Optimization procedures using a variety of input parameters have gotten a lot of attention, but using three non-edible seed oils of Jatropha (Jatropha curcas), Sesame (Sesamum indicum), and Sweet Almond (Prunusamygdalus dulcis) has a few advantages, including availability and non-food competitiveness. Optimizing a two-stage trans-esterification process using a sodium hydroxide-based catalyst at a fixed catalyst (1.0wt %) and temperature (60 ^oC) while varying molar ratio (1:3, 1:6, 1:12),  time (20–60 min), and mixing speed (500–1000 rpm), to produce optimal responses of yields were studied using response surface methodology (RSM). The optimization solution of molar ratio (1:3), time (40.9 min.),

Enzymatic hydrolysis process of lignocellulosic biomass materials is difficult because of inherent structural features of biomass, which represents barriers that prevent complete hydrolysis; therefore, pretreatment techniques are necessary to render biomass highly digestible in enzymatic hydrolysis process. In this research, (non?) oxidative short-term lime pretreatment of willow wood was used. A weight of  11.40 g of willow wood was mixed with an excess of calcium hydroxide (0.4 g Ca(OH)₂/g raw biomass) and water loading (15 g/g raw biomass). Lime pretreatment was carried out for various periods of time including 1, 2, 3.5, 5 and 6 h, with temperatures at 100, 113, 130, 147 and 160⁰C, and oxygen pressures as o

Epoxy resins were modified by some thermosetting materials using unsaturated polyesters which were cured with styrene , MMA ,and MA . When unsaturated Polyester ( as thermosetting material ) was used , and cured with styrene showed better results than acrylic monomers . Thermal stability rised on modification of epoxy resins with unsaturated polyester . The new formulation had converted the epoxy resin from hard brittle material to hard and tough material .

Thermal analysis were studied using ( DSC ) and physicomechanical characteristics were measured .

The sustainable development according to the United Nation, listed firms throughout globally now routinely provide sustainability data. However, there is not enough information on Sustainability Performance Quality (SPQ) in the majority of emerging economies, including Malaysia. This study looks at how the SPQ of the top 100 Malaysian-listed businesses is affected by factors as connected with corporate governance (e.g., board meeting, board size, and board ethnic diversity). Utilizing 500 firm-year data, a longitudinal sample of 500 nonfinancial firms on the Bursa Malaysia for 2015-2019 is employed in this study. The findings from the analysis using the panel regression demonstrated that: ethnic diversity and board siz

Epoxy resins were modified using thermoplastics, such as polystyrene and poly (methylmethacrylate) (PMMA) or their monomers polymerized in situe. The modifications showed good results specially when (PMMA) was used. Thermal analysis of the modified polymers were studied using (DSC) and other physico-mechanical properties measurement.

This research includes the using of statistical to improve the quality of can plastics which is produced at the state company for Vegetable oils (Almaamon factory ) by using the percentage defective control chart ( p-chart ) of a fixed sample. A sample of size (450) cans daily for (30) days was selected to determine the rejected product . Operations research with a (win QSB ) package for ( p-chart ) was used to determine test quality level required for product specification to justify that the process that is statistically controlled.
The results show high degree of accuracy by using the program and the mathematical operations (primary and secondary ) which used to draw the control limits charts and to reject the statistically uncontr

In  this  work,  three  inorganic  additives were 1,1sed,  these  are  (I)  ;

tetraethyl ammonium bromodichloro phenylphsphin, (II) Chlorinated paraffine. and (ITI) a mixture  of  (50%  by weight  of each) to study the synergetic effect.  These  additives \'v·cre used  as flame retardants with unsaturated  polyester  and  epoxy  resins.;, since  these  resins  are industrially important  and of \Vide uses in life.

Results showed efficiency of these  additives to retard  fl mmabillty and stop burning of resins throqght the ASTM tests used Measurement of Limiting oxygen  index (LOI), &nbs

Image is an important digital information that used in many internet of things (IoT) applications such as transport, healthcare, agriculture, military, vehicles and wildlife. etc. Also, any image has very important characteristic such as large size, strong correlation and huge redundancy, therefore, encrypting it by using single key Advanced Encryption Standard (AES) through IoT communication technologies makes it vulnerable to many threats, thus, the pixels that have the same values will be encrypted to another pixels that have same values when they use the same key. The contribution of this work is to increase the security of transferred image. This paper proposed multiple key AES algorithm (MECCAES) to improve the security of the tran

In this investigation , borax (B) (additive I) and chlorinated paraffin (CP.) (additive II) ,were used as flame retardants for each of epoxy and unsaturated polyester resins in the weight ratios of 2,4,6, & 8% by preparing films of (130×130×3) mm dimensions. Also films of these resins with a mixture of [50%(B.)+50%(CP.)] (additive III) in the same weight ratios were prepared in order to study the synergistic effect of these additives on the flammability of the two resins . Three standard test methods were used to measure the flame retardation which are : 1-ASTM : D-2863 2-ASTM : D-635 3-ASTM : D-3014

This research studies the development and synthesis of blended nanocomposites filled with Titanium dioxide (TiO2). Blended nanocomposites based on unsaturated polyester resin (UPR) and epoxy resins were synthesized by reactive blending. The optimum quantity from nano partical of titanium dioxide was selected and different weight proportions 1%, 3%, 5%, and 7% ratios of new epoxy are blended with UPR resin. The dielectric breakdown strength and thermal conductivity properties of the blended nanocomposites were compared with those of the basis material (UPR and 3% TiO2).The results show good compatibility epoxy resins with the UPR resin on blending, dielectric breakdown strength values  are higher while thermal conductivity values of