This contribution investigates the impact of adding transition metal of Ti to CeOy samples at various concentrations referring to 0, 15.84, 24.46, 34.46, 36.23, 38.46, 45.38% and pure TiOy, correspondingly. The samples were fabricated by the magnetron sputtering technique. X-ray diffraction (XRD) configurations demonstrate the presence of α-Ce2O3 and Ce2O3 phases with increased Ti contents in the systems. X-ray photoelectron spectroscopy (XPS) experimentation confirms the purity of the S1-sample (CeO2) and the purity of the S8-sample (TiO2). Further XPS analysis reveals that Ti incorporation in the doped systems functions as a reducing agent because of the existence of α-Ce2O3 and Ce2O3 phases. Moreover, based on UV–vis spectroscopy res

... Show More
View Publication
Scopus Clarivate Crossref
Publication Date
Mon Oct 01 2018
Journal Name
Ceramics International
Influence of DC magnetron sputtering reaction gas on structural and optical characteristics of Ce-oxide thin films
...Show More Authors

The influence of the reaction gas composition during the DC magnetron sputtering process on the structural, chemical and optical properties of Ce-oxide thin films was investigated. X-ray diffraction (XRD) studies confirmed that all thin films exhibited a polycrystalline character with cubic fluorite structure for cerium dioxide. X-ray photoelectron spectroscopy (XPS) analyses revealed that cerium is present in two oxidation states, namely as CeO2 and Ce2O3, at the surface of the films prepared at oxygen/argon flow ratios between 0% and 7%, whereas the films are completely oxidized into CeO2 as the aforementioned ratio increases beyond 14%. Various optical parameters for the thin films (including an optical band gap in the range of 2.25–3.

... Show More
View Publication
Scopus (19)
Crossref (18)
Scopus Clarivate Crossref
Publication Date
Tue May 01 2018
Journal Name
Applied Surface Science
Structural, morphological, and optical characterizations of Mo, CrN and Mo:CrN sputtered coatings for potential solar selective applications
...Show More Authors

View Publication
Scopus (23)
Crossref (19)
Scopus Clarivate Crossref
Publication Date
Tue Feb 13 2018
Journal Name
Journal Of Optics
Solar selective performance of metal nitride/oxynitride based magnetron sputtered thin film coatings: a comprehensive review
...Show More Authors

View Publication
Scopus (27)
Crossref (18)
Scopus Clarivate Crossref
Publication Date
Sat Apr 01 2017
Journal Name
Journal Of Alloys And Compounds
Structural and optical characteristics of pre- and post-annealed sol-gel derived CoCu-oxide coatings
...Show More Authors

Sol-gel derived CuCo-oxide coatings as solar selective surfaces, synthesized onto aluminium substrates at various annealing temperatures, are analysed by correlating their structural, chemical bonding states, and surface morphological topographies. As the annealing progressed, all the coatings displayed a Cu0.56Co2.44O4 (ICSD 78-2175) phase with preferential orientation along (400) reflection plane. Rietveld refinement of X-ray diffraction (XRD) data indicate that residual stress and microstrains developed around the coating surfaces are reduced resulting in mechanically stable thin films. Enhancement of the crystallite size and preferred orientation of the surface were confirmed via XRD, field emission scanning electron microscopy (FESEM),

... Show More
View Publication
Scopus (13)
Crossref (13)
Scopus Clarivate Crossref
Publication Date
Sat Apr 30 2022
Journal Name
Iraqi Journal Of Science
Effect of Films Thickness on Structural and Optical Properties of Gold (Au) Thin Films Prepared by DC Magnetron Sputtering
...Show More Authors

In this paper, the effect of films thickness on the structural and optical properties of gold (Au) thin films prepared by the DC sputtering method was studied. At three different deposition times, three samples of gold thin films of three different thicknesses (200,400, and 600 nm) were prepared. X-ray diffraction patterns, scanning electron microscopy (SEM), and atomic force microscopy (AFM) images, as well as optical spectroscopy, were used to characterize thin films. The crystalline structure of gold thin films was determined by the XRD pattern which showed to be cubic phase and polycrystalline in nature. The preferred orientation was (111) at 2Ѳ equal 37.4. The effect of deposition time on the morphology of the deposited films was v

... Show More
View Publication Preview PDF
Scopus (1)
Scopus Crossref
Publication Date
Fri Feb 01 2019
Journal Name
Physica B: Condensed Matter
Effect of gas mixing ratio on structural characteristics of titanium dioxide nanostructures synthesized by DC reactive magnetron sputtering
...Show More Authors

View Publication
Scopus (26)
Crossref (4)
Scopus Clarivate Crossref
Publication Date
Sat May 01 2021
Journal Name
Journal Of Physics: Conference Series
Tailoring the structural, morphological, electrical and optical characteristics of transparent and conductive ZnO/Ag-NPs thin film coatings
...Show More Authors
Abstract<p>In this study, high quality ZnO/Ag-NPs thin transparent and conductive film coatings were fabricated <italic>via</italic> sol-gel process combined with spin-coating technique. Structural, surface morphology, electrical and optical properties were investigated by means of XRD, Hall effect measurements, FESEM and UV-Vis. The synthesized ZnO/Ag-NPs thin films shows a polycrystalline wurtzite structure, and the grain sizes enlarged when the annealing temperature increased. The surface morphologies of the coatings were dense, smooth and homogeneous as proved by FESEM images. The resistivity of (5.8×10<sup>−4</sup> Ω.cm), the carrier concentration of (3×10<sup></sup></p> ... Show More
View Publication
Scopus Crossref
Publication Date
Wed May 25 2022
Journal Name
Iraqi Journal Of Science
Optical Properties of Manufactured Mirrors Using DC Plasma Magnetron Sputtering Technique
...Show More Authors

    This paper defines a method for sputtering high strength, extremely conductive silver mirrors on glass substrates at temperatures ranging from 20o to 22o C. The silver coated layer thicknesses in this work ranges from 7.5 to 16.1 nm using sputtering time from 10 to 30 min at power 25 W, 13.7 to 29.2 nm for time 10 to 30 min at 50 W, 15.7 to 26.4 nm for time 10 to 30 min at 75 W and 13.8 to 31.1 nm for time 10 to 30 min at 100 W. The optimum values of pressure and electrode gape for plasma sputtering system are 0.1 mbar and 5 cm respectively. The effect of DC sputtering power, sputtering duration or (sputtering time), and thickness on optical properties was investigated using an ultraviolet-visible spectrophot

... Show More
View Publication Preview PDF
Scopus (2)
Scopus Crossref
Publication Date
Thu Oct 01 2020
Journal Name
Iraqi Journal Of Applied Physics
Spectral and Electrical Characteristics of Nanostructured NiO/TiO 2 Heterojunction Fabricated by DC Reactive Magnetron Sputtering
...Show More Authors

In this work, p-n junctions were fabricated from highly-pure nanostructured NiO and TiO2 thin films deposited on glass substrates by dc reactive magnetron sputtering technique. The structural characterization showed that the prepared multilayer NiO/TiO2 thin film structures were highly pure as no traces for other compounds than NiO and TiO2 were observed. It was found that the absorption of NiO-on-TiO2 structure is higher than that of the TiO2-on-NiO. Also, the NiO/TiO2 heterojunctions exhibit typical electrical characteristics, higher ideality factor and better spectral responsivity when compared to those fabricated from the same materials by the same technique and with larger particle size and lower structural purity.

View Publication Preview PDF